Robustness and printed sensor qualification

Abstract

A limiting factor of additive manufactured (AM) sensors for in-pile applications is the development of appropriate interconnection and packaging strategies that can maintain reliable performance in extreme environments. Failure mechanisms in these harsh conditions could include, but not limited to, materials interaction (i.e., intermetallic formation) and coefficient of thermal expansion (CTE) mismatch between the individual components of the sensors. To mitigate premature failure and enable the successful sustained operation of AM sensors, non-destructive qualification tests are used as an intermediate process control step used for verifying robustness and reliability of the sensor before they are deployed. A materials system of interest is the use of barium strontium titanium oxide (BST) films on stainless steel 316L (SS316L) substrate. Due to BST’s high dielectric constant and tunable dielectric properties, there is an interest for its application as an insulation/encapsulation layer for capacitive strain gauges when printed on structural materials. Previous work on the BST/SS316L material system, however, showed that the BST cracks when exposed to temperatures up to 600 °C due to CTE mismatch between the printed BST film and the metallic substrate. When comparing different fabrication techniques, less surface cracking was observed in the samples that deposited thinner (i.e., 2-20 μm) than samples that were thicker (i.e., 135 µm – 300 µm). The objective of this report is to establish a qualification process that will determine and address any challenges (i.e., mechanical failure of thick prints) of the AM sensor prior to its application in experimental tests. To demonstrate the qualification process in this report, laser spallation and uniaxial tensile tests using dynamic and quasi-static loading, respectively, will be discussed.