Determination of the Wetting Angle of Germanium and Germanium-Silicon Melts on Different Substrate Materials

During Bridgman growth of semiconductors detachment of the crystal and the melt meniscus has occasionally been observed, mainly under microgravity (microg) conditions. An important factor for detached growth is the wetting angle of the melt with the crucible material. High contact angles are more likely to result in detachment of the growing crystal from the ampoule wall. In order to achieve detached growth of germanium (Ge) and germanium-silicon (GeSi) crystals under 1g and microg conditions, sessile drop measurements were performed to determine the most suitable ampoule material as well as temperature dependence of the surface tension for GeSi. Sapphire, fused quartz, glassy carbon, graphite, SiC, pyrolytic Boron Nitride (pBN), AIN, and diamond were used as substrates. Furthermore, different cleaning procedures and surface treatments (etching, sandblasting, etc.) of the same substrate material and their effect on the wetting behavior were studied during these experiments. pBN and AIN substrates exhibited the highest contact angles with values around 170 deg.

Kaiser, Natalie↗

NASA NTRS1999

Influence of Applied Thermal Gradients and a Static Magnetic Field on Bridgman-Grown GeSi Alloys

The effect of applied axial and radial thermal gradients and an axial static magnetic field on the macrosegregation profiles of Bridgman-grown GeSi alloy crystals has been assessed. The axial thermal gradients were adjusted by changing the control setpoints of a seven-zone vertical Bridgman furnace. The radial thermal gradients were affected by growing samples in ampoules with different thermal conductivities, namely graphite, hot-pressed boron nitride (BN), and pyrolytic boron nitride (PBN). Those samples grown in a graphite ampoule exhibited radial profiles consistent with a highly concave interface and axial profiles indicative of complete mixing in the melt. The samples grown in BN and PBN ampoules had less radial variation. Axial macrosegregation profiles of these samples fell between the predictions for a completely mixed melt and one where solute transport is dominated by diffusion. All of the samples were grown on Ge seeds. This resulted in a period of free growth until the Si concentration in the solid was in equilibrium with the Si concentration in the liquid. The length of crystal grown during this period was inversely proportional to the applied axial thermal gradient. Several samples were grown in an axial 5 Tesla magnetic field. Measured macroscopic segregation profiles on these samples indicate that the magnetic field did not, in general, reduce the melt flow velocities to below the growth velocities.

Volz, M. P.↗

NASA NTRS1999

Determination of the Solid/Liquid Interface Shape and Resultant Radial Homogeneity in Directionally Solidified Hg(0.89)Mn(0.11)Te

Directional solidification and interrupted directional solidification experiments were used to determine tile shape of the solid/liquid interface and the resultant radial homogeneity in Hg(0.89)Mg(0.11)Te. For directionally solidified samples solidified at a rate of 0.09 microns/sec in a thermal gradient of 83 C/cm, a maximum of 0.006 molar percent MnTe radial variation across the Hg0.89)Mn(0.11)Te boules at specific locations was determined using an FTIR technique. This FTIR evaluation of the radial homogeneity also indicated an asymmetrical, convex interface shape during solidification. The asymmetrical, convex shape of the growth interface was confirmed by interrupted directional solidification experiments. These were performed under the same growth conditions as the normally completed directional solidification experiments except that the samples were quenched before the final growth transient was reached. In these experiments, etching and scanning X-ray fluorescence were used to reveal the shape of the solid/liquid interface. Microprobe analysis of composition gradients across the interface was used to confirm the authors' previous work in evaluating the segregation coefficient of Hg(0.89)Mn(0.11)Te alloy. Microprobe analysis of the interface region of the interrupted growth sample revealed a dendritic structure containing secondary and tertiary dendritic arms.

