Engineering topics

Tien, J. K.

Publications and source records attributed to Tien, J. K..

At least 19 records

NASA NTRS1990

Interfacial reactions in high temperature metallic and intermetallic matrix composites - A status review

Interdiffusion and interdiffusion-related phenomena in metal and intermetallic matrix composites can be of crucial interest for the prolonged application of these systems at high temperature. The level of complication that these effects can have can vary significantly from system to system. Reviewed herein are recent efforts to address interdiffusion and reaction kinetics for both a simple system, the single phase W/Nb system, and more complex systems such as tungsten fiber reinforced superalloys (TFRS) and beryllide reinforced aluminides. Additionally, recent work on inhibiting interdiffusion in MMCs via ion-implanted diffusion barriers will be presented.

Tien, J. K.↗

NASA NTRS1988

Interdiffusional effects between TiBe12 and NiAl intermetallics

The TiBe12/NiAl composites fabricated by a powder metallurgy technique were examined for the extent of interdiffusion between its components, using scanning Auger microscopy. The results revealed an evidence of a reaction between the two component intermetallics after annealing at 1300 K for 100 h, with a 95-micron reaction zone extending from the TiBe12/NiAl interface. The concentration profile across the reaction zone showed that the Ni, Al, and Be concentrations were in a 1:1:2 ratio, while Ti was present in only very small amounts.

Carbone, A. J.↗

NASA NTRS1988

The effect of Co alloying content on the kinetics of reaction zone growth in tungsten fiber reinforced superalloy composites

A Co-free modified superalloy similar in composition to Waspaloy is investigated in an effort to understand the effect of Co on reaction zone growth kinetics and verify the chemistry dependence of reaction zone growth in the matrix of tungsten fiber reinforced superalloy composites. The values of the parabolic rate constant, characterizing the kinetics of reaction zone growth, for the Waspaloy matrix and the C-free alloy as well as five other alloys from a previous study confirm the dependence of reaction zone growth kinetics on cobalt content of the matrix. The Co-free alloy composite exhibits the slowest reaction zone growth among all tungsten fiber reinforced composites studied to date.

Rodriguez, A.↗

NASA NTRS1988

Reaction kinetics between fiber and matrix

Interdiffusion and interdiffusion controlled intermediate phase formation in metal matrix composites can be of interest for the prolonged application of these systems at high temperatures. Methods are discussed that address the kinetics of interdiffusion in systems that exhibit solid solution intermixing or the formation of a third intermediate phase at the fiber/matrix interface, or both. The tungsten fiber reinforced niobium and tungsten fiber reinforced superalloy systems are employed as model systems for experimentation and discussion. In an effort to impede interdiffusion, the concept of ion implanted diffusion barriers have been examined. Preliminary results on the feasibility and effectiveness of ion implanted diffusion barriers are presented.

Kopp, M. W.↗

NASA NTRS1986

Precision cast vs. wrought superalloys

While cast polycrystalline superalloys recommend themselves in virtue of better 'buy-to-fly' ratios and higher strengthening gamma-prime volume fractions than those of wrought superalloys, the expansion of their use into such critical superalloy applications as gas turbine hot section components has been slowed by insufficient casting process opportunities for microstructural control. Attention is presently drawn, however, to casting process developments facilitating the production of defect-tolerant superalloy castings having improved fracture reliability. Integrally bladed turbine wheel and thin-walled turbine exhaust case near-net-shape castings have been produced by these means.

Tien, J. K.↗

NASA NTRS1985

Interdiffusional effects between tungsten fibers and an iron-nickel-base alloy

Tungsten fibers in the INCOLOY 903 alloy were annealed for over 100 hours at 1038 C and 1200 C. It was found that interdiffusion results in the formation of a reaction zone. SEM-EDS probe analysis showed that the chemistries across this zone were constant, suggesting the zone was a compound phase. The composition of the compound was estimated to be that of a mu-type phase. The local chemistry (in atomic percent) at the reaction zone/alloy matrix interface was found to be approximately 8 pct W, 1.2 pct Nb, 40 pct Fe, 14 pct Co, and 36 pct Ni. In addition, recrystallization was observed in both the remaining tungsten fiber and the nearby INCOLOY 903 matrix after annealing at 1200 C, but not at 1038 C. The results of this study suggest that reaction zone growth kinetics can be minimized by the reduction of Co and Fe and the increase of W in the matrix alloy.

Caulfield, T.↗

NASA NTRS1984

Modeling of gamma/gamma-prime phase equilibrium in the nickel-aluminum system

A theoretical model is proposed for the determination of phase equilibrium in alloys, taking into consideration dissimilar lattice parameters. Volume-dependent pair interactions are introduced by means of phenomenological Lennard-Jones potentials and the configurational entropy of the system is treated in the tetrahedron approximation of the cluster variation method. The model is applied to the superalloy-relevant, nickel-rich, gamma/gamma-prime phase region of the Ni-Al phase diagram. The model predicts reasonable values for the lattice parameters and the enthalpy of formation as a function of composition, and the calculated phase diagram closely approximates the experimental diagram.

