Understanding the Larson-Miller parameter

Abstract

The Larson-Miller (L-M) method of extrapolating stress rupture and creep results is based on the contention that the absolute temperature-compensated time function should have a unique value for a given material. This value should depend only on the applied stress level. The L-M method has been found satisfactory in the case of many steels and superalloys. The derivation of the L-M relation is discussed, taking into account a power law creep relationship considered by Dorn (1965) and Barrett et al. (1964), a correlation expression reported by Garofalo et al. (1961), and relations concerning the constant C. Attention is given to a verification of the validity of the considered derivation with the aid of suitable materials.