Price, M. W.↗

NASA NTRS1999

Preliminary Concepts for the Materials Science Research Facility on the International Space Station

The Materials Science Research Facility (MSRF) is designed to accommodate the current and evolving cadre of peer-reviewed materials science investigations selected to conduct research in the microgravity environment of the International Space Station (ISS). The MSRF consists of modular autonomous Materials Science Research Racks (MSRR's). The initial MSRF concept consists of three Materials Science Research Racks (MSRR-1, MSRR-2, and MSRR-3) which will be developed for a phased deployment beginning on Utilization Flight 3. Each MSRR is a stand-alone autonomous rack and will be comprised of either on-orbit replaceable Experiment Modules, Module Inserts, investigation unique apparatus, or multi-user generic processing apparatus Each MSRR will support a wide variety of scientific investigations.

Cobb, S.D.↗

NASA NTRS1999

The Influence of Static and Rotating Magnetic Fields on Heat and Mass Transfer in Silicon Floating Zones

Heat and mass transfer in float-zone processing are strongly influenced by convective flows in the zone. They are caused by buoyancy convection, thermocapillary (Marangoni) convection, or artificial sources such as rotation and radio-frequency heating. Flows in conducting melts can be controlled by the use of magnetic fields, either by damping fluid motion with static fields or by generating a defined flow with rotating fields. The possibilities of using static and rotating magnetic fields in silicon floating-zone growth have been investigated by experiments in axial static fields up to 5 T and in transverse rotating magnetic fields up to 7.5 mT. Static fields of a few 100 mT already suppress most striations but are detrimental to the radial segregation by introducing a coring effect. A complete suppression of dopant striations caused by time-dependent thermocapillary convection and a reduction of the coring to insignificant values, combined with a shift of the axial segregation profile toward a more diffusion-limited case, is possible with static fields greater than or equal to 1 T. However, under certain conditions the use of high axial magnetic fields can lead to the appearance of a new type of pronounced dopant striations, caused by thermoelectromagnetic convection. The use of a transverse rotating magnetic field influences the microscopic segregation at quite low inductions, of the order of a few millitesla. The field shifts time- dependent flows and the resulting striation patterns from a broad range of low frequencies at high amplitudes to a few high frequencies at low amplitudes.

Croll, A.↗

NASA NTRS1998

Differential Thermal Analysis of Hg(1-x)Mn(x)Te Alloys in the X=0 to 0.3 Range

Understanding the experimental conditions necessary for the development of radial and axial compositional homogeneity in directionally solidified Hg(0.89)Mn(0.11)Te(MMT) crystals has been difficult due to the lack of segregation coefficient data on the Hg(1-x)Mn(x)Te alloy system in the X = 0 to 0.3 composition range. Determining segregation coefficient data from the available Hg(1-x)Mn(x)Te alloy phase equilibria data is not practical due to discrepancies in the shape of the reported solidus and liquidus curves in the X = 0 to 0.3 range. To resolve these discrepancies and to obtain segregation coefficient data which can be used to understand homogeneity in directionally solidified MMT crystals, the solidus and liquidus temperatures of seven Hg(1-x)Mn(x)Te alloys in the X = 0 to 0.3 range were determined using differential thermal analysis (DTA). The Hg(1-x)Mn(x)Te phase diagram constructed for the X = 0 to 0.3 range of this alloy system from the DTA measurements clarifies the shape of the solidus and liquidus curves in this range. The segregation coefficient for the Hg(1-x)Mn(x)Te system was found to vary from 5 to 4.4 as the solidus composition increased from 0-30 atomic percent MnTe. This information will be useful in the analysis of axial and radial homogeneity of directionally solidified MMT crystals.

