65 records · Page 4
All sourcesNASA NTRSDOE OSTI
NASA NTRS1975

Effect of polymer properties and adherend surfaces on adhesion

The surface properties associated with good adhesive joints were evaluated in terms of application of adhesive bonding in aerospace technology. The physical and chemical nature was determined of Ti and Al adherend surfaces after various surface treatments, and the effects on fracture surfaces of high temperature aging, and variations in amide, anhydride, and solvent during polymer synthesis. The effects were characterized of (1) high temperature during shear strength testing, (2) fiber-reinforced composites as adherends, (3) acid/base nature of adherends, (4) aluminum powder adhesive filler, and (5) bonding pressure.

Dwight, D. W.↗
NASA NTRS1974

Interaction of gases with ablative composites. I - Ar, CO2, and N2

The sorption of argon, carbon dioxide, and nitrogen on two heat shield composites (SLA-561 and SLA-561V) and on the SLA components was measured over the pressure range of 0.001 to 760 torr and in the temperature range of 30 to 50 C. The sorption of the gases by both the composites and the components varied directly with pressure. The sorption of CO2 by the phenolic spheres and the silicone elastomer and of Ar by the silicone elastomer varied inversely with temperature. The mechanism involved in the gas sorption was primarily absorption.

King, C. A.↗
NASA NTRS1974

Interaction of gases with ablative composites. II - Water

An investigation was conducted to study the sorption of water on two ablative composites and their components as a function of pressure and temperature. A pressure range from 0.001 to 10 torr and a temperature range from 25 to 35 C were considered in the investigation. It was found that the sorption of water vapor by the ablative composites and their components varied directly with pressure. The components of the ablative composites included phenolic spheres, cork, a carbon-glass fiber mixture, glass spheres, silica fibers, and a silicone elastomer.

Honeycutt, R. H., III↗
NASA NTRS1972

Physisorption of argon on pyrex at low pressures.

Equilibrium pressures, numbers of argon atoms adsorbed per unit area and the DR parameters are given for argon adsorption on Pyrex for pressures ranging from 0.625 nanotorr to 12.7 microtorr at 77, 81.4, 87.8 and 90 K. Physical adsorption isotherms, Dubinin-Radushkevich plots, and isosteric heat curves are also given for argon on Pyrex.

Jen, J. S.-C.↗
NASA NTRS1971

Physisorption of Ar, Kr, CH4, and N2 on 304 stainless steel at very low pressures.

Determination of physisorption isotherms of these gases on stainless steel by pressure change measurements in very low pressure cryogenic baths where a steel nipple was brought in contact with the test gas at 77 to 90 K in a sealed constant-volume system. The position of the nipple in the gas was changed in such a manner that gas adsorption on a 47.5 sq cm area of the steel surface could be measured. The Dubinin-Radushkevich (DR) equation (1947) was used for an empirical description of isotherms at different temperatures. The mean adsorption energies calculated from the DR plots were 1290, 1545, 1490 and 1903 cal/mol for Ar, Kr, CH4 and N2, respectively, being about 10% higher than the corresponding values on Pyrex.

Troy, M.↗