Engineering topics

Chiang, K. T.

Publications and source records attributed to Chiang, K. T..

3 records

NASA NTRS1998

Creep of Uncoated and Cu-Cr Coated NARloy-Z

Stress rupture creep tests were performed on uncoated and Cu-30vol%Cr coated NARloy-Z copper alloy specimens exposed to air at 482 C to 704 C. The results showed that creep failure in air of unprotected NARloy-Z was precipitated by brittle intergranular surface cracking produced by strain assisted grain boundary oxidation (SAGBO) which in turn caused early onset of tertiary creep. For the protected specimens, the Cu-Cr coating remained adherent throughout the tests and was effective in slowing down the rate of oxygen absorption, particularly at the higher temperatures, by formation of a continuous chromium oxide scale. As the result of reducing oxygen ingress, the coating prevented SAGBO initiated early creep failure, extended creep deformation and increased the creep rupture life of NARloy-Z over the entire 482 C to 704 C test temperature range.

Walter, R. J.↗

NASA NTRS1983

Low temperature hot corrosion

The reaction of Co-Cr, Ni-Cr, Co-Cr-Al, and Ni-Cr-Al alloys with Na2SO4 in the presence of SO3 at temperatures between 700 and 750 C leads to the formation of liquid CoSO4-Na2SO4 or NiSO4-Na2SO4 deposits on the alloy surface. The formation of Cr2O3 and/or Al2O3 below this deposit results in a locally low P(O2) and a higher P(S2) and P(SO2). It is noted that these conditions can prevent protective oxide formation either by sulfide formation in the alloy, which localizes the Cr and/or Al in discrete particles, or by acid fluxing involving a reaction between Al2O3 or Cr2O3 and SO2 to form a salt-soluble species and subsequent reprecipitation as porous oxides in regions of higher P(O2). These processes may occur simultaneously, although a given alloy generally exhibits features of predominantly one type. Here, the Ni-Cr and Ni-Cr-Al alloys, and to some extent the Co-Cr alloys, exhibit features indicative of the sulfidation mechanism, whereas the morphology for the Co-Cr-Al alloy is more consistent with a predominant acid fluxing mechanism.

Chiang, K. T.↗

NASA NTRS1980

Hot corrosion of Co-Cr, Co-Cr-Al, and Ni-Cr alloys in the temperature range of 700-750 deg C

The effect of SO3 pressure in the gas phase on the Na2SO4 induced hot corrosion of Co-Cr, Ni-Cr, and Co-Cr-Al alloys was studied in the temperature range 700 to 750 C. The degradation of the Co-Cr and Ni-Cr alloys was found to be associated with the formation of liquid mixed sulfates (CoSO4-Na2SO4 or NiSO4-Na2SO4) which provided a selective dissolution of the Co or Ni and a subsequent sulfidation oxidation mode of attack which prevented the maintenance of a protective Cr2O3 film. A clear mechanism was not developed for the degradation of Co-Cr-Al alloys. A pitting corrosion morphology was induced by a number of different mechanisms.

Chiang, K. T.↗