Radiation-Conditioned Ti–hBN Coatings for Space Mechanisms: Bridging Tribology and Irradiation Effects from Laboratory to Low-Earth Orbit

Abstract

The longevity of tribological components in extraterrestrial environments is challenged by abrasive regolith, extreme temperatures, and ionizing radiation. This study evaluates the performance of vacuum plasma sprayed (VPS) Ti-2vol.% hexagonal boron nitride (hBN) coatings applied to joint mechanisms such as rod and slot, ball and socket, and hinge assemblies, fabricated from Al6061 and Ti6Al4V for planetary structures. Coated and uncoated samples were tested under vacuum with lunar regolith simulant (JSC-1A), followed by environmental exposures including electron radiation and thermal cycling. Results show that coated samples consistently outperformed uncoated counterparts across all configurations. Wear depth in coated components was reduced by over 80%, as confirmed by 3D profilometry and surface imaging. SEM analysis revealed severe abrasion and localized plastic deformation in uncoated surfaces, while coated samples retained structural integrity due to synergy of hard protective phases formed during deposition and retained hBN providing solid lubrication in the sliding surface. Coated and exposed samples exhibited smoother actuation profiles and reduced friction, indicating a beneficial "conditioning" effect from environmental exposure. The coatings-maintained performance even on complex geometries with minimal delamination. These findings demonstrate the potential of VPS Ti-hBN coatings to extend the operational life of lunar mechanisms, bridging laboratory-scale tribology with flight-relevant mechanical applications.