Engineering Papers⌕ Search

SEARCH · Engineering Papers

Results for “solid oxide cells”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 37 records · Page 2
All sourcesNASA NTRSDOE OSTI
DOE OSTI2025

CO 2 Electrolysis Using Metal-Supported Solid Oxide Cells with Infiltrated Pr 0.5 Sr 0.4 Mn 0.2 Fe 0.8 O 3-$δ$ Catalyst

Electrochemical conversion of CO 2 to CO is demonstrated with symmetric-structured metal supported solid oxide cells (MS-SOC). Perovskite Pr 0.5 Sr 0.4 Mn 0.2 Fe 0.8 O 3-δ (PSMF) and Pr 6 O 11 catalysts were infiltrated into the MS-SOC cathode and anode, using 3 cycles with firing at 850 °C and 8 cycles with firing at 800 °C, respectively. Upon reduction during operation, the perovskite PSMF was transformed to Ruddlesden–Popper structure with a highly efficient electrocatalytic activity. The impact of operating temperature (600–800 °C) and overpotential (0–1.8 V) on the CO 2 conversion was investigated. The highest CO 2 conversion of 57.2% was achieved at 750 °C and 1.8 V. During extended operation for 150 h at 750 °C and 1.2 V, a cell demonstrated relatively stable performance, with initial current density of 535 mA cm -2 and CO 2 conversion of 23%. Degradation mechanisms were studied by posttest characterization.

25 ENERGY STORAGE↗
DOE OSTI2025

Microstructure-Based Degradation Modeling in Solid Oxide Cells

The presentation is intended for a graduate class in Georgia Southern University taught by Dr. Hayri Sezer on electrochemistry, SOFC and Li ion battery. It summaries NETL's recent works on microstructure-based modeling of degradation in solid oxide cells. It covers the degradation mechanism of Ni coarsening, Ni migration and the build-up of oxygen partial pressure inside the electrolyte. The phase-field models developed for Ni coarsening and migration are reviewed and the results are compared to experiments in literature to examine different diffusion mechanisms (Ni self-diffusion, Ni(OH)2 diffusion in pores and Ni(OH) surface diffusion) and driving forces (Ni(OH)x concentration and Ni-YSZ contact angle change). It also demonstrates the developed model for oxygen partial pressure and shows that the predicted oxygen partial pressure can explain the Ni oxidation in the hydrogen electrode and crack growth on the electrolyte-oxygen electrode interface under certain operating conditions.

nickel coarsening↗
DOE OSTI2024

An Analytical Tool to Evaluate Defect Thermodynamics of (La,Ba)Fe1-xMxO3-δ Perovskites for Solid-Oxide Cell Applications

A modeling tool of the defect thermodynamics of (La,Ba)Fe1-xMxO3-δ perovskites which includes energetic information about oxygen vacancy formation, hydration, hydride formation, and charge disproportionation reactions has been developed1. This tool incorporates defect energies and entropies expressed as sixth order polynomial functions to allow refinements of the defect reaction equilibrium constants in the thermodynamic analysis. Calculation of (La,Ba)Fe1-xMxO3-δ Brouwer diagrams as a function of pO2/pH2O and pH2/H2O in a range of temperatures of interest is facilitated by this modeling tool. The results obtained can provide direct guidance how the electronic and ionic defect concentrations of the triple conducting perovskite materials can be used to optimize performance of solid oxide cells for energy applications. The impact of magnetic and electronic structures of the perovskites on the defect reaction energies and entropies as obtained from density function theory modeling and the role played by hydride defect species will also be discussed.