Sanchez, J. M.↗

NASA NTRS1984

The role of cobalt on the creep of Waspaloy

Cobalt was systematically replaced with nickel in Waspaloy (which normally contains 13% Co) to determine the effects of cobalt on the creep behavior of this alloy. Effects of cobalt were found to be minimal on tensile strengths and microstructure. The creep resistance and the stress rupture resistance determined in the range from 704 to 760 C (1300 to 1400 C) were found to decrease as cobalt was removed from the standard alloy at all stresses and temperatures. Roughly a ten-fold drop in rupture life and a corresponding increase in minimum creep rate were found under all test conditions. Both the apparent creep activation energy and the matrix contribution to creep resistance were found to increase with cobalt. These creep effects are attributed to cobalt lowering the stacking fault energy of the alloy matrix. The creep resistance loss due to the removal of cobalt is shown to be restored by slightly increasing the gamma' volume fraction. Results are compared to a previous study on Udimet 700, a higher strength, higher gamma' volume fraction alloy with similar phase chemistry, in which cobalt did not affect creep resistance. An explanation for this difference in behavior based on interparticle spacing and cross-slip is presented.

Jarrett, R. N.↗

NASA NTRS1984

Effects of cobalt on the hot workability of nickel-base superalloys

The effect of cobalt on the workability of nickel-base superalloys is examined with reference to experimental results for four heats of alloys based on the Nimonic 115 composition with varying amounts of nickel substituted for the nominal 14 percent cobalt. It is shown that Co lowers the gamma-prime solvus, which in turn lowers the Cr23C6 carbide solvus. It is further shown that these solvus temperatures bracket the hot working range for the alloys. However, thermomechanical processing modifications reflecting the effect of Co on the gamma-prime and carbide solvi are shown to restore the workability and the properties of alloys with little or no cobalt.

Jarrett, R. N.↗

NASA NTRS1983

Effects of cobalt in nickel-base superalloys

The role of cobalt in a representative wrought nickel-base superalloy was determined. The results show cobalt affecting the solubility of elements in the gamma matrix, resulting in enhanced gamma' volume fraction, in the stabilization of MC-type carbides, and in the stabilization of sigma phase. In the particular alloy studied, these microstructural and microchemistry changes are insufficient in extent to impact on tensile strength, yield strength, and in the ductilities. Depending on the heat treatment, creep and stress rupture resistance can be cobalt sensitive. In the coarse grain, fully solutioned and aged condition, all of the alloy's 17% cobalt can be replaced by nickel without deleteriously affecting this resistance. In the fine grain, partially solutioned and aged condition, this resistance is deleteriously affected only when one-half or more of the initial cobalt content is removed. The structure and property results are discussed with respect to existing theories and with respect to other recent and earlier findings on the impact of cobalt, if any, on the performance of nickel-base superalloys.

Tien, J. K.↗

NASA NTRS1983

Considerations of technology transfer barriers in the modification of strategic superalloys for aircraft turbine engines

A typical innovation-to-commercialization process for the development of a new hot section gas turbine material requires one to two decades with attendant costs in the tens of millions of dollars. This transfer process is examined to determine the potential rate-controlling steps for introduction of future low strategic metal content alloys or processes. Case studies are used to highlight the barriers to commercialization as well as to identify the means by which these barriers can be surmounted. The opportunities for continuing joint government-university-industry partnerships in planning and conducting strategic materials R&D programs are also discussed.

Stephens, J. R.↗

NASA NTRS1982

Creep and rupture of an ODS alloy with high stress rupture ductility

The creep and stress rupture properties of an oxide (Y2O3) dispersion strengthened nickel-base alloy, which also is strengthened by gamma-prime precipitates, was studied at 760 and 1093 C. At both temperatures, the alloy YDNiCrAl exhibits unusually high stress rupture ductility as measured by both elongation and reduction in area. Failure was transgranular, and different modes of failure were observed including crystallographic fracture at intermediate temperatures and tearing or necking almost to a chisel point at higher temperatures. While the rupture ductility was high, the creep strength of the alloy was low relative to conventional gamma prime strengthened superalloys in the intermediate temperature range and to ODS alloys in the higher temperature range. These findings are discussed with respect to the alloy composition; the strengthening oxide phases, which are inhomogeneously dispersed; the grain morphology, which is coarse and elongated and exhibits many included grains; and the second phase inclusion particles occurring at grain boundaries and in the matrix. The creep properties, in particular the high stress dependencies and high creep activation energies measured, are discussed with respect to the resisting stress model of creep in particle strengthened alloys.

Mcalarney, M. E.↗

NASA NTRS1982

Effects of cobalt on structure, microchemistry and properties of a wrought nickel-base superalloy

The effect of cobalt on the basic mechanical properties and microstructure of wrought nickel-base superalloys has been investigated experimentally by systematically replacing cobalt by nickel in Udimet 700 (17 wt% Co) commonly used in gas turbine (jet engine) applications. It is shown that the room temperature tensile yield strength and tensile strength only slightly decrease in fine-grained (disk) alloys and are basically unaffected in coarse-grained (blading) alloys as cobalt is removed. Creep and stress rupture resistances at 760 C are found to be unaffected by cobalt level in the blading alloys and decrease sharply only when the cobalt level is reduced below 8 vol% in the disk alloys. The effect of cobalt is explained in terms of gamma prime strengthening kinetics.