Price, M. W.↗

NASA NTRS1998

Directional Solidification and Characterization of Hg(0.89) Mn(0.11)Te

Two boules of Hg(0.89)Mn(0.11)Te(MMT) were solidified using the vertical Bridgman-Stockbarger method. Translation rates of 0.09 and 0. 18 microns/s were used. The influence of growth rate on axial compositional homogeneity in the MMT boules was evaluated experimentally by conducting precision density measurements on radial slices taken from each boule. In addition, Plane Front Solidification theory and segregation coefficient (k) data for the Hg(1-x)Mn(x)Te system were used to fit theoretical composition profiles to the measured MMT axial composition profiles. The strong correlation between the measured and calculated MMT axial composition profiles indicates diffusion dominated axial solute redistribution in the boules under the applied growth conditions. The analysis of the MMT axial composition profiles by Plane Front Solidification theory allowed the calculation of the effective diffusion coefficient (D(eff) = 3.5 x l0(exp -5) sq cm/s). The k-values for the Hg(1-x)Mn(x)Te system and the D(sub eff) - value were then used to verify that both boules were solidified under conditions which did not exceed the Constitutional Supercooling Criteria under ideal conditions. Finally, a preliminary examination of the radial compositional variation in each MMT was made using Fourier Transform Infra-Red Spectroscopy (FTIR). The radial homogeneity in the MMT boules was found to be comparable for both translation rates.

Price, M. W.↗

NASA NTRS1998

A Numerical Investigation of the Effect of Thermoelectromagnetic Convection (TEMC) on the Bridgman Growth of Ge(1-x)Si(x)

Thermoelectric currents at the growth interface of GeSi during Bridgman growth are shown to promote convection when a low intensity axial magnetic field is applied. TEMC, typically, is characterized by a meridional flow driven by the rotation of the fluid; meridional convection alters composition of the melt, and shape of the growth interface substantially. TEMC effect is more important in micro-gravity environment than the terrestrial one, and can be used to control convection during the growth of GeSi. In this work, coupled thermo-solutal flow equations (energy, scalar transport, momentum and mass) are solved in tandem with Maxwell's equations to compute the thermo-solutat flow field, electric currents, and the growth-interface shape.

Yesilyurt, Serhat↗

NASA NTRS1998

Microstructural Development of Directionally Solidified Hg(1-x)Zn(x)Se Alloys

Hg(1-x)Zn(x)Se alloys have been studied as an alternative to HgCdTe for the detection of electromagnetic radiation, because the shorter ZnSe and HgSe bonds were predicted to improve lattice stability. Previous studies showed that optical properties were stable with time and that the microhardness was higher than for HgTe based alloys. However, for this material to be commercially viable, compositional variations must be reduced, and the distribution of defects induced by the growth process must be understood. The basic structural properties of bulk materials were characterized, and dislocation etch pit densities were measured to determine whether the addition of Zn to the HgSe lattice reduced the potential for dislocation formation. Hg(0.9)Zn(0.1)Se alloys were directionally solidified using a modified Bridgman-Stockbarger method and in an applied magnetic field. Radial compositional variations were greatly reduced when solidification occurred in an applied magnetic field. The combination of a convex liquid-solid interface shape and a method for reduced wetting produced boules that were a single crystal after reaching full diameter. Observed surface features indicated ampoule wetting could be eliminated using a graphite getter. Microstructural characteristics were greatly improved over HgCdTe alloys, In six boules, a total of only one twin was observed, and no inclusions were found. A method for polishing and producing dislocation etch pits was developed for these alloys, revealing dislocation etch pit densities one to two orders of magnitude less than HgTe based alloys. A kink in the thermal profile during processing of one boule generated more dislocations than did lattice mismatch due to compositional variations. The results of this investigation indicate this alloy has improved microstructural properties and resistance to dislocation formation compared with similar II-VI alloys, and should be further investigated for the detection of electromagnetic radiation.