Lee, Yueh-Lin↗
DOE OSTI2025

Evaluation of a 5kW Solid Oxide Electrolysis Cell Stack

Solid oxide electrolysis cells (SOECs) are a developing technology for hydrogen production. They are promising due to their utilization of thermal energy to reduce their electricity consumption. The Department of Energy (DOE) has set goals to reduce the price per kilogram of hydrogen, and Idaho National Laboratory (INL) is conducting research to develop and demonstrate advanced methods and technologies to achieve making hydrogen a more affordable, efficient, and sustainable energy source. In this project, INL is collaborating with a vendor to evaluate and validate the design of a 5kW SOEC stack. The test aims to demonstrate a safe startup, operation, and shutdown on INL’s 5kW test stand, providing third-party validation in a different environment. A successful 50-hour test with stable hydrogen production will pave the way for a subsequent 1000-hour test. This project emphasized learning about electrolysis and the various support systems, referred to as balance of plant (BOP) equipment. These systems required modification while swapping to the vendor 5kW SOEC stack, most prominently the furnace door design and the controls system. It also included gaining skills in creating computer-aided design (CAD) drawings for the new door while using available materials and ensuring it met high-temperature requirements. Upon completion of modifications to the test stand, the SOEC will be test-fitted with respective wiring and piping. Instrumentation and piping will be checked for leaks and quality. This must be completed before the vendor’s engineers arrive to observe the test plan, startup, and a collection of 50 hours of data. The vendor’s engineers will ensure their stack performed sufficiently in the 50-hour test to enable the progression to a 1000-hour test.

08 - HYDROGEN↗
DOE OSTI2025

Kinetics and Thermodynamics of Sr Permeation in CeO 2 -Based Barrier Layers for Solid-Oxide Electrolyzer Cells

Solid-oxide electrolyzer cells (SOECs) convert steam to hydrogen efficiently at high temperatures. However, during operation, the diffusion of cations or impurities through the cells due to electrode degradation can cause unwanted secondary phases to form, which may degrade device performance. Here, in this study, we use atomistic and mesoscale simulations coupled with experimental analysis to study the diffusion of Sr through the Gd-doped CeO 2 (GDC) barrier layer used to protect the yttria-stabilized zirconia (YSZ) electrolyte in SOECs. From our atomistic calculations, we find Sr diffusion to be negligibly slow in bulk GDC; however, surface diffusion is much more favorable. Subsequent mesoscale simulations show that Sr diffusion is activated when the porosity of GDC exceeds ∼10% and significantly exceeds diffusion in bulk and grain boundary regions. We also find that SrO-based species can accumulate at GDC surfaces; however, SrO aggregation and coarsening will be limited by the large lattice mismatch between GDC and SrO. Energy-dispersive X-ray spectroscopy (EDS) and electron diffraction confirm that Sr can accumulate within GDC pores and form disperse Sr-containing secondary phases. Altogether, Sr diffusion in dense GDC is unlikely to give rise to thick SrO layers, which would severely limit device performance. The formation of Sr-containing secondary phases can largely be avoided by restricting the porosity of the GDC layer as much as possible.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Robust dynamic operation of high temperature electrolysis solid oxide cells

Here, this study evaluates the durability of Ni/YSZ-supported SOECs under dynamic operating conditions relevant to real-world applications. Systematic tests were conducted to assess cell performance under steam cycling (3 to 75% humidified H 2 ), mode cycling between SOFC and SOEC operation, thermal cycling (150 to 750 °C at OCV, and 600 to 800 °C at 1.3V), and redox cycling (between 50% humidified H 2 and 50% humidified N 2 ). Steam cycling, mode cycling, and thermal cycling at OCV do not significantly accelerate performance degradation. Thermal cycling at 1.3V caused minimal damage within 600 to 800 °C. Full redox cycling (multi-hour oxidation holds) induced cell structural failure, while partial redox cycling (0.5 h holds) was tolerated. Extensive characterization revealed some material evolution, namely Sr and Co secondary phase formation, within the oxygen electrode due to La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ instability, especially for steam cycling and mode cycling. Minimal changes were identified within the Ni-YSZ fuel electrodes. These findings provide critical insights into SOEC reliability under dynamic conditions, supporting their application in dynamic or intermittent energy systems.

