DOE OSTI2024

Effects of irradiation damage on the elastic properties and hardness of complex transition metal diborides

Multi-principal component transition metal (TM) diborides represent a class of high-entropy ceramics (HECs) that have received considerable interest in recent years owing to their promising properties for extreme environment applications that include thermal/ environmental barriers, hypersonic vehicles, turbine engines, and next-generation nuclear reactors. While the addition of chemical disorder through the random distribution of TM elements on the cation sublattice has offered opportunities to tailor elastic stiffness and hardness, the effects of irradiationinduced structural damage on the physical properties of these complex materials have remained largely unexplored. To this end, changes in the hardness and elastic moduli of a high-entropy TM diboride (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)B2 and three of its quaternary subsets following irradiation with 10 MeV gold (Au) ions to fluences of up to 6 × 10^15 Au cm-2 are investigated at the micrometer and sub-micrometer length-scales via the dispersion of laser-generated surface acoustic waves (SAW) and nanoindentation, respectively. The nanoindentation measurements show that the TM diborides exhibit an initial increase in hardness following irradiation with energetic Au ions, with a subsequent decrease in hardness following further irradiation. One quaternary composition, (Hf1/3Ta1/3Ti1/3)B2, exhibits a notable exception to the trend and continues to exhibit an increase in hardness with ion irradiation fluence. Although differences in the absolute values of the effective elastic moduli obtained from the measured SAW dispersion and nanoindentation are observed (and attributed to microstructural variations at the measurement length-scale), both techniques yield similar trends in the form of an initial reduction and subsequent saturation in the elastic modulus with increasing ion irradiation fluence. The quaternary TM diboride (Hf1/3Ta1/3Ti1/3)B2 again exhibits a departure from this trend. The high-entropy TM diboride (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)B2 exhibits the greatest recovery in hardness and modulus when irradiated to high ion fluences following initial changes at low fluence, indicating superior resistance to radiation-induced damage over its quaternary counterparts. Opportunities for designing HECs with superior hardness and modulus for enhanced radiation resistance (compared to their single constituent counterparts) by tailoring chemical disorder and bond character in the lattice are discussed.

36 - MATERIALS SCIENCE↗

DOE OSTI2024

Application of printed strain gauges in prototypical nuclear reactor conditions

This report discusses the current development and testing of additively manufactured temperature sensors and resistive/ capacitive strain gauges. This has potential to improve the sensor design and manufacturing techniques to meet the requirements of in-pile monitoring of mechanical properties and structural health of materials and specimens in current and advanced nuclear test reactors (i.e., in terms of environment conditions, sample geometry, and materials compatibility). The developmental additively manufactured strain gauges are exposed to separate effects testing (i.e., mechanical strain (up to 1000 µe), high temperature (up to 700 °C)) to determine environmental factors that affect the performance of the strain gauge. The robustness and integrity of a printed strain gauge layer exposed to a molten salt environment for up to 500 hours was evaluated, with the goal of assessing material compatibility of printed strain sensors for instrumented surveillance test articles in molten salt reactors. In addition, sensor qualification methodologies are further developed for determining the reliability and robustness at the interface of the additively manufactured strain gauge materials.

36 - MATERIALS SCIENCE↗

DOE OSTI2024

Robustness and printed sensor qualification

A limiting factor of additive manufactured (AM) sensors for in-pile applications is the development of appropriate interconnection and packaging strategies that can maintain reliable performance in extreme environments. Failure mechanisms in these harsh conditions could include, but not limited to, materials interaction (i.e., intermetallic formation) and coefficient of thermal expansion (CTE) mismatch between the individual components of the sensors. To mitigate premature failure and enable the successful sustained operation of AM sensors, non-destructive qualification tests are used as an intermediate process control step used for verifying robustness and reliability of the sensor before they are deployed. A materials system of interest is the use of barium strontium titanium oxide (BST) films on stainless steel 316L (SS316L) substrate. Due to BST’s high dielectric constant and tunable dielectric properties, there is an interest for its application as an insulation/encapsulation layer for capacitive strain gauges when printed on structural materials. Previous work on the BST/SS316L material system, however, showed that the BST cracks when exposed to temperatures up to 600 °C due to CTE mismatch between the printed BST film and the metallic substrate. When comparing different fabrication techniques, less surface cracking was observed in the samples that deposited thinner (i.e., 2-20 μm) than samples that were thicker (i.e., 135 µm – 300 µm). The objective of this report is to establish a qualification process that will determine and address any challenges (i.e., mechanical failure of thick prints) of the AM sensor prior to its application in experimental tests. To demonstrate the qualification process in this report, laser spallation and uniaxial tensile tests using dynamic and quasi-static loading, respectively, will be discussed.

36 - MATERIALS SCIENCE↗