Ammonolysis with N 2 -diluted NH 3 suppresses Ta( IV ) defects in BaTaO 2 N and enhances photocatalytic water oxidation

Abstract

BaTaO 2 N stands out among oxynitride photocatalysts because of its ability to capture visible light and to drive the photoelectrochemical water oxidation reaction. However, its solar energy conversion performance is limited by electron–hole recombination at Ta( IV ) defects in the material. These defects are formed by overreduction of the Ta(v) oxide precursor by excess ammonia under the high temperature conditions during ammonolysis. Here we show for the first time that Ta( IV ) defect concentrations can be lowered by conducting the ammonolysis reaction in mixed NH 3 /N 2 gas. The obtained BaTaO 2 N samples crystallize in the cubic CaTiO 3 structure type and form 200–300 nm faceted nanocrystals, based on X-ray diffraction, scanning electron microscopy, and HRTEM. Electron paramagnetic resonance spectra observe the Ta( IV ) defects at g = 1.999 and confirm an 11-fold reduction for the product synthesized in mixed (0.13 : 1.0 vol) NH 3 /N 2 gas, equivalent to 1.14 × 10 16 cm −3 Ta( IV ) ions. This optimized BaTaO 2 N has nearly twice the photocatalytic oxygen evolution activity (AQE of 6.78% at 400 nm) of a reference material made with 1.0 atm ammonia and 78% higher photoelectrochemical water oxidation photocurrent (0.9 mA cm −2 at 1.23 V vs. RHE) under simulated sunlight. According to X-ray photoelectron spectroscopy, remaining Ta( IV ) defects are concentrated in the surface region of the BaTaO 2 N particles, where >50% of all Ta ions are found in the +4 oxidation state. This surface Ta( IV ) population can be directly observed in Vibrating Kelvin Probe Surface Photovoltage Spectra (VK-SPV) via its 1.2–1.4 eV photovoltage onset. Here, it suggests that the surface Ta( IV ) ions contribute empty d-states 0.5–0.7 eV below the BaTaO 2 N conduction band edge. These findings highlight how the energetics and concentrations of Ta( IV ) defects influence the photoelectrochemical water oxidation ability of BaTaO 2 N. Additionally, the work establishes ammonolysis with diluted NH 3 as a new tool to minimize defects in BaTaO 2 N and to raise its solar energy conversion efficiency toward its theoretical limit. Because of its simplicity, the reduced ammonia pressure strategy will likely be applicable to other oxynitrides, which generally suffer from overreduction problems during ammonolysis.

Keep this discovery

BibTeXRIS

Salmanion, Mahya [University of California, Davis, CA (United States)] (ORCID:0000000157155917), Wang, Li [University of California, Davis, CA (United States)], Kandel, Rajesh [University of California, Davis, CA (United States)], Najaf, Zainab [University of California, Davis, CA (United States)], Rao, Guodong [University of California, Davis, CA (United States)] (ORCID:0000000180433436), Hahn, William [University of California, Davis, CA (United States)], van Benthem, Klaus [University of California, Davis, CA (United States); University of Alabama, Tuscaloosa, AL (United States)], Britt, R. David [University of California, Davis, CA (United States)] (ORCID:0000000308898436), Osterloh, Frank E. [University of California, Davis, CA (United States)] (ORCID:0000000292883407). 2026-01-01. Ammonolysis with N 2 -diluted NH 3 suppresses Ta( IV ) defects in BaTaO 2 N and enhances photocatalytic water oxidation. https://doi.org/10.1039/d5ta09305h

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Aliovalent gallium dopants remove Ti 3+ defects and improve photocatalytic and photoelectrochemical water oxidation properties of LaTiO 2 N

