Surface analysis of graphite fiber reinforced polyimide composites

Several techniques have been used to establish the effect of different surface pretreatments on graphite-polyimide composites. Composites were prepared from Celion 6000 graphite fibers and the polyimide LARC-160. Pretreatments included mechanical abrasion, chemical etching and light irradiation. Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were used in the analysis. Contact angle of five different liquids of varying surface tensions were measured on the composites. SEM results showed polymer-rich peaks and polymer-poor valleys conforming to the pattern of the release cloth used durng fabrication. Mechanically treated and light irradiated samples showed varying degrees of polymer peak removal, with some degradation down to the graphite fibers. Minimal changes in surface topography were observed on concentrations of surface fluorine even after pretreatment. The light irradiation pretreatment was most effective at reducing surface fluorine concentrations whereas chemical pretreatment was the least effective. Critical surface tensions correlated directly with the surface fluorine to carbon ratios as calculated from XPS.

Messick, D. L.↗
NASA NTRS1983

Hot-Melt Adhesive Attachment System

Adhesive system is as effective on Earth as in space. Fiberglass cloth mounted in head assembly. When adhesive reaches melt temperature head is attached to metals composites, ceramics, and other materials. Once attached, head cooled rapidly for quick stick. Used to tether tools or attach temporary scaffolding to walls, buildings, or beams.

Fox, R. L.↗
NASA NTRS1983

Recharging "Hot-Melt" Adhesive Film

Technique for recharging surface with "hot-melt" film makes use of one sided, high-temperature, pressure-sensitive adhesive tape. Purpose of the one-sided tape is to hold hot-melt charge in place until fused to surface. After adhesive has fused to surface and cooled, tape is removed, leaving adhesive on surface.

Progar, D. J.↗
NASA NTRS1983

Surface analysis of grapite fiber reinforced polyimide composites. I

The results of experimental analyses of the effects of pretreatment on bonding between composite materials are reported. The materials comprised graphite fibers in a polyimide matrix. The surfaces were bonded as-received or subjected to grit blasting, bead blasting, hand sanding, washes with ethanolic KOH, NH2NH2-H2O or H2SO4 + 0.30 H2O2 or flashblasting. SEM and X-ray photoelectron spectroscopy revealed fluorine contents in the as-received samples. Contact angles were determined by means of five different liquids with various surface tensions. The flashblast technique removed all fluorine from the samples. Low critical surface tensions were found in the composite surfaces with high fluorine concentrations. The surface scanning techniques are concluded to be useful for studying factors influencing the strength and durability of adhesively bonded composites.

Messick, D. L.↗
NASA NTRS1981

A novel addition polyimide adhesive

An addition polyimide adhesive, LARC 13, was developed which shows promise for bonding both titanium and composites for applications which require service temperatures in excess of 533 K. The LARC 13 is based on an oligomeric bis nadimide containing a meta linked aromatic diamine. The adhesive melts prior to polymerization due to its oligomeric nature, thereby allowing it to be processed at 344 kPa or less. Therefore, LARC 13 is ideal for the bonding of honeycomb sandwich structures. After melting, the resin thermosets during the cure of the nadic endcaps to a highly crosslinked system. Few volatiles are evolved, thus allowing large enclosed structures to be bonded. Preparation of the adhesive as well as bonding, aging, and testing of lap shear and honeycomb samples are discussed.

St.clair, T. L.↗
NASA NTRS1979

LARC-13 polyimide adhesive bonding

The development of an addition-curing polyimide adhesive suitable for low pressure bonding without the generation of volatiles during cure is reported. LARC-13 is designed for bonding of polyimide matrix composites and of titanium to be used above 500 F, and is based on an oligomeric bis-nadimide which allows its processing at 50 psi or less, making it suitable for the bonding of fragile honeycomb sandwich structures. Few volatiles are evolved during its cure allowing large enclosed structures to be bonded, and it has high room and elevated temperature strengths and good strength retention after short terms up to 1100 F. LARC-13 was successfully used to bond the outer and inner skins of a polyimide/graphite wing shear panel for 500 F use, and for a short-term exposure up to 1100 F. Preparation of the adhesive, bonding, aging, and testing of lap shear and honeycomb samples are discussed.