Jarrett, R. N.↗

NASA NTRS1982

Effects of cobalt in nickel-base superalloys

A study has been carried out to assess the role of cobalt in Udimet 700, a representative nickel-base superalloy containing 17 percent or more cobalt. The study spans the spectrum of microstructural, microchemical, and mechanical behavior aspects which together form a basis for superalloy performance in jet engines. The results suggest that cobalt affects the solubility of elements in the gamma matrix, which leads to enhanced gamma-prime volume fraction and to the stabilization of MC-type carbides and sigma phase. However, these microstructural and microchemical changes are too slight to significantly affect the strength and ductile properties. Depending on the heat treatment, the creep and stress rupture resistance can be cobalt-sensitive. In the coarse-grained, fully solutioned and aged condition, all of the alloy's 17 percent Co can be replaced by nickel without decreasing the creep and stress rupture resistance. These findings are discussed with reference to existing theories and experimental data obtained by other workers.

Tien, J. K.↗

NASA NTRS1980

Creep and stress rupture of oxide dispersion strengthened mechanically alloyed Inconel alloy MA 754

The creep and stress rupture behavior of the mechanically alloyed oxide dispersion strengthened nickel-base alloy MA 754 was studied at 760, 982 and 1093 C. Tensile specimens with a fine, highly elongated grain structure, oriented parallel and perpendicular to the longitudinal grain direction were tested at various stresses in air under constant load. It was found that the apparent stress dependence was large, with power law exponents ranging from 19 to 33 over the temperature range studied. The creep activation energy, after correction for the temperature dependence of the elastic modulus, was close to but slightly larger than the activation energy for self diffusion. Rupture was intergranular and the rupture ductility as measured by percentage elongation was generally low, with values ranging from 0.5 to 16 pct. The creep properties are rationalized by describing the creep rates in terms of an effective stress which is the applied stress minus a resisting stress consistent with the alloy microstructure. Values of the resisting stress obtained through a curve fitting procedure are found to be close to the values of the particle by-pass stress for this oxide dispersion strengthened alloy, as calculated from the measured oxide particle distribution.

Howson, T. E.↗

NASA NTRS1980

Creep and stress rupture of a mechanically alloyed oxide dispersion and precipitation strengthened nickel-base superalloy

The creep and stress rupture behavior of a mechanically alloyed oxide dispersion strengthened (ODS) and gamma-prime precipitation strengthened nickel-base alloy (alloy MA 6000E) was studied at intermediate and elevated temperatures. At 760 C, MA 6000E exhibits the high creep strength characteristic of nickel-base superalloys and at 1093 C the creep strength is superior to other ODS nickel-base alloys. The stress dependence of the creep rate is very sharp at both test temperatures and the apparent creep activation energy measured around 760 C is high, much larger in magnitude than the self-diffusion energy. Stress rupture in this large grain size material is transgranular and crystallographic cracking is observed. The rupture ductility is dependent on creep strain rate, but usually is low. These and accompanying microstructural results are discussed with respect to other ODS alloys and superalloys and the creep behavior is rationalized by invoking a recently-developed resisting stress model of creep in materials strengthened by second phase particles.

Howson, T. E.↗

NASA NTRS1980

The role of the alloy matrix in the creep behavior of particle-strengthened alloys

The strengthening microstructural features in heat-resistant super-alloys are oxide dispersoids and/or gamma-prime precipitates. The role of the strength of the alloy matrix in the creep resistance of these alloys is considered. An evaluation was made of experimental data on oxide-dispersion- and/or precipitation-strengthened nickel-based alloys with various levels of matrix solid solution strengthening; a generalized expression for creep rates which separates the matrix contributions from the particle contributions to the resisting stress and creep strength of these alloys was derived. It is concluded that the major role of the alloy matrix in the creep behavior of these alloys is in determining the apparent stress dependence of the creep rates.

Ajaja, O.↗

NASA NTRS1978

Role of back stress in the creep behavior of particle strengthened alloys

Recent developments in the interpolation of high-temperature steady-state creep results have introduced the concept that the stress dependence of the creep rate should be in terms of the effective stress referred to as the applied stress minus a back stress. This paper reports on back stresses taken from data on a gamma-prime-strengthened wrought nickel-base superalloy, an oxide dispersion-strengthened ODS nickel-base solid solution alloy, and an ODS nickel-base superalloy. The effect of air versus vacuum environments and the effect of dynamic changes in the strengthening microstructures on the magnitude of the back stress are assessed. The role of modulus normalization and the back stress correction in determining the true creep activation energy are examined. It is shown that the high values of the apparent stress exponent 'n' of the steady-state creep equation can be easily explained through a relationship between n, the true stress exponent of steady-state creep, and the stress which when subtracted from the applied stress results in the effective driving stress acting on the mobile dislocations during creep.

Purushothaman, S.↗