Engineering Papers⌕ Search

SEARCH · Engineering Papers

Results for “Grain microstructure evolution”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 253 records · Page 14
All sourcesNASA NTRSDOE OSTI
NASA NTRSDate not supplied

Towards Integrated Computational Materials Engineering for Quantifying Performance Impacts of Microstructure and Defect Interactions in Powder Bed Fusion Parts

Powder bed fusion (PBF) additive manufacturing (AM) enables the creation of parts with complexity and functionality levels that were previously impossible with traditional manufacturing methods. By modifying the laser power, hatch spacing, or the numerous other processing parameters, the PBF process supports the production of a wide set of materials and geometries. However, that same process parameter design flexibility causes the process-design space of PBF to be massive and expensive to explore experimentally. Another challenge is quality variation across a build. As a part is being built, geometric variance between locations, such as at a thin-wall section vs. the bulk material, may cause the specified processing parameters to no longer be acceptable for producing defect-free printing. Furthermore, if the processing parameters deviate during the print process, it is difficult to assess if the part will still perform satisfactorily. Integrated Computational Materials Engineering (ICME) provides a way to understand and address these various challenges. This talk will present advancements in process-structure simulations of PBF at NASA Langley Research Center. The ability to simulate grain-scale PBF microstructures using the Physically Based Monte Carlo method will be demonstrated and compared to experimental measurements. Techniques for simulating three-dimensional lack-of-fusion and keyhole porosity defects based on the specific processing conditions and approaches for integrating the two porosity prediction techniques alongside the computational microstructure evolution models will be shown. Finally, the integration of simulated PBF microstructures, embedded process defects, and crystal plasticity finite element models to elucidate the interaction of porosity and microstructure on micromechanical fields will be demonstrated. These integrated techniques demonstrate an example of using ICME to relate processing to performance for PBF AM materials. With continued maturity, it is hoped that such ICME approaches will lead to next-generation computational-materials supported qualification and certification of AM parts.

Additive manufacturing↗
DOE OSTI2023

A Limit to Accelerated Free-Sintering: Nano-Phase Separation Interferes With Organic Debinding

Nano-phase separating Ni–12 at. pct Ag powders are processed via high-energy ball milling and brought into a supersaturated state with a reduction of the grain size to the nanocrystalline scale, a combination that is designed to encourage rapid densification by phase separation upon heating. This unstable powder is then characterized by dilatometry, in-situ x-ray diffraction, thermogravimetry and microstructure analysis for sintering cycles up to 940 °C. However, these powder compacts exhibit excessive pore evolution and significant macroscopic swelling caused by removal of the organic process additives. This competition of organic removal with densification is known in nanocrystalline metals, but the present study adds an additional dimension of phase separation, which shifts the dominant swelling mechanism as the formation of the second phase traps the volatilizing organics and hinders the debinding process. The creep swelling and overall loss in relative density is then dominated by the creep deformation of the second Ag phase. The interference between organic removal and low-temperature onset of consolidation represents a new challenge to efforts aimed at rapid free sintering and should guide the design of rapidly sintering alloys; specifically, the present work emphasizes the need to select alloys that have their sintering-accelerating phase separation temperature above the range where gases are evolved.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Geometry and size dependent microstructure and crack formation in Rene 41 superalloy fabricated by laser powder bed fusion

This study provides a systematic investigation into the size and geometry-dependent microstructural evolution and cracking susceptibility of LPBF-fabricated Rene 41. By coupling experimental microstructural analysis with thermal modeling, this research uniquely identifies the relationship between geometry-specific thermal histories, carbide coarsening, and liquation cracking. Four different geometries with varying thickness were fabricated with the identical process parameters. It was found that the grain size and morphology are not affected by the part size. However, the thinner parts exhibited coarser sub-grain structures compared to the thicker ones. The crack formation was observed for the parts with cross-sections smaller than 1 mm, whereas thicker parts had high density without any defects. Further, the cracks were observed in the interdendritic regions, suggesting that liquation cracking was the active micro-crack formation mechanism. The detailed microstructural analysis combined with a thermal finite element analysis proved that the heat extraction efficiency was lower for thinner parts causing a lower cooling rate and coarser carbides, making them more susceptible to constitutional liquation. Microhardness measurements were conducted for each geometry and correlated with the observed microstructural variations. The findings highlight the critical need for geometry-specific optimization of LPBF process parameters to mitigate cracking and achieve microstructural uniformity, offering valuable insights into the fabrication of complex, high-performance aerospace components.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Role of scan strategies and heat treatment on grain structure evolution in Fe-Si soft magnetic alloys made by laser-powder bed fusion