Saint Clair, T. L.↗
NASA NTRS1979

High temperature adhesives for bonding composites

Selection and evaluation of candidate adhesives for bonding composites are described. These are based on mechanical property tests (lap shear and flatwise tensile) and processibility. Consideration is given to composite-to-composite, composite-to-titanium, and honeycomb sandwich structures.

Progar, D. J.↗
NASA NTRS1977

Polyimide adhesives

A process was developed for preparing aromatic polyamide acids for use as adhesives by reacting an aromatic dianhydride to an approximately equimolar amount of an aromatic diamine in a water or lower alkanol miscible ether solvent. The polyamide acids are converted to polyimides by heating to the temperature range of 200 - 300 C. The polyimides are thermally stable and insoluble in ethers and other organic solvents.

Progar, D. J.↗
NASA NTRS1977

High temperature composite bonding with PPQ

A polyphenylquinoxaline (PPQ) was evaluated as a high temperature adhesive for joining polyimide graphite laminates (PI/Gr) to PI/Gr, PI/Gr to titanium (Ti), and Ti to Ti. The effect of polymer molecular weight, processing parameters, 3-day water boil, and 316 C (600 F) aging in air upon lap shear strengths is presented. Titanium to Ti climbing drum peel and PI/Gr to polyimide glass honeycomb flatwise tensile strengths are also presented.

Hergenrother, P. M.↗
NASA NTRS1975

Process for preparing polyimide adhesives

High bonding strengths are obtained for metals and fiber-reinforced organic resin composites with no significant loss in thermo-oxidative stability of the adhesive resin.

Progar, D. J.↗
NASA NTRS1975

Preliminary evaluation of a novel polyimide adhesive for bonding titanium and reinforced composites

A novel polyimide has been developed which shows promise as an adhesive for bonding titanium-to-titanium, titanium-to-polyimide composite and composite-to-composite with excellent lap shear strengths at room temperature and moderate strengths at 288 C. The adhesive is a high molecular weight polyimide made from commercially available monomers. The use of an ether as the solvent for the polymerization and for application of the polyamic acid enhanced the adhesive properties of the polyimide. At room temperature, P13N/glass composite bonded to titanium or to itself failed primarily in the surface layer of the composite, whereas at 260 C the failure was primarily cohesive. Failure of the P13N/unidirectional HT-S graphite composite-to-titanium bonded composites occurred in the composite regardless of the test temperature. Preliminary shear results with cross-plied P13N/HT-S graphite composite-to-composite specimens showed failure in the bonded surface fibers.

Progar, D. J.↗
NASA NTRS1974

Polyimide adhesives

A process of preparing aromatic polyamide-acids for use as adhesives is described. An equimolar quantity of an aromatic dianhydride is added to a stirred solution of an aromatic diamine in a water or alcohol-miscible ether solvent to obtain a viscous polymer solution. The polymeric-acid intermediate polymer does not become insoluble but directly forms a smooth viscous polymer solution. These polyamic-acid polymers are converted, by heating in the range of 200-300 C and with pressure, to form polyimides with excellent adhesive properties.

Progar, D. J.↗
NASA NTRS1973

Applying high-emittance and solar-absorptance coating to aluminum

Coated surface withstands space environment with negilgible change in radiation characteristics and physical properties. Process can be used with any porous substance, as long as pores are large enough to allow molecules of reacting solutions to enter and yet not so large as to allow nickel sulfide to be leached out of pores before sealing.

Progar, D. J.↗
NASA NTRS1971

Vacuum and ultraviolet radiation effects on binders and pigments for spacecraft thermal control coatings

An evaluation of several silicone resin binders and powdered inorganic pigments for potential use in spacecraft thermal-control paint formulations is presented. The pigments were selected on the basis of a hypothesis relating the heat of formation of a compound to the compound's resistance to ultra-radiation-induced degradation. Reflectance measurements were made in situ to determine degradation rates due to ultraviolet radiation. The tested polydimethylsiloxane resins were not significantly affected by long exposures to ultraviolet radiation. All the pigments, which were dispersed in a polydimethylsiloxane resin, were degraded by ultraviolet radiation as determined by an increase of solar absorptance. For the materials evaluated in this study, no evidence was found to indicate that pigments with high heats of formation were resistant to ultraviolet degradation.

Progar, D. J.↗