Optical and photoelectric properties of surface barrier diodes based on n- Hg3In2Te6 crystals
The high radiation resistance of Hg3In2Te6 (MIT) single crystals to large doses of ionizing radiation makes devices quite attractive. Such a feature of the crystal structure has not only important advantages, but also causes serious technological difficulties in doping and controlling the specific resistance within the required limits and type of conductivity of single crystals. These technological difficulties create serious problems when creating structures with a potential barrier, especially with a p-n junction. At the moment, there are no publications on the creation of a p-n junction based on MIT. The only alternative is to create a potential barrier such as a Schottky diode or a metal-dielectric-semiconductor structure. This limits the use of MIT to produce, for example, rectifier diodes that can operate at relatively high reverse bias voltages. The typical resistivity of single crystals of MIT of n-type conductivity, which are used for the manufacture of diodes and photodiodes, is approximately equal to ρ≈103-104 Ω×cm. Such a specific resistance leads to a relatively large resistance of the neutral part of the single crystal, which in turn limits the direct currents of the rectifier diodes and significantly limits an important parameter of photodiodes - the dynamic range of the watt-ampere characteristic. This problem arises from the relatively high series resistance of the substrate. For rectifier diodes, this relatively large series resistance leads to a significant forward bias voltage drop, which reduces both the rectification factor and the amount of rectified current. We have already created diodes and photodiodes on Cr/MIT/Cr single crystals with a specific resistance of ρ≈103-104 Ω×cm. The diodes had relatively small dark currents but had the disadvantage of a relatively large specific resistance of the substrate, which we have already discussed above [1,2,3].