Electrochemical Deconstruction of Ortho-Phthalate Plasticizers and Recovery of Plasticizing Moieties

Dauzvardis, Fabian [University of Delaware, Newark, DE (United States)] (ORCID:0009000397459028); Rosenthal, Joel [University of Delaware, Newark, DE (United States)] (ORCID:0000000268146503)

doi:10.3390/compounds6030035

DOE OSTI · 3600524

Electrochemical Deconstruction of Ortho-Phthalate Plasticizers and Recovery of Plasticizing Moieties

Dauzvardis, Fabian [University of Delaware, Newark, DE (United States)] (ORCID:0009000397459028)·Rosenthal, Joel [University of Delaware, Newark, DE (United States)] (ORCID:0000000268146503)

View original source ↗Read source document ↗Export metadata ↓

Abstract

Electrochemical methods for the direct reduction of alkyl esters have been understudied but provide a potential advantage for addressing specific waste streams given that such strategies often require only a minimal chemical profile. One such waste stream that could benefit from electrochemical remediation is poly(vinyl chloride) (PVC) plastics. PVC recycling often faces challenges due to the complexity of such waste. Solvent-based recycling methods pose several advantages for addressing post-use PVC; however, such methods are complicated by the high amounts of toxic legacy plasticizers (ortho-phthalates) present in PVC. A potential solution to addressing such phthalates is to address them electrochemically, coupled with recovery of the resulting valuable products. Presented herein is an optimized electrochemical method for ester activation that is leveraged to separate and recover the aromatic and alkyl components of ortho-phthalate plasticizers. The resulting aliphatic alcohols may be reused to prepare other non-toxic plasticizers. This electro-degradation method is demonstrated on six phthalates that have been identified to pose health concerns in addition to plasticizers recovered from commercial samples of PVC.

Explore related subjects

di-(2-ethylhexyl) phthalate electrochemistry plastic additives upcycling

Keep this discovery

BibTeX RIS

Dauzvardis, Fabian [University of Delaware, Newark, DE (United States)] (ORCID:0009000397459028), Rosenthal, Joel [University of Delaware, Newark, DE (United States)] (ORCID:0000000268146503). 2026-06-26. Electrochemical Deconstruction of Ortho-Phthalate Plasticizers and Recovery of Plasticizing Moieties. https://doi.org/10.3390/compounds6030035

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

di-(2-ethylhexyl) phthalate subject upcycling subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2024

Making Plasticized Polymer Electrolytes Stable Against Sodium Metal for High‐Energy Solid‐State Sodium Batteries

Solid polymer electrolytes based on plastic crystals are promising for solid-state sodium metal (Na 0 ) batteries, yet their practicality has been hindered by the notorious Na 0 -electrolyte interface instability issue, the underlying cause of which remains poorly understood. Here, in this study, by leveraging a model plasticized polymer electrolyte based on conventional succinonitrile plastic crystals, we uncover its failure origin in Na 0 batteries is associated with the formation of a thick and non-uniform solid electrolyte interphase (SEI) and whiskery Na 0 nucleation/growth. Furthermore, we design a new additive-embedded plasticized polymer electrolyte to manipulate the Na 0 deposition and SEI formulation. For the first time, we demonstrate that introducing fluoroethylene carbonate (FEC) additive into the succinonitrile-plasticized polymer electrolyte can effectively protect Na 0 against interfacial corrosion by facilitating the growth of dome-like Na 0 with thin, amorphous, and fluorine-rich SEIs, thus enabling significantly improved performances of Na//Na symmetric cells (1,800 h at 0.5 mA cm −2 ) and Na//Na 3 V 2 (PO 4 ) 3 full cells (93.0 % capacity retention after 1,200 cycles at 1 C rate in coin cells and 93.1 % capacity retention after 250 cycles at C/3 in pouch cells at room temperature). Our work provides valuable insights into the interfacial failure of plasticized polymer electrolytes and offers a promising solution to resolving the interfacial instability issue.

