All sourcesNASA NTRSDOE OSTI
NASA NTRS1986

Tetraglycidyl epoxy resins and graphite fiber composites cured with flexibilized aromatic diamines

Studies were performed to synthesize new ether modified, flexibilized aromatic diamine hardeners for curing epoxy resins. The effect of moisture absorption on the glass transition temperatures of a tetraglycidyl epoxy, MY 720, cured with flexibilized hardeners and a conventional aromatic diamine was studied. Unidirectional composites, using epoxy-sized Celion 6000 graphite fiber as the reinforcement, were fabricated. The room temperature and 300 F mechanical properties of the composites, before and after moisture exposure, were determined. The Mode I interlaminar fracture toughness of the composites was characterized using a double cantilever beam technique to calculate the critical strain energy release rate.

Delvigs, P.↗
NASA NTRS1985

PMR polyimides from solutions containing mixed endcaps

Previous studies have shown that partial substitution of p-aminostyrene (PAS) for the monomethylester of endo-5-norbornene-2, 3-dicarboxylic acid (NE) lowered the cure temperature of PMR polyimides from 316 to 260 C, but the modified PMR polyimides required higher compression-molding pressures than state-of-the-art PMR-15. In this study PMR polyimides are prepared employing three encaps: NE, PAS, and endo-N-phenyl-5-norbornene-2,3-dicarboximide (PN). The effect of PN addition on the processing characteristics and glass transition temperatures of graphite fiber-reinforced PMR composites is studied. The room temperature and short-time 316 C mechanical properties of the composites are determined. The weight loss and mechanical property retention characteristics of the composites after exposure in air at 316 C are also determined.

Delvigs, P.↗
NASA NTRS1985

The 371 deg C mechanical properties of graphite/polyimide composites

A series of condensation polyimides based on pyromellitic dianhydride is synthesized and evaluated for potential application at 371 C. Several three-and four-ring benzenoid diamine systems containing oxygen bridging groups are investigated. Thermomechanical analysis of neat resin specimens indicate that the polyimide prepared from the dimethyl ester of pyrometallitic acid (PMDE) and 2,2-bis4-(4'-aminophenoxy) phenyl]-1,1,1,3,3,3- hexafluoropropane (BDAF) is the only resin system which has a glass transition temperature (Tg) above 371 C. The Tg of the PMDE/BDAF polyimide is found to be 390 C after a postcure air at 371 C for 24 hr. Unidirectional composites are fabricated from the PMDE/BDAF system and unsized Celion 6000 graphite fibers. Final cure temperatures in the range of 371 to 427 C with an applied pressure of 10.34 to 13.78 MPa are investigated. The void content of the composites ranges from 4.6 to 8.6 percent. Composites cured at 399 C under a pressure of 10.34 MPa and postcured in air at 371 C for 24 hr exhibit the highest 371 C interlaminar shear strength (ILSS, 40.7 MPa) and flexural strength (758 MPa). The thermo-oxidative stability of the composites is determined by subjecting specimens to isothermal exposure at 371 C in air at atmospheric pressure, as well as a pressure of 0.52 MPa. Specimens exposed at atmospheric pressure exhibit a weight loss of 12 percent after 200 hr of exposure and 88 percent retention of its original 371 C ILSS. In contrast, the specimens exposed at 0.52 MPa pressure exhibit a comparable weight loss after only 72 hr, and a 71 percent retention of its original 371 C ILSS.

Delvigs, P.↗
NASA NTRS1983

Lower-curing-temperature PMR polyimides

Partial substitution of a p-aminostyrene end-cap for the monomethyl ester of 5-norbornene-2, 3-dicarboxylic acid lowered the final cure temperature of typical PMR resins from 600 F to 500 F. The weight loss characteristics of neat resins and graphite fiber composites prepared by using the mixed end-cap approach were determined at 600 F. The room temperature and short-time elevated temperature mechanical properties of the composites at 550 F and 600 F were determined. The mechanical property retention characteristics of the composites at 550 F and 600 F are discussed. Previously announced in STAR as N83-10118

Delvigs, P.↗
NASA NTRS1982

Lower-curing-temperature PMR polyimides

Partial substitution of a p-aminostyrene end-cap for the monomethyl ester of 5-norbornene-2, 3-dicarboxylic acid lowered the final cure temperature of typical PMR resins from 600 F to 500 F. The weight loss characteristics of neat resins and graphite fiber composites prepared by using the mixed end-cap approach were determined at 600 F. The room temperature and short-time elevated temperature mechanical properties of the composites at 550 F and 600 F were determined. The mechanical property retention characteristics of the composites at 550 F and 600 F are discussed.

Delvigs, P.↗
NASA NTRS1982

Low temperature cross linking polyimides

A polyimide is formed by cross linking a prepolymer formed by reacting a polyfunctional ester, a polyfunctional amine, and an end-capping unit. By providing an end-capping unit, the prepolymer is curable at a relatively low temperature of about 175 to 245 C.

Serafini, T. T.↗
NASA NTRS1982

PMR polyimides-review and update

Fiber reinforced PMR polyimides are finding increased acceptance as engineering materials for high performance structural applications. Prepreg materials based on this novel class of highly processable, high temperature resistant polyimides are commercially available and the PMR concept is used by other investigators. The current status of first and second generation PMR polyimides were reviewed. Emphasis is given to the chemistry, processing and applications of the first generation material known as PMR-15.