A major goal in printing soft magnetic Fe-Si steels using additive manufacturing is to take advantage of the potential for complex geometric designs and site-specific grain control. One major step in the processing of these alloys is understanding how processing parameters might impact how the as-built microstructure responds to annealing (i.e. the annealing response). The impact of scan strategy on the annealing response for thin wall geometries is specifically explored. Two scan strategies were explored for a thin wall geometry that produced a strongly columnar grain structure and equiaxed grain structure. Additionally, samples from both scan strategies annealed at 1200 °C showed a marked difference in annealing response with the more equiaxed sample seeing full recrystallization and grain growth, while the more columnar grain structure saw little change in microstructure. After analysis through characterization techniques and thermal-mechanical simulations Differences in internal energy within the grains were ruled out because calculated GND density values were similar for both samples. The formation of secondary particles was ruled out as a contributing factor due to the type of oxide formations and their size. It was concluded that the contributing factor to the difference in the annealing response were a difference in the resulting grain size and the density of high angle grain boundaries. These two differences were largely attributed to differences in the thermal gradient conditions due to grains preferentially growing in the direction of the steepest thermal gradient.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Influence of implantation temperature and He implantation-induced defects on morphological evolution of co-deposited Cu-Mo nanocomposites

Here, we investigate the effect of high-temperature helium (He) implantation on microstructural evolution in physical-vapor-co-deposited nanocomposite thin films of copper (Cu) and molybdenum (Mo). The microstructure morphologies of He-implanted and He-free domains are characterized using transmission electron microscopy and statistical analysis. High implantation temperatures (500°C and 750°C) lead to coarsening of Cu and Mo domains and their eventual reorientation. The microstructure evolution in He-implanted and He-free domains is comparable, indicating that implantation-induced defects do not accelerate the coarsening of the nanocomposite as compared to annealing alone. This observation contrasts with previously reported effects of implantation-induced defects on single-phase nanocrystalline metals, which include enhancement of grain growth by increasing self-diffusivity or its inhibition by pinning of grain boundaries.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Carbon nanotube (CNT) reinforced 316L stainless steel composites made by laser powder bed fusion: Microstructure and wear response

Carbon nanotube (CNT) reinforced 316L stainless steel (SS) composites were fabricated by laser powder bed fusion (LPBF) additive manufacturing (AM). This study focuses on microstructure evolution, hardness, and wear behavior. The wear behavior for AM 316L SS and 1 wt% CNT/316L SS was studied by a dry sliding test under normal loads of 10, 15, and 25 N. The addition of CNT to 316L SS led to the change of solidification mode from cellular/columnar to dendritic growth, producing grain refinement. Nanoscale dendrites were observed. Although TEM characterization confirmed the existence of CNT in cell interior, most CNT were damaged, resulting in carbon material segregation along cellular/dendritic boundaries. The wear rate was found dramatically decreased due to the improved hardness. Compared to the adhesive and abrasive wear in AM 316L SS, the wear mechanism of CNT/316L composite was adhesion and oxidative wear. Furthermore, enhanced cellular/dendritic boundary strengthening by carbon segregation was the main strengthening mechanism of CNT/316L composite.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Densification, microstructure, and mechanical properties of Mo–30W alloys fabricated from conditioned powders

Refractory alloys, such as molybdenum-based systems, are attracting growing interest for applications in extreme environments, such as in the nuclear and aerospace industries. Recent advances in sintering technologies, coupled with mechanical alloying, have enabled the tailored design of these alloys by leveraging powder characteristics to control final microstructures and mechanical properties. In this study, Mo-30W alloys were fabricated using electric field-assisted sintering (EFAS) from ball-milled powders with and without hydrogen treatment to investigate the influence of surface oxides on material properties and sintering behavior. The results revealed that samples processed from as-ball-milled powder contained a high density of oxides within the microstructure, whereas oxide presence was significantly reduced in samples fabricated from hydrogen-treated powders. Interestingly, the two powder types led to opposite trends in grain size distribution: samples from untreated powders exhibited grain refinement from sample periphery to the center, while samples from hydrogen-treated powders showed grain coarsening toward the center. This behavior is attributed to temperature gradients present during sintering due to electrical percolation pathway differences during Joule heating. The powder surface oxides may have influenced the temperature distribution and grain evolution. Microhardness profiles measured along both axial and thickness directions were consistent with the grain size distribution. Furthermore, oxide films on powder surfaces have delayed densification by hindering particle necking and atomic diffusion during sintering.

