Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS)

Narottam P Bansal·Anita Garg·Wayne D Jennings·Gustavo Costa
View original source ↗Read source document ↗Export metadata ↓

Abstract

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures for consideration as a thermal and environmental barrier coating (T/EBC) material. CYbS apatite powder was synthesized from the constituent oxides via a solid-state reaction method. Hot-pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high-angle annular dark-field imaging, selected area electron diffraction, and energy dispersive x-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1 to 50 h at 1200 °C as well as in those heat treated at 1300 °C for 1 h. Residual CMAS was depleted of Ca when cyclosilicate was present. Dendritic wollastonite (CaSiO3) was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

Keep this discovery

BibTeXRIS

Narottam P Bansal, Anita Garg, Wayne D Jennings, Gustavo Costa. 2026-08-01. Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS). https://ntrs.nasa.gov/citations/20260006201

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI1961

Laboratory Development of a Pot Calcination Process for Converting Liquid Wastes to Solids

Simulated Darex, Purex, Thorex, and TBP-25 wastes were batch-evaporated and calcined to solids. The weight of residue was decreased to ~ 8% of the original waste for Darex, to ~ 4% for Purex, to ~ 2% for Thorex, and ~ 7% for TBP-25 by calcination to 1200°C. Semicontinuous evaporation and calcination to solids at 900°C of Darex and Purex wastes gave volume reduction factors of ~ 8 and 7 to 10, respectively. The nitrate contents of the residues from batch calcination to 800°C were from ~ 0.07 to 0.5 wt % while the nitrate contents of the residues from semicontinuous calcination to 900°C were from ~ 0.1 to 0.7 wt %. Sodium, calcium, and magnesium additives to Purex waste decreased the percent of sulfate volatilized into the condensate from ~ 30% to <0.5%. Replacement of the atmosphere above the waste with nitric oxide decreased ruthenium volatility from 50 to 60% of that originally present in Purex waste to 0.5 to 3.5%. The thermal conductivities for the calcined wastes, measured in situ, were all >0.1 Btu/hr ft °F at ~ 400°F and increased almost linearly with increasing temperature to >0.3 Btu/hr ft °F at ~ 1600°F in all cases studied.

052001* -- Nuclear Fuels-- Waste Processing↗
DOE OSTI2026

Application of Ibuprofen Sodium Dihydrate for Thermochemical Energy Storage

Thermochemical energy storage (TCES) offers a transformative approach to address grid instability by harnessing reversible chemical reactions for efficient heat storage and release. Here, we introduce pharmaceutical organic salt hydrates as a class of materials with exceptional performance for low-grade waste heat recovery. We demonstrate ibuprofen sodium dihydrate (ISD) as an example organic hydrate exhibiting a dehydration temperature range of 60-110 °C and a remarkable dehydration enthalpy of up to 59.5 kJ/mol of water, ideally suited for capturing industrial and residential waste heat. Using rigorous multimodal characterization, including thermogravimetric analysis, differential scanning calorimetry, in-situ FTIR, in-situ PXRD, and NMR, we demonstrate ISD's superior thermal, chemical, and structural stability over 150 hydration-dehydration cycles, achieving an unprecedented cycling efficiency of ~99.9%. Compared to conventional inorganic salt hydrates like strontium chloride hexahydrate and calcium oxalate monohydrate, ISD showcases enhanced durability without deliquescence or pulverization, even under high-humidity conditions. In-situ analyses confirm the transition from ISD to ibuprofen sodium anhydrous (ISA) proceeds with structural reorganization, thereby combining the dehydration mechanism with phase transitions, resulting in higher energy storage capacity. Microstructural analyses reveal that repeated water intercalation and structural transitions aid in creating significant porosity that enhances water transport kinetics, further improving the hydration/dehydration performance. By combining the phase change and chemical dehydration mechanisms, ISD paves the way for designing a new class of organic salt hydrates, offering tunable properties to meet diverse thermal energy storage demands and supporting sustainable grid resilience.

Thangaraj, Kavin C.↗