LaTiO 2 N is a promising semiconductor for the water splitting reaction due to its 2.1 eV band gap and stability against corrosion. However, its solar energy conversion is limited by Ti 3+ recombination defects introduced during ammonolysis. Here we show for the first time that Ti 3+ defects in LaTiO 2 N can be suppressed with incorporation of 2, 5, and 10% aliovalent gallium (Ga 3+ ) dopants during synthesis via the layered La 2 Ti 2 O 7 intermediate. Electron paramagnetic resonance (EPR) spectroscopy on the solid powders confirms a reduction in the Ti 3+ donor density from 2.97 × 10 17 cm −3 for the non-doped material to ∼6.24 × 10 16 cm −3 for 5% Ga-doped LaTiO 2 N. The remaining Ti 3+ defects are concentrated near the LaTiO 2 N surface, according to X-ray photoelectron spectroscopy. The defect reduction shifts the optical absorption edge from 2.02 to 2.09 eV and eliminates a broad absorption band at 1050 nm from the optical absorption spectra. It also removes a 1.0–1.7 eV sub-band gap photovoltage signal from surface photovoltage spectra. This suggests that empty Ti 3+ d-orbitals are located 1.0–1.7 eV above the LaTiO 2 N valence band edge. Removing these recombination states with increasing Ga 3+ content enhances the photoconversion efficiency of LaTiO 2 N during water oxidation. The optimized 2 wt% CoO x -loaded 5% Ga-doped LaTi O2 N material has a 16% AQE (400 nm) for O 2 production from aqueous silver nitrate solution and a ∼2.1 mA cm −2 water oxidation photocurrent at 1.23 V under 100 mW cm −2 Xe arc lamp illumination. The water oxidation photocurrent is stable during a 50 min test, and the Faraday efficiency for O 2 generation is 97%, confirming short-term corrosion stability of LaTiO 2 N. Altogether, these results provide a better understanding of the distribution, concentration, and impact of Ti 3+ defects on the optical, photovoltage, and photoelectrochemical properties of LaTiO 2 N. In combination with other defect control strategies, aliovalent Ga 3+ doping can help bring the solar energy conversion efficiency of LaTiO 2 N closer to the theoretical limit.

Wang, Li [University of California, Davis, CA (Uni

Fast lithium ion diffusion in brownmillerite Li x Sr 2 Co 2 O 5

Transition metal oxides not only exhibits novel magnetic properties but also provides outstanding ionic transports. Ionic conductors have great potential for interesting tunable physical properties via ionic liquid gating and novel energy storage applications such as all-solid-state lithium batteries. In particular, low migration barriers and high hopping attempt frequency are the keys to achieve fast ion diffusion in solids. Taking advantage of the oxygen-vacancy channel in Li x Sr 2 Co 2 O 5 , we show that migration barriers of lithium ion are as small as 0.28–0.17 eV depending on the lithium concentration rates. Our first-principles calculation also investigated hopping attempt frequency and concluded the room temperature ionic diffusivity and ion conductivity are high as 10 −7 –10 −6 cm 2 s −1 and 10 −3 –10 −2 Scm −1 , respectively, which outperform most of perovskite-type, garnet-type, and sulfide Li-ion solid-state electrolytes. This work proves Li x Sr 2 Co 2 O 5 as a promising super-ionic conductor.

Crystallographic defects

Photovoltage behaviour of p-Sb 2 S 3 photocathodes for hydrogen evolution: effect of n-In 2 S 3 passivation layers

The 1.76 eV band gap of antimony(iii) sulphide (Sb 2 S 3 ) makes this semiconductor material a promising light absorber for photoelectrochemical water splitting, but scalable fabrication approaches to efficient devices are still lacking. Here we show that compact Sb 2 S 3 films on FTO can be obtained by electrochemical growth from aqueous colloidal sulphur and antimony trichloride solutions, followed by mild annealing. These films can be converted into hydrogen evolution photocathodes after coating with In 2 S 3 passivation layers and the addition of Pt proton reduction co-catalysts. For the first time, vibrating Kelvin probe surface photovoltage (VKP-SPV) spectroscopy is used to observe the carrier dynamics in such photoelectrodes. While the bare Sb 2 S 3 films suffer from high surface recombination rates and poor electron extraction, the In 2 S 3 overlayer is found to raise the photovoltage and cathodic photocurrent density, due to passivation of surface defects and formation of a p–n heterojunction. In thick In 2 S 3 films, these benefits are offset by shading and slow electron transfer. Also, we find that O 2 strongly affects the band bending in the Sb 2 S 3 –air and In 2 S 3 –air junctions and their photovoltage. The optimised devices evolve H 2 at 77.5% Faradaic efficiency and with 0.084% applied bias photon-to-current efficiency (ABPE) at 0.12 V vs. RHE. The low ABPE value is attributed to Sb 2 S 3 sub-bandgap defects visible in SPV spectra, the random orientation of Sb 2 S 3 crystallites in the films, which inhibits charge transport, the absence of crystal facets of Sb 2 S 3 , and a detrimental Schottky junction at the FTO|Sb 2 S 3 interface.

de Araújo, Moisés A. [University of California, Da