Pretreated and primed Ti 6-4 surfaces were characterized by scanning electron microscopy/energy dispersive analysis of X-rays (SEM/EDAX) and electron spectroscopy for chemical analysis (ESCA). Fractured lap shear bonded Ti 6-4 specimens were also characterized by SEM/EDAX and ESCA. A number of surface techniques were used to characterize Ti02 powders.
Several techniques were used to study pretreated Ti 6-4 surfaces including scanning electron microscopy (SEM), electron spectroscopy of chemical analysis (ESCA), and, reflectance visible spectroscopy. Each pretreatment type gave a characteristic surface morphology as seen by SEM. Elemental analysis of the Ti 6-4 surfaces was done using ESCA. Trace residual contaminants from particular chemical pretreatments were identified readily. Results indicate that reflectance visible spectroscopy using indicator dyes placed on Ti 6-4 surfaces appears to be a feasible approach to establish surface acidity. Differences in surface acidity were observed using bromthymol blue on Ti 6-4 surfaces pretreated by two different methods.
The acid-base properties of titanium 6-4 plates (low surface area) were investigated after three different pretreatments, namely Turco, phosphate-fluoride and Pasa-Jell. A series of indicators was used and color changes were detected using diffuse reflectance visible spectroscopy. Electron spectroscopy for chemical analysis was used to examine the indicator on the Ti 6-4 surface. Specular reflectance infra-red spectroscopy was used to study the adsorption of stearic acid from cyclohexane solutions on the Ti 6-4 surface.
Explore the source record for details and available documents.
Several techniques have been used to study pretreated Ti 6-4 surfaces including scanning electron microscopy (SEM), electron spectroscopy of chemical analysis (ESCA), and, reflectance visibile spectroscopy. Each pretreatment type gives a characteristic surface morphology as seen by SEM. Elemental analysis of the Ti 6-4 surfaces was done using ESCA. Trace residual contaminants from particular chemical pretreatments are identified readily. Reflectance visible spectroscopy using indicator dyes placed on Ti 6-4 surfaces appears to be a feasible approach to establish surface acidity. Differences in surface acidity have been observed using bromthymol blue on Ti 6-4 surfaces pretreated by two different methods.
The results of analyses by ESCA (Electron Spectroscopy for Chemical Analysis) on several Nuclepore filters which were exposed during air pollution studies are presented along with correlative measurements by Neutron Activation Analysis and Scanning Electron Microscopy. Samples were exposed during air pollution studies at Norfolk, Virginia and the NASA Kennedy Space Center (KSC). It was demonstrated that with the ESCA technique it was possible to identify the chemical (bonding) state of elements contained in the atmospheric particulate matter collected on Nuclepore filters. Sulfur, nitrogen, mercury, chlorine, alkali, and alkaline earth metal species were identified in the Norfolk samples. ESCA binding energy data for aluminum indicated that three chemically different types of aluminum are present in the launch and background samples from NASA-KSC.
The characterization of water adsorption on silica is necessary to an understanding of how hydrogen chloride interacts with silica. The adsorption as a function of outgas temperatures of silica and as a function of the isotherm temperature was studied. Characterization of the silica structure by infrared analysis, X-ray diffraction and differential scanning calorimetry, surface area determinations, characterization of the sample surface by electron spectroscopy for chemical analysis (ESCA), and determinations of the heat of immersion in water of silica were investigated. The silica with a scanning electron microscope was examined.
The interaction of hydrogen chloride with quartz was studied to determine the extent to which silica can irreversibly remove hydrogen chloride from the atmosphere. Adsorption isotherms were measured at 30 C for hydrogen chloride on silica outgassed between 100 C and 400 C. Readsorption isotherms were also measured. The silica surface was characterized further by infrared spectroscopy, electron spectroscopy for chemical analysis, scanning electron microscopy, and immersional calorimetry. Ground debris samples obtained from the Kennedy Space Center, were likewise examined.
Adherend surfaces and fractography were studied using electron spectroscopy for chemical analysis and scanning electron microscopy/energy dispersive analysis of X-rays. In addition, Auger Electron Spectroscopy with depth profiling capability was used. It is shown that contamination of adhesion systems plays an important role not only in determining initial bond strengths but also in the durability of adhesive bonds. It is concluded that the analytical techniques used to characterize and monitor such contamination.
The influence of temperature, pressure, and outgas conditions on the absorption of hydrogen chloride and water vapor on both alpha and gamma alumina was studied. Characterization of the adsorbents was performed using X-ray powder diffraction, scanning electron microscopy (SEM), low temperature nitrogen adsorption desorption measurements, BET nitrogen surface area measurements and electron spectroscopy for chemical analysis (ESCA). Water vapor adsorption isotherms at 30, 40, and 50 C were measured on alpha and gamma alumina after outgassing at 80, 200, and 400 C. Both outgas temperature and adsorption temperature influenced the adsorption of water vapor on the aluminas. The water vapor adsorption was completely reversible. Alpha alumina absorbed more water per unit area than gamma alumina. Differences in the adsorption capacity for water vapor of the two aluminas were explained on the basis of ideal surface models of alpha and gamma alumina. Isosteric heats of adsorption for water vapor on the aluminas were determined over a limited range of surface coverage.