Serafini, T. T.↗
NASA NTRS1981

Curing agent for polyepoxides and epoxy resins and composites cured therewith

A curing for a polyepoxide is described which contains a divalent aryl radical such as phenylene a tetravalent aryl radical such as a tetravalent benzene radical. An epoxide is cured by admixture with the curing agent. The cured epoxy product retains the usual properties of cured epoxides and, in addition, has a higher char residue after burning, on the order of 45% by weight. The higher char residue is of value in preventing release to the atmosphere of carbon fibers from carbon fiber-epoxy resin composites in the event of burning of the composite.

Serafini, T. T.↗
NASA NTRS1981

Composition and method for making polyimide resin-reinforced fabric

A composition for making polyimide resin reinforced fibers or fabric is discussed. The composition includes a polyfunctional ester, a polyfunctional amine, and an end capping agent. The composition is impregnated into fibers or fabric and heated to form prepreg material. The tack retention characteristics of this prepreg material are improved by incorporating into the composition a liquid olefinic material compatible with the other ingredients of the composition. The prepreg material is heated at a higher temperature to effect formation of the polyimide resin and the monomeric additive is incorporated in the polyimide polymer structure.

Serafini, T. T.↗
NASA NTRS1981

High char yield epoxy curing agents

Class of imide-amine curing agents preserves structural integrity, prevents fiber release, and is fully compatible with conventional epoxy resins; agents do not detract from composite properties while greatly reducing char yield. Materials utilizing curing are used in aerospace, automotive, and other structural components where deterioration must be minimized and fiber release avoided in event of fire.

Delvigs, P.↗
NASA NTRS1981

Lower-curing-temperature PMR polyimides

Studies were performed to achieve a lower-curing-temperature PMR polyimide. The use of m-aminostyrene as the end-cap instead of the monoalkyl ester of 5-normbornene-2,3 dicarboxylic acid was investigated in typical PMR formulations. Model compound studies were also performed. Differential scanning calorimetry studies were performed on model compounds and neat resins to establish their melting and curing characteristics. The elevated temperature weight loss characteristics of neat resins and graphite fiber composites were determined. The room temperature and short-time 260 C (500 F) mechanical properties of the composites were also determined. The use of m-aminostyrene end-caps reduced the final cure temperature of PMR resins by about 55 C (100 F), but the composites prepared with these resins are limited to use temperatures of about 260 C (500 F).

Serafini, T. T.↗
NASA NTRS1979

Effects of graphite fiber stability on the properties of PMR polyimide composites

The effect of the stability of graphite fibers on composite properties after exposure in air at 600 F was investigated. Composites were fabricated from PMR-15 and PMR-2 monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at that temperature compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗
NASA NTRS1979

High char imide-modified epoxy matrix resins

The synthesis of a class of bis(imide-amine) curing agents for epoxy matrix resins is discussed. Glass transition temperatures and char yield data of an epoxy cured with various bis(imide-amines) are presented. The room temperature and 350 F mechanical properties, and char yields of unidirectional graphite fiber laminates prepared with conventional epoxy and imide-modified epoxy resins are presented.

Serafini, T. T.↗
NASA NTRS1979

Effects of graphite fiber stability on the properties of PMR polyimide composites

Studies were performed to investigate the effect of the stability of graphite fibers on composite properties after exposure in air at 600 F. Composites were fabricated from PMR-15 and PMR-II monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at 600 F compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗
NASA NTRS1979

High char imide-modified epoxy matrix resins

Studies were performed to synthesize a novel class of bis (imide-amine) curing agents for epoxy matrix resins. Glass transition temperatures and char yield data of an epoxy cured with various bis (imide-amines) are presented. The room temperature and 350 F mechanical properties, and char yields of unidirectional graphite fiber laminates prepared with conventional epoxy and imide-modified epoxy resins are presented.

Serafini, T. T.↗
NASA NTRS1978

PMR Polyimide prepreg with improved tack characteristics

Current PMR Polyimide prepreg technology utilizes methanol or ethanol solvents for preparation of the PMR prepreg solutions. The volatility of these solvents limits the tack and drape retention characteristics of unprotected prepreg exposed to ambient conditions. Studies conducted to achieve PMR 15 Polyimide prepreg with improved tack and drape characteristics are described. Improved tack and drape retention were obtained by incorporation of an additional monomer. The effects of various levels of the added monomer on the thermo-oxidative stability and mechanical properties of graphite fiber reinforced PMR 15 composites exposed and tested at 316 C (600 F) are discussed.

Serafini, T. T.↗
NASA NTRS1976

Effects of tetraamine crosslinking agents on the thermomechanical properties of PMR polyimide composites

The effects were investigated of partial substitution of tetraamine crosslinking agents for diamine reactants on the thermomechanical properties of PMR polyimide resins and graphite fiber-reinforced composites. The effect of tetraamine content on isothermal weight loss, glass transition, and softening temperatures of neat resin samples is discussed. Composites were fabricated using PMR methodology. Monomeric solution of various stoichiometric ratios was used to impregnate Hercules HTS graphite fiber. The mechanical property retention characteristics of the composites at 316 C (600 F) are described.

Delvigs, P.↗