25 ENERGY STORAGE↗

DOE OSTI2025

Influence of functional additives, fillers, and pigments on thermal and catalytic pyrolysis of polyethylene for waste plastic upcycling

Pyrolysis offers a relatively green and economical method to convert waste plastics into valuable chemicals and fuels without the need for harmful solvents, toxic chemicals, or costly high-pressure reactors. Despite its popularity among chemical upcycling technologies, industrial adoption suffers from feedstock heterogeneity, low-quality products, and catalyst deactivation. Most plastics in our daily lives are formulated with functional additives, fillers, and colorants. These additives remaining in end-of-life waste streams increase feedstock heterogeneity, creating a challenging issue in recycling plastics. Still, the potential impacts of additives on the chemical upcycling of plastics have been poorly understood. In this study, polyethylene compounded with a range of widely used additives (antioxidants, stabilizers, pigments, fillers, slip agents, and flame retardants) was subjected to both thermal pyrolysis and catalytic pyrolysis in different catalyst-to-feedstock contact modes. It showed that many inorganic additives, such as talc, kaolin, CaCO 3 , TiO 2 , carbon black, and zinc stearate, facilitated polymer decomposition during pyrolysis, increasing light hydrocarbons while also promoting aromatic and carbon residue formation. Conversely, antioxidants and stabilizers inhibited depolymerization, favoring heavier hydrocarbons. During catalytic pyrolysis with HZSM-5 zeolite, additives strongly enhanced aromatic and catalytic coke formation, especially when there was direct contact between plastics and catalysts. Although certain additives seem beneficial in the short term by promoting polymer cracking and improving the selectivity of aromatics, the transport of the additives and their degradation products and increased carbon coking can contaminate products, deactivate or modify catalysts, and foul reactors. These findings address a critical knowledge gap in effectively converting waste plastics via a greener route.

42 ENGINEERING↗

DOE OSTI2026

Process control-enabled mitigation of microstructural and plastic heterogeneities in additively manufactured Grade 91 steel

Synergizing wire arc-directed energy deposition (WA-DED) additive manufacturing (AM) with particle-strengthened creep strength-enhanced ferritic (CSEF) steels enables fabrication and repair of critical power-plant components. Investigations focused on fusion-welded particle-strengthened CSEF steels, such as Grade 91 steel, have linked microstructurally heterogeneous regions—forming due to heat affected zones (HAZ)—with premature failure during elevated temperature service. Fusion-based AM, including WA-DED, likewise generates microstructurally and plastically heterogeneous regions due to spatiotemporally varying thermokinetics during deposition. However, works investigating such microstructural heterogeneities, their implications for mechanical behavior, and strategies to mitigate their formation remain scarce. This work identifies microstructurally and plastically heterogeneous regions within the WA-DED-processed Grade 91 steel. Spatial microhardness variations in the as-fabricated specimen correlate with the variation in the attributes of grain, martensitic microstructure, and precipitates across the fusion zone and HAZ. Digital image correlation-enabled tensile tests performed at 500 °C revealed pronounced deformation localization and a wave-like strain distribution, with wavelength close to the melt pool depth, indicating susceptibility of the as-fabricated components to premature creep failure. Such heterogeneity in microstructural and mechanical behavior was attributed to recurring solid-state phase transformations. Subsequently, an interlayer temperature control strategy was implemented, wherein maintaining interlayer temperature above the martensitic start temperature mitigated the heterogeneous microstructural and plastic response in the as-fabricated condition. Findings open pathways to achieving deformation-localization- and creep-resistant microstructures in WA-DED fabricated particle-strengthened CSEF steel components, reducing reliance on post-welding heat treatments—conventionally required to enhance creep resistance—and enabling on-demand, short lead-time fabrication of next-generation power-plant components.

Heat affected zones↗