Some effects of composition on friction and wear of graphite-fiber-reinforced polyimide liners in plain spherical bearings

Oscillating, plain spherical bearings with graphite-fiber-reinforced polyimide (GFRPI) liners were tested for friction and wear from 25 to 315 C. A condensation polymer was compared with an addition polymer, and a high-modulus fiber was compared with a lower cost, low-modulus fiber. All polymer-fiber combinations gave friction coefficients from 0.05 to 0.18 and low wear. Adding CdO and CdI2 reduced the wear of degassed bearings in dry air. These additives were not needed when the bearing liners contained adsorbed moisture. Although, at 25 C, MoS2 reduced the friction and wear of the base composite at unit loads above 70,000,000 N/m squared (10,000 psi), it had no beneficial effect at lighter loads.

Sliney, H. E.↗
NASA NTRS1978

Some load limits and self-lubricating properties of plain spherical bearings with molded graphite fiber reinforced polyimide liners to 320 C

Plain spherical bearings with molded liners of self-lubricating graphite fiber-polyimide composite were developed and their dynamic load capacities were determined. Liners were prepared by transfer molding a prepolymer resin-fiber mix into the space between the ball and outer race, the completing polymerization under heat and pressure. Bearing dynamic load capacities were in excess of 140 MPa (20,000 psi) from room temperature to 260 C and about 70 MPa (10,000 psi) at 320 C. Friction coefficients were about 0.20 at room temperatures and light loads and tended to decrease with increasing temperatures and loads to about 0.15. Thermal expansion of the liner at uniform bearing temperatures of 200 C or higher produced a bearing preload which could be alleviated by providing an initial internal diametral clearance of 0.05 to 0.10 mm.

Sliney, H. E.↗
NASA NTRS1978

Graphite-fiber-reinforced polyimide liners of various compositions in plain spherical bearings

Composites made of graphite-fiber-reinforced polyimide (GFRPI) with a fiber-resin ratio (by weight) of about 1 were evaluated as molded outer-race liners in plain spherical bearings. Several compositions were examined: two types of polyimide (addition and condensation polymers), two types of graphite fiber (high and low modulus) and four powder additives (CdO, CdI2, (CF1.1)n, and MoS2). Friction and wear were measured during oscillation at 25, 200, and 315 C. It is shown that all compositions provided good lubrication in dry air, that neither type of polyimide or graphite fiber nor the additives gave a clear advantage, and that wear rates were always higher during run-in, before conditions stabilized. It is concluded that GFRPI composites are self-lubricating under all but the most extreme moisture-free conditions at 25 C. The additives are helpful only with very high loads or extremely dry environments.

Sliney, H. E.↗
NASA NTRS1977

Friction and wear behavior of graphite fiber reinforced polyimide composites

The friction and wear rate characteristics of 50/50 (weight per cent) graphite fiber-polyimide composites were studied by sliding metallic hemispherically tipped riders against disks made from the composites. Two different polyimides and two different graphite fibers were evaluated. Also studied were such variables as the effect of adding 10 per cent weight additions of powdered (CF-1.1)n, CdI2, or CdO, the effect of moisture in an air atmosphere, the effect of temperature, and the effect of different sliding speeds. In general, wear to the metallic riders was negligible and composite wear increased at a constant rate as a function of number of sliding cycles.

Fusaro, R. L.↗
NASA NTRS1977

Friction and wear behavior of graphite fiber reinforced polymide composites

The friction and wear rate characteristics of 50/50 (weight percent) graphite fiber polyimide composites were studied by sliding metallic hemispherically tipped riders against disks made from the composites. Two different polyimides and two different graphite fibers were evaluated. Also studied were such variables as the effect of moisture in an air atmosphere; the effect of temperature; and the effect of different sliding speeds. In general, wear to the the metallic riders was negligible, and composite wear increased at a constant rate as a function of number of sliding cycles.

Fusaro, R. L.↗
NASA NTRS1976

Dynamics of solid lubrication as observed by optical microscopy

A bench metallograph was converted into a 'micro contact imager' by the addition of a tribometer employing a steel ball in sliding contact with a glass disk. The sliding contact was viewed in real time by means of projection microscope optics. The dynamics of abrasive particles and of solid lubricant particles within the contact were observed in detail. The contact was characterized by a constantly changing pattern of elastic strain with the passage of surface discontinuities and solid particles. Abrasive particles fragmented upon entering the contact, embedded in one surface and scratched the other; in contrast, the solid lubricant particles flowed plastically into thin films. The rheological behavior of the lubricating solids gave every appearance of a paste-like consistency within the Hertzian contact.

Sliney, H. E.↗
NASA NTRS1976

Bearing material

A composite material is described which will provide low friction surfaces for materials in rolling or sliding contact and is self-lubricating and oxidation resistant up to and in excess of about 930 C. The composite is comprised of a metal component which lends strength and elasticity to the structure, a fluoride salt component which provides lubrication and, lastly, a glass component which not only provides oxidation protection to the metal but may also enhance the lubrication qualities of the composite.

