Lower-curing-temperature PMR polyimides

Abstract

Studies were performed to achieve a lower-curing-temperature PMR polyimide. The use of m-aminostyrene as the end-cap instead of the monoalkyl ester of 5-normbornene-2,3 dicarboxylic acid was investigated in typical PMR formulations. Model compound studies were also performed. Differential scanning calorimetry studies were performed on model compounds and neat resins to establish their melting and curing characteristics. The elevated temperature weight loss characteristics of neat resins and graphite fiber composites were determined. The room temperature and short-time 260 C (500 F) mechanical properties of the composites were also determined. The use of m-aminostyrene end-caps reduced the final cure temperature of PMR resins by about 55 C (100 F), but the composites prepared with these resins are limited to use temperatures of about 260 C (500 F).