Measure the effect of molten halide salt exposure on creep rupture lifetime

Recent resurgence in the research and commercial interests in molten salt reactors (MSRs) as a viable advanced reactor concept to achieve the short- and long-term climate goals has resulted in ongoing efforts to demonstrate their commercial potential. These are relying on a combination of the extensive legacy knowledge from the molten salt reactor experiment (MSRE) and relatively recent data on materials compatibility of structural materials of interest such as 316H in molten salts environments. However, there is a critical lack of data on the mechanical behavior of alloys of interest for MSRS such as 316H, 617 and 709 in molten fluoride (FLiNaK or FLiBe) or chloride (NaCl-MgCl 2 ) salts. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy (Ni-15Cr-7Fe wt.%) in the molten fluoride NaF-ZrF4-UF4 (50-46-4 mol.%) salt. With ongoing efforts to commercialize different molten salt reactor concepts, the industry can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. Creep tests for 316H were conducted with fluoride (FLiNaK) and chloride (NaCl-MgCl 2 ) salts tat 650°C/150 MPa while alloys 709 and 617 were tested with FLiNaK at 700C/158 MPa and 750C.146 MPa respectively. Baseline tests were conducted in air to assess the impact of the molten salts on the creep behavior.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2025

Measure Effects of Molten Halide Salt on Creep Rupture Lifetime for 316H, 709 and 617

Ongoing commercialization of different molten salt reactor concepts can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy in molten fluoride salt. This task evaluated the creep behavior of candidate structural materials 316H, 709 and 617 for advanced nuclear reactors under molten halide salt environments at 650, 700 and 750°C respectively. Creep tests were conducted in air, Ar, fluoride (FLiNaK) and chloride (NaCl-MgCl 2 ) salts. The molten salt environment caused a 50% reduction in creep rupture lifetime for 316H in FLiNaK and an 80% reduction in creep rupture lifetime in NaCl-MgCl 2 compared to air exposures. The molten fluoride salt environment resulted in almost a 90% and 50% reduction in creep rupture time for 709 and 617 irrespective of the cover gas environment (air and Ar). Significant differences in the compositional changes between the salt- and air-facing surfaces were observed in the alloy subsurface which might have potentially lead to formation of phases detrimental to the creep behavior.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

Measure the effect of molten halide salt exposure on creep rupture lifetime

Recent resurgence in the research and commercial interests in molten salt reactors (MSRs) as a viable advanced reactor concept to achieve the short- and long-term climate goals has resulted in ongoing efforts to demonstrate their commercial potential. These are relying on a combination of the extensive legacy knowledge from the molten salt reactor experiment (MSRE) and relatively recent data on materials compatibility of structural materials of interest such as 316H in molten salts environments. However, there is a critical lack of data on the mechanical behavior of alloys of interest for MSRS such as 316H, 617 and 709 in molten fluoride (FLiNaK or FLiBe) or chloride (NaCl-MgCl 2 ) salts. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy (Ni-15Cr-7Fe wt.%) in the molten fluoride NaF-ZrF4-UF4 (50-46-4 mol.%) salt. With ongoing efforts to commercialize different molten salt reactor concepts, the industry can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. Creep tests for 316H were conducted with fluoride (FLiNaK) and chloride (NaCl-MgCl 2 ) salts tat 650°C/150 MPa while alloys 709 and 617 were tested with FLiNaK at 700C/158 MPa and 750C.146 MPa respectively. Baseline tests were conducted in air to assess the impact of the molten salts on the creep behavior.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2022

Composites of (C4F)n and (CF)n Synthesized by Uncatalyzed Fluorination of Graphite

