Measure Effects of Molten Halide Salt on Creep Rupture Lifetime for 316H, 709 and 617

Abstract

Ongoing commercialization of different molten salt reactor concepts can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy in molten fluoride salt. This task evaluated the creep behavior of candidate structural materials 316H, 709 and 617 for advanced nuclear reactors under molten halide salt environments at 650, 700 and 750°C respectively. Creep tests were conducted in air, Ar, fluoride (FLiNaK) and chloride (NaCl-MgCl 2 ) salts. The molten salt environment caused a 50% reduction in creep rupture lifetime for 316H in FLiNaK and an 80% reduction in creep rupture lifetime in NaCl-MgCl 2 compared to air exposures. The molten fluoride salt environment resulted in almost a 90% and 50% reduction in creep rupture time for 709 and 617 irrespective of the cover gas environment (air and Ar). Significant differences in the compositional changes between the salt- and air-facing surfaces were observed in the alloy subsurface which might have potentially lead to formation of phases detrimental to the creep behavior.