NASA NTRS1974

EPR measurement of the effect of glass composition on the oxidation states of europium

An investigation was conducted concerning the dependence of the concentration ratio of Eu(2+) to Eu(3+) on composition for silicate liquids whose compositional end members are CaAl2Si2O8 and MgSiO3, MG2SiO4, CaMgSi2O6, CaMgSiO4, CaSiO3, or Ca2SiO4. The liquids were quenched to produce glasses. An electron paramagnetic resonance spectrometer was used to determine the concentration ratios of Eu(2+) to Eu(3+) in the glasses.

Morris, R. V.↗

NASA NTRS1993

Shock-induced devolatization of calcium sulfate and implications for K-T extinctions

Calcium sulfate devolatization during the impact at Chicxulub, Mexico and dispersal in the stratosphere of the resultant sulfuric acid aerosol have been suggested as a possible mechanism for the Cretaceous-Tertiary extinctions. In this paper, we investigated two shock-induced devolatization reactions of calcium sulfate up to 42 GPa in the laboratory: CaSO4 + SiO2 yields CaSiO3 + SO3(degassed) and CaSO4 yields CaO + SO2(degassed) + 1/2 O2(degassed). We found both to proceed to a much less extent than calculated by equilibrium thermodynamic calculations. Reaction products are found to be 10(exp -2) times those calculated for equilibrium. Consequently our estimate of the amount of sulfur oxides degassed into the atmosphere from shock devolatization of CaS04 in the Chicxulub lithographic section (6x10(exp 15)-2x10(exp 16)g in sulfur mass) is lower by a factor of 70 to 400 than previous estimates; the related environmental stress arising from the resultant global cooling of approximately 4 K and fallout of acid rain does not appear to suffice to explain the widespread K-T extinctions.

Chen, Guangqing↗

NASA NTRS2014

Properties of Desert Sand and CMAS Glass

As-received desert sand from a Middle East country has been characterized for its phase composition and thermal stability. X-ray diffraction analysis showed the presence of quartz (SiO2), calcite (CaCO3), gypsum (CaSO4.2H2O), and NaAlSi3O8 phases in as-received desert sand and showed weight loss of approx. 35 percent due to decomposition of CaCO3 and CaSO4.2H2O when heated to 1400 C. A batch of as-received desert sand was melted into calcium magnesium aluminosilicate (CMAS) glass at approx. 1500 C. From inductively coupled plasma-atomic emission spectrometry, chemical composition of the CMAS glass was analyzed to be 27.8CaO-4MgO-5Al2O3-61.6SiO2-0.6Fe2O3-1K2O (mole percent). Various physical, thermal and mechanical properties of the glass have been evaluated. Bulk density of CMAS glass was 2.69 g/cc, Young's modulus 92 GPa, Shear modulus 36 GPa, Poisson's ratio 0.28, dilatometric glass transition temperature (T (sub g)) 706 C, softening point (T (sub d)) 764 C, Vickers microhardness 6.3 +/- 0.4 GPa, indentation fracture toughness 0.75 +/- 0.15 MPa.m (sup 1/2), and coefficient of thermal expansion (CTE) 9.8 x 10 (exp -6)/degC in the temperature range 25 to 700 C. Temperature dependence of viscosity has also been estimated from various reference points of the CMAS glass using the Vogel-Fulcher-Tamman (VFT) equation. The glass remained amorphous after heat treating at 850 C for 10 hr but crystallized into CaSiO3 and Ca-Mg-Al silicate phases at 900 C or higher temperatures. Crystallization kinetics of the CMAS glass has also been investigated by differential thermal analysis (DTA). Activation energies for the crystallization of two different phases in the glass were calculated to be 403 and 483 kJ/mol, respectively.

Desert sand↗

NASA NTRS2015

Crystallization Kinetics of Calcium-magnesium Aluminosilicate (CMAS) Glass

The crystallization kinetics of a calcium-magnesium aluminosilicate (CMAS) glass with composition relevant for aerospace applications, like air-breathing engines, were evaluated using differential thermal analysis (DTA) in powder and bulk forms. Activation energy and frequency factor values for crystallization of the glass were evaluated. X-ray diffraction (XRD) was used to investigate the onset of crystallization and the phases that developed after heat treating bulk glass at temperatures ranging from 690 to 960 deg for various times. Samples annealed at temperatures below 900 deg remained amorphous, while specimens heat treated at and above 900 deg exhibited crystallinity originating at the surface. The crystalline phases were identified as wollastonite (CaSiO3) and aluminum diopside (Ca(Mg,Al) (Si,Al)2O6). Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were employed to examine the microstructure and chemical compositions of crystalline phases formed after heat treatment.

X-ray diffraction (XRD)↗

NASA NTRS2021

Melting and Crystallization Behavior of CaO-MgO-Al2O3-SiO2 Silicates Relevant to Turbine Engine Applications

The melting and crystallization behavior of four quaternary CaO-MgO-Al2O3-SiO2(CMAS) silicates were investigated. The CaO:SiO2 ratios of these systems were based on various terrestrial sources of ingested particles relevant to gas turbine engine operating environments. Melting behavior was characterized using differential scanning calorimetry, and high temperature intrinsic crystallization products were determined by furnace heat treatments of the glasses at 1200°C, 1300°C, and 1400°C. The silicates exhibited a wide range of melting temperatures from ~1240°C up to ~1500°C, with most of the compositions exhibiting incongruent melting behavior. High temperature crystallization products included CaSiO3,CaAl2Si2O8, Ca2MgSi2O7, and Ca(Mg,Al)Si2O6, although SiO2 was the only crystalline phase observed at 1400°C.

Jamesa L. Stokes↗

NASA NTRS2026

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures for consideration as a thermal and environmental barrier coating (T/EBC) material. CYbS apatite powder was synthesized from the constituent oxides via a solid-state reaction method. Hot-pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high-angle annular dark-field imaging, selected area electron diffraction, and energy dispersive x-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1 to 50 h at 1200 °C as well as in those heat treated at 1300 °C for 1 h. Residual CMAS was depleted of Ca when cyclosilicate was present. Dendritic wollastonite (CaSiO3) was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

Narottam P Bansal↗