Cobb, S. D.↗

NASA NTRS1998

Bridgman Growth of GeSi Alloys in a Static Magnetic Field

Ge(0.95)Si(0.050 alloy crystals have been grown by the vertical Bridgman technique, both with and without an axial 5 Tesla magnetic field. The crystals were processed in a constant axial thermal gradient and the effects of graphite, hot pressed boron nitride, and pyrolitic boron nitride ampoule materials on interface shapes and macrosegregation profiles were investigated. The sample grown in a graphite ampoule at 5 Tesla exhibited a macroscopic axial concentration profile close to that of complete mixing and strong striation patterns. In samples grown in boron nitride ampoules, both with and without a 5 Tesla magnetic field applied, measured macroscopic axial concentration profiles were intermediate between those expected for a completely mixed melt and diffusion-controlled growth, and striation patterns were also observed. Possible explanations for the apparent inability of the magnetic field to reduce the flow velocities to below the growth velocities are discussed, and results of growth experiments in pyrolitic boron nitride ampoules are also described.

Volz, M. P.↗

NASA NTRS1997

Bridgman Growth of Germanium

The high-magnetic-field crystal growth facility at the Marshall Space Flight Center will be briefly described. This facility has been used to grow bulk germanium by the Bridgman technique in magnetic fields up to 5 Tesla. The results of investigations of ampoule material on the interface shape and thermal field applied to the melt on stability against convection will be discussed.

Szofran, F. R.↗

NASA NTRS1996

Directional Solidification of Mercury Cadmium Telluride During the Second United States Microgravity Payload Mission (USMP-2)

As a solid solution semiconductor having, a large separation between liquidus and solidus, mercury cadmium telluride (MCT) presents a formidable challenge to crystal growers desiring an alloy of high compositional uniformity. To avoid constitutional supercooling during Bridgman crystal growth it is necessary to solidify slowly in a high temperature gradient region. The necessary translation rate of less than 1 mm/hr results in a situation where fluid flow induced by gravity on earth is a significant factor in material transport. The Advanced Automated Directional Solidification Furnace (AADSF) is equipped to provide the stable thermal environment with a high gradient, and the required slow translation rate needed. Ground based experiments in AADSF show clearly the dominance of flow driven transport. The first flight of AADSF in low gravity on USMP-2 provided an opportunity to test theories of fluid flow in MCT and showed several solidification regimes which are very different from those observed on earth. Residual acceleration vectors in the orbiter during the mission were measured by the Orbital Acceleration Research Experiment (OARE), and correlated well with observed compositional differences in the samples.

Gillies, D. C.↗

NASA NTRS1996

Convective Influence on Radial Segregation During Unidirectional Solidification of the Binary Alloy HgCdTe

In order to simulate the space environment for basic research into the crystal growth mechanism, Hg(0.8)Cd(0.2)Te crystals were grown by the vertical Bridgman-Stockbarger method in the presence of an applied axial magnetic field. The influence of convection, by magneto hydrodynamic damping, on mass transfer in the melt and segregation at the solid-liquid interface was investigated by measuring the axial and radial compositional variations in the grown samples. The reduction of convective mixing in the melt through the application of the magnetic field is found to have a large effect on radial segregation and interface morphology in the grown crystals. Direct comparisons are made with a Hg(0.8)Cd(0.2)Te crystal grown without field and also in the microgravity environment of space during the second United States Microgravity Payload Mission (USMP-2).

Watring, D. A.↗

NASA NTRS1996

The Influence of Reduced Gravity on the Crystal Growth of Electronic Materials

The imperfections in the grown crystals of electronic materials, such as compositional nonuniformity, dopant segregation and crystalline structural defects, are detrimental to the performance of the opto-electronic devices. Some of these imperfections can be attributed to effects caused by Earth gravity during crystal growth process and four areas have been identified as the uniqueness of material processing in reduced gravity environment. The significant results of early flight experiments, i.e. prior to space shuttle era, are briefly reviewed followed by an elaborated review on the recent flight experiments conducted on shuttle missions. The results are presented for two major growth methods of electronic materials: melt and vapor growth. The use of an applied magnetic field in the melt growth of electrically conductive melts on Earth to simulate the conditions of reduced gravity has been investigated and it is believed that the superimposed effect of moderate magnetic fields and the reduced gravity environment of space can result in reduction of convective intensities to the extent unreachable by the exclusive use of magnet on Earth or space processing. In the Discussions section each of the significant results of the flight experiments is attributed to one of the four effects of reduced gravity and the unresolved problems on the measured mass fluxes in some of the vapor transport flight experiments are discussed.

