NASA NTRS1994

Thermal Testing of High Performance: Thermal Barrier Coatings for Turbine Blades

A 350 micron thick 7 wt.% Y 2 O 3 -ZrO 2 (7YSZ) ceramic Thermal Barrier Coating (TBC) was manufactured in an argon atmosphere and with a strictly controlled substrate temperature on flat IN 600 samples and on IN 100 aircraft turbine blades. This new atmosphere and temperature controlled spraying (ATCS) allows the reduction of the residual stresses and an improvement in the microstructure and in the mechanical properties of the coating. The good performance of these new TBC's was assessed in thermal fatigue and in thermal shock tests carried out in air at 1100°C and at 1280°C respectively. The oxidation rate of the metal-ceramic interface was measured at 1100°C. Failure of the TBC's was induced only by the deterioration (like oxidation, cracking, ...) of the uncoated parts of the samples, as testing temperature was too severe for the base metals. Spalling was thereafter driven by compressive stresses near the aluminum oxide layer at the metal-ceramic interface. The results of these tests underline the good quality of the ceramic coating manufactured by the new ATCS technology.

L Bertamini↗

NASA NTRS2026

Radiation-Conditioned Ti–hBN Coatings for Space Mechanisms: Bridging Tribology and Irradiation Effects from Laboratory to Low-Earth Orbit

The longevity of tribological components in extraterrestrial environments is challenged by abrasive regolith, extreme temperatures, and ionizing radiation. This study evaluates the performance of vacuum plasma sprayed (VPS) Ti-2vol.% hexagonal boron nitride (hBN) coatings applied to joint mechanisms such as rod and slot, ball and socket, and hinge assemblies, fabricated from Al6061 and Ti6Al4V for planetary structures. Coated and uncoated samples were tested under vacuum with lunar regolith simulant (JSC-1A), followed by environmental exposures including electron radiation and thermal cycling. Results show that coated samples consistently outperformed uncoated counterparts across all configurations. Wear depth in coated components was reduced by over 80%, as confirmed by 3D profilometry and surface imaging. SEM analysis revealed severe abrasion and localized plastic deformation in uncoated surfaces, while coated samples retained structural integrity due to synergy of hard protective phases formed during deposition and retained hBN providing solid lubrication in the sliding surface. Coated and exposed samples exhibited smoother actuation profiles and reduced friction, indicating a beneficial "conditioning" effect from environmental exposure. The coatings-maintained performance even on complex geometries with minimal delamination. These findings demonstrate the potential of VPS Ti-hBN coatings to extend the operational life of lunar mechanisms, bridging laboratory-scale tribology with flight-relevant mechanical applications.

tribology↗

NASA NTRS2025

Erosion Behavior of Ti-hBN Multifunctional Coatings in A Custom-Made Planetary Test Rig at Extreme Lunar Temperatures

Spacecraft landings and takeoffs on the lunar surface, along with extreme temperature variations between day and night (-196 to 150° C), cause high-velocity dust impacts and erosion, resulting in the premature failure of structures. Ti/2 vol% hBN coatings were deposited using atmospheric (APS) and vacuum plasma spray (VPS) using cryo-milled powder feedstock to protect the structural components. The erosion performance of coatings at extreme lunar temperature regimes (-150 to 150° C) was evaluated in a custom-made planetary erosion test rig (PETR) at low (50 mph) and high impact velocities (250 mph). The mass loss of VPS coatings was reduced by 50% compared to the APS coatings and 40% compared to the Ti6Al4V substrate. The cryogenic temperature induces brittleness in the material, rendering it susceptible to extreme conditions of material loss. The particle impact-deformation behavior was captured using a high-speed camera to study the erosion mechanism. This analysis revealed chipping in substrates and brittle APS coatings, while particles rebounding and embedding were observed in VPS coatings. Energy calculations, aided by particle trajectory tracking from the high-speed camera, have conclusively shown that VPS coatings absorb 5–10% more energy than APS coatings during erosion tests. A modified erosion index was developed incorporating the fracture toughness and temperatures. New erosion models for brittle and ductile target materials are proposed for developing erosion-resistant material systems.

Abhijith Kunneparambil Sukumaran↗