Ionic Conductive and Highly-Stable Interface for Alkali Metal Anodes

Abstract

Alkali metals are regarded as the most promising candidates for advanced anode for the next-generation batteries due to their high specific capacity, low electrochemical potential, and lightweight. However, critical problems of the alkali metal anodes, especially dendrite formation and interface stabilization, remain challenging to overcome. The solid electrolyte interphase (SEI) is a key factor affecting Li and Na deposition behavior and electrochemical performances. Herein, a facile and universal approach is successfully developed to fabricate ionic conductive interfaces for Li and Na metal anodes by modified atomic layer deposition (ALD). In this process, the Li metal (or Na metal) plays the role of Li (or Na) source without any additional Li (or Na) precursor during ALD. Moreover, the key questions about the influence of ALD deposition temperature on the compositions and structure of the coatings are addressed. The optimized ionic conductive coatings have significantly improved the electrochemical performances. In addition, the electrochemical phase-field model is performed to prove that the ionic conductive coating is very effective in promoting uniform electrodeposition. Further, this approach is universal and can be potentially applied to other different metal anodes. At the same time, it can be extended to other types of coatings or other deposition techniques.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Jin, Enzhong, Tantratian, Karnpiwat, Zhao, Changtai, Codirenzi, Anastasia, Goncharova, Lyudmila V., Wang, Changhong, Yang, Feipeng, Wang, Yijia, Pirayesh, Parham, Guo, Jinghua, Chen, Lei, Sun, Xueliang, Zhao, Yang. 2022-07-23. Ionic Conductive and Highly-Stable Interface for Alkali Metal Anodes. https://doi.org/10.1002/smll.202203045

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Frontiers in divalent $f$-block chemistry

Divalent f-block chemistry has undergone rapid expansion in recent years, driven by advances in the stabilization of low-valent lanthanide and actinide complexes. Although f-elements were historically accessed in the +3 or higher oxidation states, the isolation of +2 species has revealed unusual spectroscopic signatures, distinct bonding motifs, and multiple accessible electronic configurations that influence their chemical and physical properties. These developments have generated opportunities in areas including quantum information science, molecular magnetism, catalysis, and luminescence. Computational chemistry has played a pivotal role in interpreting the electronic structure and reactivity of these systems. However, accurately modeling divalent f-block complexes remains challenging because of strong electronic correlation, multiconfigurational character, and the presence of close-in-energy competing electronic states. As experimental capabilities and theoretical methodologies continue to advance, a comprehensive assessment of divalent chemistry is both timely and needed. In this Review, we integrate experimental and theoretical perspectives to provide a systematic analysis of divalent lanthanide and actinide complexes across the f-block series. We critically assess the role of ligands in determining competing ground-state configurations (f n d 1 vs. f n+1 ) resulting in their distinct spectroscopic, magnetic, and bonding properties. Finally, we discuss emerging strategies for predictive modeling and rational design of low-valent f-block molecular systems, with potential applications ranging from dinitrogen reduction to quantum technologies.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Unveiling the electronic structure and chemical bonding of the deprotonated cisplatin anion [(NH 3 )(NH 2 )PtCl 2 ] − via low-temperature photoelectron spectroscopy and theoretical calculations

The dehydrogenated cisplatin anion, [(NH 3 )(NH 2 )PtCl 2 ] − , was investigated via low-temperature photoelectron spectroscopy and theoretical calculations. Seven and four spectral peaks are respectively resolved at 193 and 266 nm, yielding rich electronic structure information for both the anion and neutral. From the threshold and maximum of the lowest electron binding energy band, the experimental adiabatic (ADE) and vertical detachment energies (VDE) are determined to be 3.3 ± 0.1 and 3.525 ± 0.025 eV, respectively. Theoretical calculations indicate the dominant isomer adopting a cis-geometry, in which the platinum center is coplanar with two chlorine and two nitrogen ligands. The calculated VDE of 3.54 eV based on this structure agrees well with the experimental value. Charge analyses reveal that the excess electron in the anion is primarily localized on the Pt and Cl atoms. A suite of theoretical analysis tools was employed to elucidate the bonding characteristics and interaction strength between Pt and its ligands.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Adsorption, charge transfer and a coverage-driven transition of alkali metals on rutile TiO 2 (110)

The interaction of alkali metals with metal oxide surfaces is central to tuning surface reactivity in heterogeneous catalysis and photocatalysis. Here we present a comprehensive DFT+U study of the adsorption of alkali metals (Li, Na, K, Rb, Cs) on the (110) surface of rutile TiO 2 . At low coverage (θ = 1/8), all alkali metals bind preferentially to bridging oxygen sites with adsorption energies in the range −4.06 to −3.33 eV, transferring nearly one full electron (0.92–0.99 |e|) to the substrate and inducing Ti 4+ → Ti 3+ reduction. The excess charge localizes preferentially at subsurface Ti sites in the form of small polarons. Diffusion barriers indicate facile motion along bridging-oxygen rows, whereas inter-row hopping is strongly hindered. Coverage effects were examined systematically for potassium: adsorption energy and charge transfer per K atom decrease monotonically with increasing θ. Strikingly, a sharp energy discontinuity occurs between θ = 4/8 and θ = 5/8 (ΔE ≈ 1 eV per atom), which we identify as a coverage-driven structural transition arising from steric packing constraints and enhanced K–K electrostatic repulsion once every (1×1) surface cell is occupied. This structural transition perfectly correlates with a dramatic drop in the work function down to an ultra-low minimum of 0.84 eV at θ=5/8, followed by a metallization- driven recovery at higher coverages. Ab initio molecular dynamics simulations confirm zigzag K arrangements at moderate coverage (θ = 1/3), while at high coverage (θ = 2/3) short-range K–K correlations emerge without long-range order. These results provide atomistic insight into the structure–activity relationships underlying alkali promotion effects on oxide-supported catalysts.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