Thermochemistry of Protective Coatings and Molten Silicate Debris

The durability of gas-turbine engine components can be significantly affected by the ingestion of siliceous particles, which can melt at high temperature and corrode protective coatings that are essential for long life requirements. The silicate debris consists mainly of CaO-MgO-Al2O3-SiO2 (CMAS) and is usually ingested by aircraft engines during and after take-off, sticking to their hot surfaces and resulting in the formation of calcium rare-earth silicate oxyapatites. The thermochemistry of coatings and their reaction products with molten silicate debris are crucial to understand in order to improve the durability of gas-turbine engines. Here we discuss results of high temperature drop solution calorimetry, drop-and-catch calorimetry (DnC) and differential thermal analysis (DTA) techniques for the thermodynamic properties of both thermal barrier coatings (TBCs) and environmental barrier coatings (EBCs) and their reaction with CMAS compositions. The enthalpies of solution of Y2Si2O7, Yb2Si2O7, 31YSZ, and 16RESZ based coatings and the oxyapatite are moderately positive. However, oxyapatite formation is only favorable over coating dissolution in terms of enthalpy for 7YSZ. The enthalpies of mixing between the coatings and the molten silicate are less exothermic for Yb2Si2O7 and CaYb4Si3O13 than for 7YSZ, indicating lower energetic stability of the latter against molten silicate corrosion. We also report for the first time the calorimetric measurements of the enthalpies of formation of rare-earth silicate based EBC coatings and oxyapatites (rare-earth, RE = Y, Yb, Gd, Dy, Er, Nd and Sm).

Costa, Gustavo↗
NASA NTRS2020

Calorimetric Measurements of the Thermodynamic Properties of RE-Silicate Coating Materials

Thermodynamic quantities of coatings materials and siliceous debris-induced corrosion products are crucial to understand in order to develop mitigation strategies necessary to improve the durability of gas-turbine engines. Siliceous induced corrosion can occur when debris consisting mainly of CaO-MgO-Al2O3-SiO2 (CMAS) is ingested by aircraft engines during and after take-off, which sticks to hot surfaces and forms calcium rare-earth silicate oxyapatites. In this work, high-temperature oxide melt drop solution calorimetry (HT drop solution calorimetry) was used to obtain the enthalpies of formation for RE silicate (RE2Si2O7, RE2SiO5 where RE = Yb, Er, Y, Dy, Nd, Lu and Gd) environmental barrier coatings (EBCs) and the calcium RE silicate oxyapatite Ca2RE8(SiO4)6O2 (RE = Yb, Er, Y, Dy, Nd, Gd and Sm) corrosion products. Trends in the enthalpy of formation as a function of the ionic potential of the rare-earth cations in their related crystallographic sites are discussed.

Costa, Gustavo↗
NASA NTRS2025

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-AluminoSilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures. CYbS apatite powder was synthesized from the constituent oxides via solid state reaction method. Hot pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high angle annular dark field imaging, selected area electron diffraction and energy dispersive X-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1-50 h at 1200 °C and those heat treated at 1300 °C for 1 h. Residual CMAS was Ca-depleted when cyclosilicate was present. Dendritic wollastonite CaSiO 3 was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

X-ray diffraction↗
NASA NTRS2026

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures for consideration as a thermal and environmental barrier coating (T/EBC) material. CYbS apatite powder was synthesized from the constituent oxides via a solid-state reaction method. Hot-pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high-angle annular dark-field imaging, selected area electron diffraction, and energy dispersive x-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1 to 50 h at 1200 °C as well as in those heat treated at 1300 °C for 1 h. Residual CMAS was depleted of Ca when cyclosilicate was present. Dendritic wollastonite (CaSiO3) was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

Narottam P Bansal↗