Sliney, H. E.↗
NASA NTRS1976

Dynamics of solid lubrication as observed by optical microscopy

A bench metallograph was converted into a micro contact imager by the addition of a tribometer employing a steel ball in sliding contact with a glass disk. The sliding contact was viewed in real time by means of projection microscope optics. The dynamics of abrasive particles and of solid lubricant particles within the contact were observed in detail. The contact was characterized by a constantly changing pattern of elastic strain with the passage of surface discontinuities and solid particles. Abrasive particles fragmented upon entering the contact, embedded in one surface and scratched the other; in contrast, the solid lubricant particles flowed plastically into thin films. The rheological behavior of the lubricating solids gave every appearance of a paste-like consistency within the Hertzian contact.

Sliney, H. E.↗
NASA NTRS1975

Dynamic load capacities of graphite fiber: Polyimide composites in oscillating plain bearings to 340 C (650 F)

Load capacities were determined for plain spherical bearings with self-lubricating spherical elements of graphite-fiber-reinforced-polyimide, and for plain cylindrical bearings with thin-wall liners of the composite in the bearing bores. Composites consisted of a 1-to-1 weight ratio of graphite fibers and polyimide. Oscillation was at an amplitude of + or - 15 deg at a frequency of 1 hertz. Bearings with composite ball material had a load capacity of approximately 69 MN/sq m (10 000 psi) at room temperature 25 MN/sq m (3600 psi) at 340 C (650 F). Bearings with thin-wall composite liners had much higher load capacities of 280 MN/sq m (40 000 psi) at room temperature amd 240 MN/sq m (35 000 psi) at 320 C (600 F). Friction coefficients were in the range of 0.12 to 0.19. The addition of 10 wt.% graphite fluoride solid lubricant to the composition of the thin-wall liners reduced friction coefficients into the range of 0.10 to 0.12.

Sliney, H. E.↗
NASA NTRS1975

Performance of graphite fiber-reinforced polyimide composites in self-aligning plain bearings to 315 C

A 50/50 (weight percent) composite of graphite fibers and polyimide was studied in self-aligning plain bearings oscillating + or - 15 degrees at 1 hz. The friction coefficient was 0.15 + or - 0.05 at 250 C, and 0.05 + or - 0.02 at 315 C. Best results were obtained with a molded composite liner with chopped graphite fibers randomly oriented in the composite. The specific wear rate is given. It was found that the dynamic unit load capacity was higher for a composite bushing (thin liner), than for a composite ball.

Sliney, H. E.↗
NASA NTRS1975

Plasma-sprayed, self-lubricating coatings for use from cryogenic temperatures to 870 deg C (1600 deg F)

A plasma-sprayed coating is described with good lubricating properties over a wide temperature range. The coating, designated NASA LUBE PS101, contains silver, nichrome, calcium fluoride, and an oxidation protective glass. Oscillating tests were conducted of self-aligning, plain cylindrical bearings, in which the bore was lined with 0.025 cm (0.010 in.) thick coatings of PS101; these were conducted at a radial load of 3.5 x 10 to the 7th power N/sq m (5000 psi) in nitrogen gas at -107 C (-160 F), in vacuum at room temperature, and in air from room temperature to 870 C (1600 F). Friction coefficients were less than 0.25 in all cases and wear rates were low. The coating is not brittle, and it has adequate oxidation resistance in air to at least 870 C.

Sliney, H. E.↗
NASA NTRS1974

Plasma-sprayed metal-glass and metal-glass fluoride coatings for lubrication to 900 C

Plasma-sprayed composites, which have good oxidation resistance and self-lubricating characteristics to 900 C, were developed. The composites are a nichrome matrix containing dispersed glass for oxidation protection and calcium fluoride for lubrication; they are applied to bearing surfaces by plasma spraying layers about 0.050 cm thick which are then machined to 0.025 cm. Oscillating bearing tests were performed in air to 900 C at unit radial loads up to 5000 psi and a thrust load of 440 lb. Bearings with a composite liner in the bore were in good condition after over 50,000 oscillating cycles accumulated during repeated bearing temperature cycles between 25 and 900 C.

Sliney, H. E.↗
NASA NTRS1974

Self-lubricating plasma-sprayed composites for sliding contact bearings to 900 C

Plasma-sprayed composites which have good oxidation-resistance and self-lubricating characteristics to 900 C were developed. The composites are a Nichrome matrix containing dispersed glass for oxidation protection and calcium fluoride for lubrication. They are applied to bearing surfaces in layers about 0.050 cm thick by plasma-spraying; the layers are then machined to a thickness of 0.025 cm. Oscillating bearing tests were performed in air to 900 C at unit radial loads up to 3.5 times 10 to the 7th power Newtons per square meter (5000 psi) and a thrust load of 1960 Newtons (440 lb). Bearings with a composite liner in the bore were in good condition after over 50,000 oscillating cycles accumulated during repeated bearing temperature cycles between 25 and 900 C.

Sliney, H. E.↗
NASA NTRS1974

Tribological properties of self-lubricating fluoride-metal composites to 900 C (1650 F): A review and some new developments

The friction and wear behavior of some fluoride-metal, self-lubricating composites are summarized. Fluoride-infiltrated sintered nickel alloy composites and plasma-sprayed, co-deposited fluoride-nickel alloy composites are described. The importance of proper surface-conditioning of the composites is stressed. Performance of fluoride-metal composites in some machine application evaluation is discussed.

Sliney, H. E.↗