Low temperature hot corrosion

Abstract

The reaction of Co-Cr, Ni-Cr, Co-Cr-Al, and Ni-Cr-Al alloys with Na2SO4 in the presence of SO3 at temperatures between 700 and 750 C leads to the formation of liquid CoSO4-Na2SO4 or NiSO4-Na2SO4 deposits on the alloy surface. The formation of Cr2O3 and/or Al2O3 below this deposit results in a locally low P(O2) and a higher P(S2) and P(SO2). It is noted that these conditions can prevent protective oxide formation either by sulfide formation in the alloy, which localizes the Cr and/or Al in discrete particles, or by acid fluxing involving a reaction between Al2O3 or Cr2O3 and SO2 to form a salt-soluble species and subsequent reprecipitation as porous oxides in regions of higher P(O2). These processes may occur simultaneously, although a given alloy generally exhibits features of predominantly one type. Here, the Ni-Cr and Ni-Cr-Al alloys, and to some extent the Co-Cr alloys, exhibit features indicative of the sulfidation mechanism, whereas the morphology for the Co-Cr-Al alloy is more consistent with a predominant acid fluxing mechanism.