08 HYDROGEN↗
DOE OSTI2025

Infiltrated electrodes for metal supported solid oxide electrolysis cells

Metal-supported solid oxide cells (MSOCs) are an alternative to conventional solid oxide cells (SOCs) based on ceramic cermets, offering lower material costs and higher operational flexibility. In this study symmetric MSOCs with infiltrated electrodes are explored for steam electrolysis operation to understand the underlying operation and degradation principles and suggest a direction for future MSOCs development. Two different fuel electrode backbones are used: an electronically-conductive lanthanum strontium co-doped iron nickel titanate (LSFNT) infiltrated with cerium-gadolinium oxide (CGO), or an ionic conductive zirconia based backbone (10ScYSZ) infiltrated with Ni:CGO. At the oxygen side, the backbone is 10ScYSZ, which is infiltrated with lanthanum-strontium co-doped cobalt oxide (LSC), or praseodymium oxide as cobalt-free alternative for comparison. This study suggests that the backbone electronic conductivity is key for good electrochemical performance as well as for boosting cell durability. Highly electronically conductive nanoparticles, especially nickel, were observed to irreversibly agglomerate driven by thermal conditions, whereas CGO proved to be a very stable electrocatalyst. At the fuel side, CGO (LSFNT) electrode showed lower ASR and degradation rate than Ni:CGO(ScYSZ) configuration with measured values of 0.50 Ω cm2 and 11 %/1000 h (at 0.60 A/cm2), and 0.70 Ω cm2 and 26 %/1000 h (at 0.50 A/cm2) at 1.30 V, respectively (700 °C, 50 % steam in hydrogen at the fuel side and air at the oxygen electrode side, LSC(ScYSZ) oxygen electrode).

25 ENERGY STORAGE↗
NASA NTRS2004

Increasing the Thermal Stability of Aluminum Titanate for Solid Oxide Fuel Cell Anodes

Solid-oxide fuel cells (SOFCs) show great potential as a power source for future space exploration missions. Because SOFCs operate at temperatures significantly higher than other types of fuel cells, they can reach overall efficiencies of up to 60% and are able to utilize fossil fuels. The SOFC team at GRC is leading NASA's effort to develop a solid oxide fuel cell with a power density high enough to be used for aeronautics and space applications, which is approximately ten times higher than ground transport targets. layers must be able to operate as a single unit at temperatures upwards of 900'C for at least 40,000 hours with less than ten percent degradation. One key challenge to meeting this goal arises from the thermal expansion mismatch between different layers. The amount a material expands upon heating is expressed by its coefficient of thermal expansion (CTE). If the CTEs of adjacent layers are substantially different, thermal stresses will arise during the cell's fabrication and operation. These stresses, accompanied by thermal cycling, can fracture and destroy the cell. While this is not an issue at the electrolyte-cathode interface, it is a major concern at the electrolyte-anode interface, especially in high power anode-supported systems. electrolyte are nearly identical. Conventionally, this has been accomplished by varying the composition of the anode to match the CTE of the yittria-stabilized zirconia (YSZ) electrolyte (approx.10.8x10(exp -6/degC). A Ni/YSZ composite is typically used as a base material for the anode due to its excellent electrochemical properties, but its CTE is about 13.4x10(exp -6/degC). One potential way to lower the CTE of this anode is to add a small percentage of polycrystalline Al2TiO5, with a CTE of 0.68x10(exp -6/degC, to the Ni/YSZ base. However, Al2TiO5 is thermally unstable and loses its effectiveness as it decomposes to Al2O3 and TiO2 between 750 C and 1280 C. be used as additives to increase the thermal stability of Al2TiO5 in SOFC operating conditions without adversely affecting the electrochemical properties of the SOFC anode. Three candidate materials were chosen through an extensive literature review: MgO, Fe2O3, and ZrTiO4. Although all three have been shown to prevent Al2TiO5 decomposition under various conditions, their effectiveness in the temperature range and atmosphere of the SOFC has not yet been evaluated. Several batches of Al2TiO5 with varying amounts of additives were prepared, exposed to reducing and oxidizing atmospheres at elevated temperatures, and the resulting decomposition of Al2TiO5 was measured. The most promising additives were further evaluated with the goal of ultimately preparing low CTE anodes that are chemically compatible to current systems. Adding minor constituents to stabilize Al2TiO5 could ultimately preserve its low CTE for the life of the fuel cell and improve the cell's long-term performance without a drop in anode conductivity. Further, these low CTE filler additions could allow the use of new sulfur tolerant anode materials, improving the viability of SOFCs for future aeronautics and space applications. Every SOFC consists of a cathode and an anode separated by an electrolyte, These three One way to avoid this problem is to design the cell such that the CTEs of the anode and The objective of this summer research project was to evaluate several materials that could

