Predicting and Synthesizing Interface Stabilized 2D Layers

Abstract

The compound (Pb 2 MnSe 3 ) 0.6 VSe 2 was predicted to be kinetically stable based on density functional theory (DFT) calculations on an island of Pb 2 MnSe 3 between layers of VSe 2 . This approach provides a high degree of freedom by not forcing interlayer lattice match, making it ideal to investigate the likelihood of formation of new incommensurate layer misfit structures. The free space around the island is critical, as it allows atoms to diffuse and hence exploring the local energy landscape around the initial configuration. (Pb 2 MnSe 3 ) 0.6 VSe 2 was synthesized via a near diffusionless reaction from precursors where a repeating sequence of elemental layers matches the local composition and layer sequence of the predicted compound. The VSe 2 layer consists of a Se–V–Se trilayer with octahedral coordination of the V atoms. The Pb 2 MnSe 3 layer consists of three rock-salt-like planes, with a MnSe layer between the planes of PbSe. The center MnSe plane stabilizes the puckering of the outer PbSe layers. Electrical properties indicate that (Pb 2 Mn 1 Se 3 ) 0.6 VSe 2 undergoes a charge density wave transition at ~100 K and orders ferromagnetically at 35 K. Overall, the combination of theory and experiment enables a faster convergence to new heterostructures than either approach in isolation.