36 - MATERIALS SCIENCE↗
DOE OSTI2020

Dislocation loop evolution in F/M steel T91 under in-situ ion irradiation: Influence of the presence of initial dislocations

Ferritic/Martensitic (F/M) steel T91 was irradiated in-situ to 4 and 10 dpa at 470 °C using 1 MeV Kr 2+ . Additionally, the microstructure evolution under irradiation was followed and characterized by in-situ Transmission Electron Microscopy (TEM), in terms of dislocation loop Burgers vector, average size and density as a function of dose. Furthermore, the influence of the presence of dislocations in the pre-irradiated matrix was investigated by comparing the radiation induced defect evolution in grains with and without initial dislocations.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Characterization of the microstructure of yttrium hydride under proton irradiation

High moderation per unit volume solid moderator materials like yttrium hydride (YH x ) are necessary for compact nuclear microreactors. However, the phase stability and hydrogen transport processes of YH x under high-temperature irradiation are largely unknown. Proton irradiation was conducted on YH x at 300 °C and 580 °C to 0.2 dpa using 1 MeV or 2 MeV protons in a high-vacuum environment. The hydrogen concentration was determined before and after irradiation using elastic recoil detection analysis, and microstructural evolution was examined via post-irradiation scanning transmission electron microscopy and Raman spectroscopy. Dislocation loops and cavities were observed in all conditions; their distribution was correlated with the bombarding proton energy and ion irradiation temperature. This work revealed that hydrogen retention is proportional to the formation of traps for hydrogen gas atoms and identified pathways for hydrogen release. The relative contributions of bulk or fast diffusion paths, such as grain boundaries, delamination boundaries, and stacking faults are discussed; the primary mechanisms of hydrogen loss are likely based on diffusion, ruling out artefacts of the experimental design. In conclusion, the study suggests proton irradiation may be a strong surrogate to study hydrogen transport in hydride moderator materials under irradiation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

In Situ Micro-Pillar Compression to Examine Radiation-Induced Hardening Mechanisms of FeCrAl Alloys

Here, the effects of 5 MeV Fe 2+ ion irradiation at 300°C on the microstructure evolution and deformation behavior of a FeCrAl C26M alloy are presented. It has been found that dislocation loop density increases an order of magnitude from 1 dpa to 16 dpa irradiations, whereas, the dislocation loop size saturates with increasing damage. Micropillars, 600 nm in diameter and 1.3 µm in height, were fabricated and compressed inside grains with <001>, <011> and <111> crystallographic orientations, respectively. {112} <111> has been identified as the primary slip system in both unirradiated and irradiated alloy. The increase in yield stress after irradiation is observed with measurable variation along <001> and <011> vs. along <111>. By applying the Orowan dispersed barrier model, the increase of yield stress is found mainly due to the slip resistance of radiation generated defect loops. Detailed transmission electron microscopy (TEM) studies were performed to quantify the Burgers vector and the distribution of irradiation induced dislocations at elevated strains. It is revealed that localized shear instability is caused by avalanche slip events of ½<111> dislocations gliding out of tested pillars. Simultaneously, a large number of sessile/immobile <100> dislocations formed in the vicinity of slip band, leading to the hardening at elevated strains.

36 MATERIALS SCIENCE↗
DOE OSTI2026

In-situ observations of cyclic deformation in an extruded Mg-2Nd-1Y-0.1Zr-0.1Ca alloy

In this study, the evolution of deformation mechanisms during cyclic loading in an extruded, solution-treated Mg–2Nd–1Y–0.1Zr–0.1Ca alloy was investigated using a combination of in-situ loading, scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and focused ion beam (FIB) nanofabrication. The initial microstructure exhibited a random crystallographic texture with no preferred grain orientation. Flat, rectangular dog-bone specimens were subjected to load-controlled, fully reversed fatigue for 50 cycles, during which the same region was sequentially mapped to track microstructural changes. After 10 cycles of loading deformation twins were observed. During tensile reloading detwinning or narrowing of those twinned regions occurred. After 20 cycles, detwinning ceased and residual twins remained in the material. SEM imaging revealed numerous surface slip traces after cyclic loading. EBSD-assisted slip trace analysis identified the activation of prismatic and pyramidal < c+a> slip systems during low-cycle fatigue. Site-specific scanning transmission electron microscopy (STEM) further revealed that deformation was also accommodated by basal < a> slip and the dissociation of < c+a> dislocations. Center-of-symmetry (COS) analysis confirmed that the dissociation of < c+a> dislocations resulted in the formation of I₁ intrinsic stacking faults after cyclic loading. These findings provide new insights into the complex interplay of dislocation mechanisms governing fatigue deformation in rare-earth-containing Mg alloys.