Bender, Jeffrey B.↗
DOE OSTI2025

Flexible Nuclear-Based Integrated Energy System

Presentation on a conceptual study of combining a small modular nuclear reactor (SMR) with a solid oxide fuel cell, solid oxide electrolysis cell, and a gas turbine as an integrated energy system with high operational flexibility and rapid load following. Virtually presented at the MILLENNIUM CLEAN and SUSTAINABLE POWER workshop 2025, University of Genoa, Italy.

flexibility↗
DOE OSTI2024

Market optimization and technoeconomic analysis of hydrogen-electricity coproduction systems

Decarbonization efforts across North America, Europe, and beyond rely on variable renewable energy sources such as wind and solar, as well as alternative fuels, such as hydrogen, to support the sustainable energy transition. These advancements have prompted a need for more flexibility in the electric grid to complement non-dispatchable energy sources and increased demand from electrification. Integrated energy systems are well suited to provide this flexibility, but conventional technoeconomic modeling paradigms neglect the time-varying dynamic nature of the grid and thus undervalue resource flexibility. In this work, we develop a computational optimization framework for dynamic market-based technoeconomic comparison of integrated energy systems that coproduce low-carbon electricity and hydrogen (e.g., solid oxide fuel cells, solid oxide electrolysis) against technologies that only produce electricity (e.g., natural gas combined cycle with carbon capture) or only produce hydrogen. Our framework starts with rigorous physics-based process models, built in the open-source Institute for the Design of Advanced Energy Systems (IDAES) modeling and optimization platform, for six energy process concepts. Using these rigorous models and a workflow to optimally design each technology, the framework is shown to be capable of evaluating new and emerging technologies in varying energy markets under a plethora of future scenarios (i.e., renewables penetration, carbon tax, etc.). Ultimately, our framework finds that solid oxide fuel cell-based coproduction systems achieve positive profits for 85% of the analyzed market scenarios. From these market optimization results, we use multivariate linear regression (R 2 values up to 0.99) to determine which electricity price statistics are most significant to predict the optimized annual profit of each system. The proposed framework provides a powerful tool for directly comparing flexible, multi-product energy process concepts to help discern optimal technology and integration options.

08 HYDROGEN↗
NASA NTRS2002

Strength and Fracture Toughness of Solid Oxide Fuel Cell Electrolyte Material Improved

Solid oxide fuel cells (SOFC) are being developed for various applications in the automobile, power-generation, and aeronautics industries. Recently, the NASA Glenn Research Center has been exploring the possibility of using SOFC's for aeropropulsion under its Zero Carbon Dioxide Emission Technology (ZCET) Program. 10-mol% yttriastabilized zirconia (10YSZ) is a very good anionic conductor at high temperatures and is, therefore, used as an oxygen solid electrolyte in SOFC. However, it has a high thermal expansion coefficient, low thermal shock resistance, low fracture toughness, and poor mechanical strength. For aeronautic applications, the thin ceramic electrolyte membrane of the SOFC needs to be strong and tough. Therefore, we have been investigating the possibility of enhancing the strength and fracture toughness of the 10YSZ electrolyte without degrading its electrical conductivity to an appreciable extent. We recently demonstrated that the addition of alumina to zirconia electrolyte increases its strength as well as its fracture toughness. Zirconia-alumina composites containing 0 to 30 mol% of alumina were fabricated by hot pressing. The hot pressing procedure was developed and various hot pressing parameters were optimized, resulting in dense, crackfree panels of composite materials. Cubic zirconia and a-alumina were the only phases detected, indicating that there was no chemical reaction between the constituents during hot pressing at elevated temperatures. Flexure strength sf and fracture toughness K(sub IC) of the various zirconia-alumina composites were measured at room temperature as well as at 1000 C in air. Both properties showed systematic improvement with increased alumina addition at room temperature and at 1000 C. Use of these modified electrolytes with improved strength and fracture toughness should prolong the life and enhance the performance of SOFC in aeronautics and other applications.