A new solid-state 19F magic-angle spinning NMR signal at an isotropic 19F chemical shift of −53 ppm is measured from graphite fluoride synthesized by reaction of graphite with F2 at temperatures above 750 K with no catalyst. Two-dimensional NMR suggests the −53 ppm 19F NMR signal originates from covalent fluoromethanetriyl groups belonging to ordered (CyF)n bulk domains composited with the major (CF)n domains. Quantitative 19F and 13C NMR find y=4.32±0.64. DFT calculations of NMR chemical shifts for unsaturated fluorographene models show that a (C4F)n phase with fluorine bound covalently to a single side of the carbon layer best explains the observed NMR chemical shifts. We assign the new phase to this (C4F)n structure, which constitutes up to 15% of the carbon in our graphite fluoride composites. The (C4F)n content of the composite affects bulk electrochemical properties in a manner similar to graphite fluorides produced by conventional, catalyzed fluorination processes.

Walder, Brennan J. (ORCID:0000000274539143)↗
DOE OSTI2023

Viability of Cathodic Protection for Preventing Corrosion of Stainless Steel 316H in Molten LiF-NaF-KF

Molten fluoride salts are candidate heat transfer fluids in a number of applications such as generation IV molten salt nuclear reactors and concentrated solar power plants. However, a chief concern in the design of these systems is the corrosion of structural materials that come in contact with these molten salts. Redox control methods such as the purification of salt, the addition of active elements, and applied electrochemical potential can be efficient methods for preventing the corrosion of structural materials in molten fluoride salts. Applied electrochemical potential as a redox control method for application in molten fluoride salts has rarely been explored. This study seeks to understand the viability of impressed current cathodic protection (CP) at various currents as a redox control method to prevent corrosion of stainless steel 316H in molten LiF-NaF-KF (FLiNaK) salt. Results show that application of CP can be an effective method to prevent corrosion of SS316H in molten FLiNaK salt, but the applied current will have to be optimized to prevent undesirable side effects such as reduction of salt constituents, salt deposition on electrodes, etc.

Materials Science↗
NASA NTRS1967

Pure xenon hexafluoride prepared for thermal properties studies

Preparation of a xenon hexafluoride and sodium fluoride salt yields a sample of the highest possible purity for use in thermal measurements. The desired hexafluoride can easily be freed from the common contaminants, xenon tetra-fluoride, xenon difluoride, and xenon oxide tetrafluoride, because none of these compounds reacts with sodium fluoride.

Malm, J. G.↗
NASA NTRS1971

An investigation of oxidation-resistant solid lubricant materials.

Recent research at NASA-Lewis on solid lubricants for use at high temperatures in air and other gaseous environments is presented. The characteristics of oxide and fluoride lubricants at temperatures to 1700 F are described. Data is presented for fluoride coatings with silicate and other additives incorporated to give improved wear life and better oxidation protection to the substrate metal. Experience is described for fluoride-metal self-lubricating composites with improved metal oxidation resistance to 1700 F. The concept of cast, self-lubricating ceramics is also explored.

Sliney, H. E.↗
NASA NTRS1972

Weldability, strength, and high temperature stability of chemically vapor deposited tungsten

Three types of CVD tungsten (fluoride-produced, chloride-produced and the combination of the two which is termed duplex) were evaluated to determine their weldability, high temperature strength and structural stability during 5000 hour exposure to temperatures of 1540 C and 1700 C. Each type of CVD tungsten could be successfully electron beam welded but the results for the chloride product were not as satisfactory as those of the other two materials. The high temperature strength behavior of the three materials did not differ greatly. However a large difference was noted for the grain growth behavior of the two basic CVD tungsten materials. Fluoride tungsten was found to be relatively stable while for the most part the grain size of chloride tungsten increased appreciably. The examination of freshly fractured surfaces with a scanning electron microscope revealed numerous bubbles in the fluoride material following its exposure to 1700 C for 5000 hours. Less severe thermal treatments produced relatively few bubbles in this material. Only at certain locations within the chloride material associated with the interruption of tungsten were bubbles noted.

