Process control-enabled mitigation of microstructural and plastic heterogeneities in additively manufactured Grade 91 steel

Abstract

Synergizing wire arc-directed energy deposition (WA-DED) additive manufacturing (AM) with particle-strengthened creep strength-enhanced ferritic (CSEF) steels enables fabrication and repair of critical power-plant components. Investigations focused on fusion-welded particle-strengthened CSEF steels, such as Grade 91 steel, have linked microstructurally heterogeneous regions—forming due to heat affected zones (HAZ)—with premature failure during elevated temperature service. Fusion-based AM, including WA-DED, likewise generates microstructurally and plastically heterogeneous regions due to spatiotemporally varying thermokinetics during deposition. However, works investigating such microstructural heterogeneities, their implications for mechanical behavior, and strategies to mitigate their formation remain scarce. This work identifies microstructurally and plastically heterogeneous regions within the WA-DED-processed Grade 91 steel. Spatial microhardness variations in the as-fabricated specimen correlate with the variation in the attributes of grain, martensitic microstructure, and precipitates across the fusion zone and HAZ. Digital image correlation-enabled tensile tests performed at 500 °C revealed pronounced deformation localization and a wave-like strain distribution, with wavelength close to the melt pool depth, indicating susceptibility of the as-fabricated components to premature creep failure. Such heterogeneity in microstructural and mechanical behavior was attributed to recurring solid-state phase transformations. Subsequently, an interlayer temperature control strategy was implemented, wherein maintaining interlayer temperature above the martensitic start temperature mitigated the heterogeneous microstructural and plastic response in the as-fabricated condition. Findings open pathways to achieving deformation-localization- and creep-resistant microstructures in WA-DED fabricated particle-strengthened CSEF steel components, reducing reliance on post-welding heat treatments—conventionally required to enhance creep resistance—and enabling on-demand, short lead-time fabrication of next-generation power-plant components.

Explore related subjects

Keep this discovery

BibTeXRIS

Thapliyal, Saket [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000162415904), Tang, Wei [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000292749574), Nycz, Andrzej [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000174156559), Falcon, Pablo Luna [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)], Nandwana, Peeyush [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000251471668), Yamamoto, Yukinori [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000345744890). 2026-07-01. Process control-enabled mitigation of microstructural and plastic heterogeneities in additively manufactured Grade 91 steel. https://doi.org/10.1016/j.jmrt.2026.06.208

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Uncertainty quantification for competing failure mechanisms in unidirectionally reinforced carbon–carbon composites

Microstructure-informed finite element models play a key role in the carbon–carbon composite design process. Variability in manufacturing process parameters and experimental limitations introduce model parameter uncertainty. This study quantifies the effect of model parameter uncertainty on transverse tensile fracture behavior and proposes a methodology to predict the failure mode based on competing microscale damage mechanisms. Finite element simulations incorporate fiber–matrix interface debonding with cohesive zones and matrix damage with a smeared crack band approach in a unidirectional carbon–carbon composite. Results from a variance-based global sensitivity analysis identifies interfacial and matrix damage parameters as the primary source of variability in fracture behavior. Sobol’ indices indicate that matrix and cohesive zone strengths contribute 94% of the variance in the effective ultimate stress. A local analysis elucidates the relationship between these constituent strength parameters and failure mode by estimating the probability of cohesive, matrix, and mixed-mode dominated failure. Based on the results for 4000 simulations, 93% exhibit mixed-mode or interfacial dominated failure, which underscores the crucial role of fiber–matrix interface debonding in the transverse tensile failure of carbon–carbon composites. These uncertainty quantification results facilitate more efficient model calibration and provide a framework for microstructure-informed failure predictions in the face of manufacturing-induced uncertainty.

36 MATERIALS SCIENCE

Effect of Thermomechanical Processing on the Microstructure, Properties, and Work Behavior of a Ti50.5 Ni29.5 Pt20 High-Temperature Shape Memory Alloy

TiNiPt shape memory alloys are particularly promising for use as solid state actuators in environments up to 300 °C, due to a reasonable balance of proper ties, including acceptable work output. However, one of the challenges to commercializing a viable high-temperature shape memory alloy (HTSMA) is to establish the appropriate primary and secondary processing techniques for fabrication of the material in a required product form such as rod and wire. Consequently, a Ti 50.5 Ni 29.5 Pt 20 alloy was processed using several techniques including single- pass high-temperature extrusion, multiple-pass high-temperature extrusion, and cold drawing to produce bar stock, thin rod, and fine wire, respectively. The effects of heat treatment on the hardness, grain size, room temperature tensile properties, and transformation temperatures of hot- and cold-worked material were examined. Basic tensile properties as a function of temperature and the strain-temperature response of the alloy under constant load, for the determination of work output, were also investigated for various forms of the Ti 50.5 Ni 29.5 Pt 20 alloy, including fine wire.

Grain Size

Thermo-Mechanical Phase-Field Modeling of Fracture in High-Burnup UO2 Fuels Under Transient Conditions

This study presents a novel multiphysics phase-field fracture model to analyze high-burnup uranium dioxide (UO2) fuel behavior under transient reactor conditions. Fracture is treated as a stochastic phase transition, which inherently accounts for the random microstructural effects that lead to variations in the value of fracture strength. Moreover, the model takes into consideration the effects of temperature and burnup on thermal conductivity. Therefore, the model is able to predict crack initiation, propagation, and complex morphologies in response to thermal gradients and stress distributions. Several simulations were conducted to investigate the effects of operational and transient conditions on fracture behavior and the resulting cracking patterns. High-burnup fuels exhibit reduced thermal conductivity, elevating temperature gradients and resulting in extensive radial and circumferential cracks. Transient heating rates and temperatures significantly affect fracture patterns, with higher heating rates generating steeper gradients and more irregular crack trajectories. This approach provides critical insights into fuel integrity during accident scenarios and supports the safety evaluation of extended burnup limits.

Chemistry