Alternative Solid‐State Synthesis Route for Highly Fluorinated Disordered Rock‐Salt Cathode Materials for High‐Energy Lithium‐Ion Batteries

Abstract

Abstract Fluorination has been identified as a key element for enabling the stable cycling of earth‐abundant manganese‐based disordered rock salt (DRX) cathodes. However, fluorination in the DRX bulk remains a challenge for scalable solid‐state synthesis. In this study, a tailored reaction pathway is proposed to synthesize a highly fluorinated DRX. It is demonstrated for the first time that the unconventional precursors, Li 6 MnO 4 , MnF 2 , and TiO 2 , can avoid the formation of Mn‐based intermediates (such as Li 2 (Mn,Ti)O 3, LiMnO 2 , and Mn 3 O 4 ), which, once formed, persist until the synthesis temperature reaches close to or above that required for fluorine volatility. Therefore, this method can form a highly fluorinated DRX with a composition of Li 1.23 Mn 0.40 Ti 0.37 O 2−y F y ( y = 0.29–0.34) at a low temperature (800 °C) relative to that required for conventional DRX solid‐state reactions (≥900 °C). Li 1.23 Mn 0.40 Ti 0.37 O 2−y F y ( y = 0.29–0.34) delivers a specific capacity above 300 mAh g −1 and a specific energy of 980 Wh kg −1 at 30 °C. Detailed characterization reveals that this DRX phase reversibly utilizes Mn 2+/3+ redox in the low‐voltage region and Mn 3+/4+ redox in the middle‐voltage range, whereas reversible oxygen redox is observed at high potentials.