Photovoltage behaviour of p-Sb 2 S 3 photocathodes for hydrogen evolution: effect of n-In 2 S 3 passivation layers

Abstract

The 1.76 eV band gap of antimony(iii) sulphide (Sb 2 S 3 ) makes this semiconductor material a promising light absorber for photoelectrochemical water splitting, but scalable fabrication approaches to efficient devices are still lacking. Here we show that compact Sb 2 S 3 films on FTO can be obtained by electrochemical growth from aqueous colloidal sulphur and antimony trichloride solutions, followed by mild annealing. These films can be converted into hydrogen evolution photocathodes after coating with In 2 S 3 passivation layers and the addition of Pt proton reduction co-catalysts. For the first time, vibrating Kelvin probe surface photovoltage (VKP-SPV) spectroscopy is used to observe the carrier dynamics in such photoelectrodes. While the bare Sb 2 S 3 films suffer from high surface recombination rates and poor electron extraction, the In 2 S 3 overlayer is found to raise the photovoltage and cathodic photocurrent density, due to passivation of surface defects and formation of a p–n heterojunction. In thick In 2 S 3 films, these benefits are offset by shading and slow electron transfer. Also, we find that O 2 strongly affects the band bending in the Sb 2 S 3 –air and In 2 S 3 –air junctions and their photovoltage. The optimised devices evolve H 2 at 77.5% Faradaic efficiency and with 0.084% applied bias photon-to-current efficiency (ABPE) at 0.12 V vs. RHE. The low ABPE value is attributed to Sb 2 S 3 sub-bandgap defects visible in SPV spectra, the random orientation of Sb 2 S 3 crystallites in the films, which inhibits charge transport, the absence of crystal facets of Sb 2 S 3 , and a detrimental Schottky junction at the FTO|Sb 2 S 3 interface.