Bansal, Narottam P.↗
DOE OSTI2025

Effect of high scandium doping in barium zirconate on nickel diffusion and performance of proton-conducting solid oxide electrolyzer cells

Proton-conducting solid oxide electrolyzer cells (p-SOECs) are emerging but promising technologies for hydrogen production. However, due to the lack of a robust electrolyte, p-SOECs struggle simultaneously to display high performance, Faradaic efficiency, and durability. Motivated by its high proton concentrations and stability as a barium zirconate, we have investigated BaZr 0.6 Sc 0.4 O 3-δ (BZSc40) as a potential next-generation p-SOEC electrolyte. Here, we found elevated levels of NiO diffusion through BZSc40 electrolytes during high-temperature sintering, attributed to the large oxygen vacancy concentrations present in BZSc40, as revealed by first-principle computational results. Controlling NiO diffusion is critical, as it can facilitate densification and grain size growth, but it may also detrimentally impact performance by causing electronic leakage. By optimizing sintering temperature when fabricating BZSc40 cells, we successfully controlled NiO diffusion, achieving sufficient electrolyte densification along with high performance and Faradaic efficiency. BZSc40 cells reached −0.99 A/cm 2 at 1.3 V and 600 °C and exhibited enhanced durability with a 3.37 mV/kh degradation rate at −0.8 A/cm 2 over a 200-h testing period. BZSc40 electrolytes demonstrated superior performance over BaZr 0.8 Y 0.2 O 3-δ (BZY20). In addition to elevated current densities and grain sizes, BZSc40 cells achieved Faradaic efficiencies of 76 % compared to 54 % for BZY20 at −0.2 A/cm 2 and 600 °C. This work lays the foundation for BZSc40 as a potential electrolyte due to its advantages over BZY20 while demonstrating the significance of controlling NiO diffusion when fabricating p-SOECs.

Electrolyzer↗
NASA NTRS1989

Monolithic Solid Oxide Fuel Cell development

The Monolithic Solid Oxide Fuel Cell (MSOFC) is an oxide-ceramic structure in which appropriate electronic and ionic conductors are fabricated in a honeycomb shape similar to a block of corrugated paperboard. These electronic and ionic conductors are arranged to provide short conduction paths to minimize resistive losses. The power density achievable with the MSOFC is expected to be about 8 kW/kg or 4 kW/L, at fuel efficienceis over 50 percent, because of small cell size and low resistive losses in the materials. The MSOFC operates in the range of 700 to 1000 C, at which temperatures rapid reform of hydrocarbon fuels is expected within the nickel-YSZ fuel channels. Tape casting and hot roll calendering are used to fabricate the MSOFC structure. The performance of the MSOFC has improved significantly during the course of development. The limitation of this system, based on materials resistance alone without interfacial resistances, is 0.093 ohm-sq cm area-specific resistance (ASR). The current typical performance of MSOFC single cells is characterized by ASRs of about 0.4 to 0.5 ohm-sq cm. With further development the ASR is expected to be reduced below 0.2 ohm-sq cm, which will result in power levels greater than 1.4 W/sq cm. The feasibility of the MSOFC concept was proven, and the performance was dramatically improved. The differences in thermal expansion coefficients and firing shrinkages among the fuel cell materials were minimized. As a result of good matching of these properties, the MSOFC structure was successfully fabricated with few defects, and the system shows excellent promise for development into a practical power source.

Myles, K. M.↗