Bryant, W. A.↗
NASA NTRS1973

Fluorine lubricated bearing technology

An experimental program was conducted to evaluate and select materials for ball bearings intended for use in liquid fluorine and/or FLOX. The ability of three different ball-separator materials, each containing nickel, to form and transfer a nickel fluoride film to provide effective lubrication at the required areas of a ball bearing operating in liquid fluorine was evaluated. In addition, solid lubrication of a ball bearing operating in liquid fluorine by either a fused fluoride coating applied to all surfaces of the ball separator or by a fluoride impregnation of porous sintered material ball separators was evaluated. Less bearing wear occurred when tests were conducted in the less reactive FLOX. Bearings fabricated from any of the materials tested would have relatively short wear lives and would require frequent replacement in a reusable engine.

Mallaire, F. R.↗
NASA NTRS1973

Properties of multilayer filters

New methods were investigated of using optical interference coatings to produce bandpass filters for the spectral region 110 nm to 200 nm. The types of filter are: triple cavity metal dielectric filters; all dielectric reflection filters; and all dielectric Fabry Perot type filters. The latter two types use thorium fluoride and either cryolite films or magnesium fluoride films in the stacks. The optical properties of the thorium fluoride were also measured.

Baumeister, P. W.↗
NASA NTRS1974

Some metal-graphite and metal-ceramic composites for use as high energy brake lining materials

Materials were studied as candidates for development as potential new aircraft brake lining materials. These families were (1) copper-graphite composites; (2) nickel-graphite composites; (3) copper - rare-earth-oxide (gadolinium oxide (Gd2O3) or lanthanum oxide (La2O3)) composites and copper - rare-earth-oxide (La2O3) - rare-earth-fluoride (lanthanum fluoride (LaF3)) composites; (4) nickel - rare-earth-oxide composites and nickel - rare-earth-oxide - rare-earth-fluoride composites. For comparison purposes, a currently used metal-ceramic composite was also studied. Results showed that the nickel-Gd2O3 and nickel-La2O3-LaF3 composites were comparable or superior in friction and wear performance to the currently used composite and therefore deserve to be considered for further development.

Bill, R. C.↗
NASA NTRS1974

High-temperature strength stability of three forms of chemically vapor deposited tungsten

Three types of CVD tungsten (fluoride-produced, chloride-produced, and a layered composite of the two-termed duplex) were evaluated to determine their high-temperature strength and microstructural stability following 5000-hr exposure to temperatures of 1540 and 1700 C. At the highest temperatures investigated (1540 and 1700 C), the tensile strengths of the two basic materials were essentially equal. At lower temperatures, chloride tungsten possessed lower yield strength but higher ultimate strength than fluoride tungsten while the behavior of the duplex material was generally intermediate. Apparent anomalies in high-temperature elongation behavior are explained on the basis of grain boundary cavity formation and recrystallization. The grain size of fluoride tungsten changed only slightly following 5000-h treatment at 1700 C. In contrast, chloride tungsten possessed both poor resistance to grain growth and an accompanying relatively high ductile-brittle transition temperature.

Bryant, W. A.↗
NASA NTRS1982

Development of an all-metal thick film cost effective metallization system for solar cells

Electrodes made with pastes produced under the previous contract were analyzed and compared with raw materials. A needle-like structure observed on the electroded solar cell was identified as eutectic copper-silicon, a phase considered to benefit the electrical and metallurgical properties of the contact. Electrodes made from copper fluorocarbon and copper silver fluoride also contained this phase but had poor adhesion. A liquid medium, intended to provide transport during carbon fluoride decomposition was incorporated into the paste resulting in better adhesion. The product survived preliminary environmental tests. A 2 cm by 2 cm solar cell made with fluorocarbon activated copper electrodes and gave 7% AMI efficiency (without AR coating). Both silver fluoride and fluorocarbon screened paste electrodes can be produced for approximately $0.04 per watt.