Various surface preparations for titanium 6-4 alloy were studied. An anodizing method was investigated, and compared with the results of other chemical treatments, namely, phosphate/fluoride, Pasa-Jell and Turco. The relative durability of the different surface treatments was assessed by monitoring changes in surface chemistry and morphology occasioned by aging at 505 K (450 F). Basic electron spectroscopic data were collected for polyimide and polyphenylquinoxaline adhesives and synthetic precursors. Fractographic studies were completed for several combinations of adherend, adhesive, and testing conditions.
The ability of SEM/EDAX to determine the physical and chemical composition of very small areas was used to study several diverse types of samples representative of NASA-LaRC technology. More systematic investigation was carried out on differences in the results of grit-blasting Ti 6-4 adherends and the presence of extraneous elements, primarily silicon, in some polymer/HT-S fiber composites. Initial results were obtained from a fractured (ILS) short-beam shear specimen, and from Ti 6-4 alloy, before and after a proprietary Boeing anodizing surface preparation for adhesive bonding. Photomicrographs and EDAX spectra were also obtained from new, fractured lap shear strength specimens that employed PPQ and LARC-13 adhesives.
Explore the source record for details and available documents.
The effects of composites as adherends was studied. Several other variables were studied by fractography: aluminum powder adhesive filler, fiber glass cloth scrim or adhesive carrier, new adhesives PPQ-413 and LARC-13, and strength-test temperature. When the new results were juxtaposed with previous work, it appeared that complex interactions between adhesive, adherend, bonding, and testing conditions govern the observed strength and fracture-surface features. The design parameters likely to have a significant effect upon strength-test results are listed.
High temperature polymer surface characteristics associated with joint strength were evaluated. Selected samples represented composite adherends, aluminum filler and fiber glass carrier cloth. Detailed analysis of fractured joint surfaces revealed unique characteristics typical of the specific adhesive formulations and test conditions. A fracture mechanism model was developed for correlating macroscopic shear strength and microstructure of fracture surfaces. Applications were made to unpublished data on polyimides and fluoropolymers.
This study was concerned with the effects of NH4Cl and (NH4)2SO4 aerosols on the kinetics of disappearance of atomic oxygen. Atomic oxygen was generated by a 2.45-GHz microwave discharge and the kinetics of disappearance measured in a fast flow system using NO2 titration. Values of the recombination coefficient for heterogeneous wall recombination were determined for clean, H2SO4-coated, and (NH4)2SO4-coated Pyrex to be 0.000050, 0.000020, and 0.000019, respectively. A rapid exothermic chemical reaction was found to occur between atomic oxygen and an NH4Cl wall coating; the products were NH3, NO, H2O, and HCl. The NH4Cl aerosol was generated by gas phase reaction of NH3 with HCl. The aerosol particles were approximately spherical and nearly monodisperse with a mean diameter of 1.6 plus or minus 0.2 micron. The rate constant for the disappearance of atomic oxygen in the presence of NH4Cl aerosol was measured. No significant decrease was observed in the rate of disappearance of atomic oxygen in the presence of an (NH4)2SO4 aerosol at a concentration of 285 mg per cu m.
The influence of outgas conditions and temperature on the adsorptive properties of two aluminas Alon-c and Al6sG were studied using adsorption isotherm measurements. Alon-C and Al6SG were characterized using X-ray powder diffraction, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and BET nitrogen surface areas. Some of these techniques were applied to two other aluminas but no isotherm data was obtained. Isotherm data and techniques applied to each alumina are summarized in tabular form.
The rate of disappearance of atomic oxygen was measured at several pressures in a fast flow pyrex reactor system with its walls treated with (NH4)2SO4 (s), H2SO4 (l), and NH4CL (s). Atomic oxygen, P-3 was generated by dissociation of pure, low pressure oxygen in a microwave discharge. Concentrations of atomic oxygen were measured at several stations in the reactor system using chemiluminescent titration with NO2. Recombination efficiencies calculated from experimentally determined wall recombination rate constants are in good agreement with reported values for clean Pyrex and an H2SO4 coated wall. The recombination efficiency for (NH4)2SO4, results in a slightly lower value than for H2S04. A rapid exothermic reaction between atomic oxygen and the NH4Cl wall coating prevented recombination efficiency determination for this coating. The results show that the technique is highly useful for wall recombination measurements and as a means of extrapolating to the case of free stream aerosol-gas interactions.