Cyclic deformation↗
DOE OSTI2021

In-situ TEM observation of shear induced microstructure evolution in Cu-Nb alloy

Phase boundaries in multiphase alloys govern defect interaction and chemical intermixing across different phases during plastic deformation. Dynamic interaction of defects with phase boundaries in multiphase alloys, especially for immiscible alloys, has been topic of significant research interest in recent years. In this work, we describe a novel approach for carrying out in-situ TEM shear deformation to directly observe interfacial microstructural evolution of a Cu-Nb alloy. A unique double shear specimen geometry is microfabricated by a focused ion beam technique to apply shear deformation upon push loading inside the TEM. From the real-time observation, we discover that the phase boundary with a zigzag morphology effectively blocks stacking faults nucleated in a Cu grain from slipping into a Nb grain. Meanwhile, the Cu phase bears the most plastic deformation through slip or twinning mechanisms. This work sheds light on understanding the shear deformation and the behavior of phase boundaries in multiphase alloys during shear deformation.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Tribological behaviors of nanotwinned Al alloys

Wear-induced damages cause significant materials loss each year. Al alloys are widely used by industry but usually have low wear resistance. Here, we compare the tribological behaviors of ultrafine grained Al, a nanoprecipitate hardened Al 7075 alloy and nanotwinned Al–Ni alloys using the nanoscratch. The nanotwinned Al–Ni alloys exhibit lower coefficient of friction and much greater wear resistance than the Al and Al 7075 alloys. Additionally, the enhanced wear properties of Al–Ni alloys arise from their high strength and the evolution of nanotwinned microstructures into gradient nanograins during wear. These findings on fundamental wear mechanisms in nanotwinned alloys may advance the discovery of wear-resistant metallic materials.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Evaluation of LPBF Steels for Nuclear Applications

This report provides an update on the prioritization of existing reactor materials for advanced manufacturing. This report is a Milestone 3 deliverable in FY2023, under work package CT-23AN130401 to support research and qualification activities supported by the Advanced Materials and Manufacturing Technologies (AMMT) program here at Argonne National Laboratory (ANL). The focus of FY23 for ANL included the determination of a decision criteria matrix for the prioritization of existing materials, the literature review of a select few Fe-based alloys, and working with vendors to obtain customized powders. The work package also includes fabricating test samples in a Renishaw AM400 Laser Powder Bed Fusion (LPBF) system and optimizing the process parameters. The major outcomes of this work package are: With collaborations from PNNL, ORNL, and INL, we were able to establish a decision criteria matrix containing a total of 6 categories and 31 different criteria. These will be used to downselect alloys for further evaluation; As part of that, 6 different Fe-based alloys were selected, 3 austenitic stainless steels (A709, D9, AFA) and 3 ferritic/martensitic steels (HT9, Grade 91, Grade 92). Customized powders were obtained from vendors in small quantities to fabricate initial prints to check printability of these specific alloys; A total of 72 single track experiments were performed on two alloy systems, 1 austenitic stainless steel (A709) and 1 ferritic/martensitic steel (Grade 91) in order to optimize the process parameters for the full 3d prints. The optimization led to the selection of 20 different processing conditions, 10 for each class of alloys; D9 and AFA alloys showed extensive cracking and porosity in the samples. This was due to less-than-ideal conditions present in the chamber during the deposition. A709 printed using the same process parameters showed almost fully dense samples with no noticeable porosity or any other defects. SEM and EBSD analysis revealed single phase FCC microstructure with cellular structure within the grains; HT9, Grade 91, Grade 92 alloys also showed no noticeable signs of cracking and ImageJ analysis showed porosity <0.5% in all conditions. While Grade 91 and Grade 92 showed single phase BCC microstructures, the presence of martensite laths was noted in HT9 alloy; Future work will include further characterization of these alloys to better understand the microstructural evolution during the 3d printing process.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Development of process parameters and post-build conditions for qualification of LPBF 316 SS