Ross, B.↗
NASA NTRS1983

Development of aircraft lavatory compartments with improved fire resistance characteristics. Phase 4: Sandwich panel decorative ink development

Five chemically different resin systems with improved fire resistance properties were studied for a possible screenprinting ink application. Fire resistance is hereby defined as the cured ink possessing improvements in flammability, smoke emission, and thermal stability. The developed ink is for application to polyvinyl fluoride film. Only clear inks without pigments were considered. Five formulations were evaluated compared with KC4900 clear acrylic ink, which was used as a baseline. The tests used in the screening evaluation included viscosity, smoke and toxic gas emission, limiting oxygen index (LOI), and polyvinyl fluoride film (PVF) printability. A chlorofluorocarbon resin (FPC461) was selected for optimization studies. The parameters for optimization included screenprinting process performance, quality of coating, and flammability of screenprinted 0.051-mm (0.002-in.) white Tedlar. The quality of the screenprinted coating on Tedlar is dependent on viscosity, curing time, adhesion to polyvinyl fluoride film, drying time (both inscreen and as an applied film), and silk screen mesh material and porosity.

Jayarajan, A.↗
NASA NTRS1983

Fire resistant films for aircraft applications

Alternative sandwich panel decorative films were investigated as replacements for the polyvinyl fluoride currently used in aircraft interiors. Candidate films were studied for flammability, smoke emission, toxic gas emission, flame spread, and suitability as a printing surface for the decorative acrylic ink system. Several of the candidate films tested were flame modified polyvinyl fluoride, polyvinylidene fluoride, polyimide, polyamide, polysulfone, polyphenylsulfone, polyethersulfone, polybenzimidazole, polycarbonate, polyparabanic acid, polyphosphazene, polyetheretherketon, and polyester. The films were evaluated as pure films only, films silk-screened with an acrylic ink, and films adhered to a phenolic fiberglass substrate. Films which exhibited the highest fire resistant properties included PEEK polyetheretherketon, Aramid polyamide, and ISO-BPE polyester.

Kourtides, D. A.↗
NASA NTRS1983

Fire resistant films for aircraft applications

Alternative sandwich panel decorative films were investigated as replacements for the polyvinyl fluoride currently used in aircraft interiors. Candidate films were studied for flammability, smoke emission, toxic gas emission, flame spread, and suitability as a printing surface for the decorative acrylic ink system. Several of the candidate films tested were flame modified polyvinyl fluoride, polyvinylidene fluoride, polyimide, polyamide, polysulfone, polyphenylsulfone, polyethersulfone, polybenzimidazole, polycarbonate, polyparabanic acid, polyphosphazene, polyetheretherketon, and polyester. The films were evaluated as pure films only, films silk-screened with an acrylic ink, and films adhered to a phenolic fiberglass substrate. Films which exhibited the highest fire resistant properties included PEEK polyetheretherketon, Aramid polyamide, and ISO-BPE polyester. Previously announced in STAR as N83-22320

Kourtides, D. A.↗
NASA NTRS1987

Self-lubricating coatings for high-temperature applications

Some present-day aeropropulsion systems impose severe demands on the thermal and oxidative stability of lubricant, bearing, and seal materials. These demands will be much more severe for operational systems around the turn of the century. Solid lubricants with maximum temperature capabilities of about 1100 C are known. Unfortunately, none of the solid lubricants with the highest temperature capabilities are effective below approximately 400 C. However, research shows that silver and stable fluorides, such as calcium and barium fluoride act synergistically to provide lubrication from below room temperature to approximately 900 C. Plasma-sprayed, self-lubricating composite coatings that were developed at Lewis are described. Background information is given on coatings, designed as PS100 and PS101, that contain the solid lubricants in a Nichrome matrix. These coatings have low friction coefficients over a wide temperature range, but they have inadequate wear resistance for some long-duration applications. Wear resistance was dramatically improved in a recently developed coating PS200, by replacing the Nichrome matrix material with metal-bonded chromium carbide containing dispersed silver and calcium fluoride/barium fluoride eutectic (CaF2/BaF2). The lubricants control friction and the carbide matrix provides excellent wear resistance. Successful tests of these coatings are discussed.

Sliney, Harold E.↗