Phero, Timothy Le | Engineering Papers

DOE OSTI2024

Application of printed strain gauges in prototypical nuclear reactor conditions

This report discusses the current development and testing of additively manufactured temperature sensors and resistive/ capacitive strain gauges. This has potential to improve the sensor design and manufacturing techniques to meet the requirements of in-pile monitoring of mechanical properties and structural health of materials and specimens in current and advanced nuclear test reactors (i.e., in terms of environment conditions, sample geometry, and materials compatibility). The developmental additively manufactured strain gauges are exposed to separate effects testing (i.e., mechanical strain (up to 1000 µe), high temperature (up to 700 °C)) to determine environmental factors that affect the performance of the strain gauge. The robustness and integrity of a printed strain gauge layer exposed to a molten salt environment for up to 500 hours was evaluated, with the goal of assessing material compatibility of printed strain sensors for instrumented surveillance test articles in molten salt reactors. In addition, sensor qualification methodologies are further developed for determining the reliability and robustness at the interface of the additively manufactured strain gauge materials.

36 - MATERIALS SCIENCE↗

DOE OSTI2024

Robustness and printed sensor qualification

A limiting factor of additive manufactured (AM) sensors for in-pile applications is the development of appropriate interconnection and packaging strategies that can maintain reliable performance in extreme environments. Failure mechanisms in these harsh conditions could include, but not limited to, materials interaction (i.e., intermetallic formation) and coefficient of thermal expansion (CTE) mismatch between the individual components of the sensors. To mitigate premature failure and enable the successful sustained operation of AM sensors, non-destructive qualification tests are used as an intermediate process control step used for verifying robustness and reliability of the sensor before they are deployed. A materials system of interest is the use of barium strontium titanium oxide (BST) films on stainless steel 316L (SS316L) substrate. Due to BST’s high dielectric constant and tunable dielectric properties, there is an interest for its application as an insulation/encapsulation layer for capacitive strain gauges when printed on structural materials. Previous work on the BST/SS316L material system, however, showed that the BST cracks when exposed to temperatures up to 600 °C due to CTE mismatch between the printed BST film and the metallic substrate. When comparing different fabrication techniques, less surface cracking was observed in the samples that deposited thinner (i.e., 2-20 μm) than samples that were thicker (i.e., 135 µm – 300 µm). The objective of this report is to establish a qualification process that will determine and address any challenges (i.e., mechanical failure of thick prints) of the AM sensor prior to its application in experimental tests. To demonstrate the qualification process in this report, laser spallation and uniaxial tensile tests using dynamic and quasi-static loading, respectively, will be discussed.

36 - MATERIALS SCIENCE↗