To harness the potential of laser powder bed fusion (LPBF) 316H stainless steel (SS) for use in advanced nuclear reactors, extensive research efforts are needed to develop optimal laser processing parameters and appropriate heat treatments, taking into account various manufacturing platforms and locations. Furthermore, it is crucial to assess the material properties in environments relevant to reactor operating conditions. In collaboration with Oak Ridge National Laboratory (ORNL) and Los Alamos National Laboratory (LANL), Argonne National Laboratory (ANL) is dedicated to gaining insights into how the manufacturing process and post-build treatments impact the performance of LPBF 316H SS. This report provides an overview of ANL's research findings for FY23, focusing on LPBF 316H SS produced using a Renishaw AM400 laser system. Specifically, our research has concentrated on three key areas: 1) Optimum laser processing parameters: Leveraging the high-throughput printing technology, we systematically varied the laser power, exposure time and point distance within the same build. By measuring the as-printed porosity, we identified an optimum printing parameter window that produced materials with near-complete density; 2) Post-built treatment development: Materials printed with the optimum laser parameters underwent treatments including stress relief, solution annealing, and hot isostatic pressing. Subsequently, we fabricated tension, creep, and fatigue specimens from materials subjected to these different conditions. Over the next year, a series of scoping tests will be conducted to facilitate the selection of the most suitable post-build treatment condition; 3) Thermal aging effects on microstructure and properties: thermal aging at 550°C, 650°C and 750°C was conducted on LPBF 316H SS specimens up to 2500 h. Microstructural characterization was performed with electron microscopy, and the evolution of the dislocation cell structures and secondary phases was studied. Microhardness tests and tension tests were conducted to quantify changes in mechanical properties. The results revealed that the aged LPBF 316H SS exhibited a high density of Cr-rich and Mo-rich fine precipitates within grains due to the presence of a high density of dislocations and the globally distributed dislocation cell structures, which served as heterogeneous nucleation sites for secondary phases. Along grain boundaries, a Mo-Cr-rich phase, observed in 750°C-aged conditions, displayed significant thermal coarsening. Throughout the aging process, various mechanisms, including stress relaxation, dislocation cell structure recovery, solution hardening, and precipitation hardening, competed to influence materials strength. These results contribute towards establishing the technical basis for qualifying LPBF 316H SS for advanced nuclear reactor applications.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Microchemical evolution of irradiated additive-manufactured HT9

The microstructural responses under 5 MeV Fe2 + single-ion-beam irradiation of three conditions of additive-manufactured (AM) HT9 steel using a powder-based directed energy deposition (DED) technique with and without postbuild heat treatments were investigated. Besides the observed dislocation loop formation and the absence of cavities at the irradiation condition of 50 dpa at 460 °C, Ni/Si/Mn-rich precipitates are found to form in all three conditions of AM-HT9, whereas Cu-rich clusters that arise from Cu uptake from the DED process are only observed in the heat-treated conditions, and not in the as-built (ASB) condition. Coprecipitation of the Cu- and Ni/Si/Mn-rich clusters occur near defect sinks such as line dislocations and grain boundaries in the heat-treated AM-HT9. The variation in microchemical evolution can be directly linked to the starting sink strength of the three AM-HT9 conditions, and the ASB condition with higher sink strength suppressed the responses observed in the postbuild heat-treated specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Synergistic effect of microstructure and defects on the initiation of fatigue cracks in additively manufactured Inconel 718

Fatigue cracks in additively manufactured (AMed) Inconel 718 (IN-718) in machined surface condition often initiate from persistent slip bands (PSBs) unlike other popular AM alloys such as 17-4 PH stainless steel or Ti-6Al-4V, where fatigue crack initiation is exclusively from volumetric defects; therefore, a competition between PSB- vs. defect- mediated crack initiation clearly exists. To shed light on the factors governing the competition, this study investigates the characteristics of cyclic strain localization, PSB formation, and crack initiation via crystal plasticity (CP) modeling of cyclic loading on polycrystalline aggregates which are then validated by experiments. In this work, a physics-based, free slip distance (FSD) dependent slip strength evolution law is proposed, which is shown to enable the CP model to simulate the heterogeneous strain distribution in IN-718. Implementing a crack initiation criterion based on strain contrast, the locations and lives for crack initiation can also be calculated. It is shown that both FSD and resolve shear stress influence the strain localization and crack initiation behaviors. The distribution of a localization parameter calculated based on the multiplication of FSD and Schmid factor within a grain is found to correlate well with the locations of PSBs. The maximum values of the localization parameters within a microstructure are shown to correlate well with the experimentally obtained crack initiation lives. The presence of volumetric defects in IN-718 generally do not impact strain localization behavior unless their size is large compared to the grain size.

42 ENGINEERING↗