Su, Ching-Hua↗

NASA NTRS1995

Determination of the electrical conductivity of liquid Ge(0.95)Si(0.05)

We have measured the electrical conductivity of molten germanium-silicon Ge(0.95)Si(0.05) from the liquidus temperature (1050 C) up to 1220 C. The data were acquired with a unique apparatus which utilizes the standard four-probe technique. The basic unit consists of a fused silica enclosure that contains hermetic glass-to-tungsten seals that can support vacuum pressures down to 10(exp -7) Torr. With calibration, the measurement error for the low vapor pressure materials of this study was typically less than 7%. The temperature dependence of the electrical conductivity of a Ge(0.95)Si(0.05) melt was found to vary from approximately 22,300/ohm/cm at the liquidus temperature down to approximately 16,000/ohm/cm at 1220 C. The negative temperature coefficient as well as the magnitude of these data clearly indicate that the molten material is metallic in nature despite the semiconducting properties of the solid.

Rolin, T. D.↗

NASA NTRS1995

Experimental Studies on Mass Transport of Cadmium-Zinc Telluride by Physical Vapor Transport

Experimental studies on mass transport of ternary compound, Cd(1-x)Zn(x)Te by physical vapor transport (PVT) for source compositions up to X = 0.21 are presented. The effect of thermochemical (temperatures, vapor composition) and other factors (preparation of the source, crystal growth rate, temperature gradient) on composition and composition profiles of the grown crystals were investigated. A steep decrease in the mass flux with an increase in X(crystal) for X less than 0.1, and a difference in composition between the source and the deposited material have been observed. The composition profiles of the crystals were found to depend on the density and pretreatment of the source, and on the temperature gradient in the source zone. The homogeneity of the crystals improves at low undercoolings and/or when an appropriate excess of metal constituents is present in the vapor phase. The experimental results are in good agreement with our thermochemical model of this system.

Palosz, W.↗

NASA NTRS1995

Mass Flux of ZnSe by Physical Vapor Transport

Mass fluxes of ZnSe by physical vapor transport (PVT) were measured in the temperature range of 1050 to 1160 C using an in-situ dynamic technique. The starting materials were either baked out or distilled under vacuum to obtain near-congruently subliming compositions. Using an optical absorption technique Zn and Se, were found to be the dominant vapor species. Partial pressures of Zn and Se, over the starting materials at temperatures between 960 and 1140 C were obtained by measuring the optical densities of the vapor phase at the wavelengths of 2138, 3405, 3508, 3613, and 3792 A. The amount and composition of the residual gas inside the experimental ampoules were measured after the run using a total pressure gauge. For the first time, the experimentally determined partial pressures of Zn and Se, and the amount and composition of the residual gas were used in a one-dimensional diffusion limited analysis of the mass transport rates for a PVT system. Reasonable agreement between the experimental and theoretical results was observed.

Sha, Yi-Gao↗

NASA NTRS1994

Crystal growth of selected II-VI semiconducting alloys by directional solidification

A Hg(0.84)Zn(0.16)Te alloy crystal was back-melted and partially resolidified during the first United States Microgravity Laboratory (USML-1) mission in the Marshall Space Flight Center's Crystal Growth Furnace. The experiment was inadvertently terminated at about 30% of planned completion. Nonetheless, it was successfully demonstrated that HgZnTe alloy ingots partially grown and quenched on the ground can be back-melted and regrown in space under nearly steady state growth conditions. An identical 'ground-truth' experiment was performed following the mission. Preliminary results are presented for both crystals, as well as for a series of other crystals grown prior to the mission for the purposes of optimizing in-flight growth conditions.

Lehoczky, Sandor L.↗