Initial Observations from AGR 5/6/7 Capsule 1

Stempien, John D·Palmer, Joe·T Pham, Cam Binh
View original source ↗Read source document ↗Export metadata ↓

Abstract

The fourth and final irradiation experiment in the Advanced Reactor Technologies (ART) Advanced Gas Reactor (AGR) fuel development and qualification program is designated as AGR-5/6/7. Data collected from the fabrication, irradiation, and post-irradiation examination (PIE) of this tristructural isotropic (TRISO) fuel are intended to serve as the primary data set for the qualification of this fuel for use in high-temperature gas-cooled reactors (INL 2021, Collin 2018b). However, data collected from the three preceding irradiations (i.e., AGR-1, AGR-2, and AGR-3/4) may also be used to supplement data collected from AGR-5/6/7. All components of the AGR-5/6/7 fuel (i.e., UCO kernels, TRISO coatings, and fuel compacts) were produced on an engineering scale at BWXT (Lynchburg, Virginia USA) according to the fuel specification (Marshall 2017). This fuel was irradiated in the northeast flux trap (NEFT) at the Advanced Test Reactor (ATR) at Idaho national Laboratory (INL) from February 16, 2018 to July 22, 2020 (Pham et al. 2021). Measurements in the fission product monitoring system (FPMS) indicated unexpected and significant numbers of failures of TRISO particles in Capsule 1 near the end of the sixth irradiation cycle (ATR Cycle 166A). In the fourth cycle (ATR Cycle 164B) and beyond, the sweep gas flow became very low (presumably from degradation of the capsule gas outlet line via an unidentified mechanism), and the program deliberately isolated Capsule 1 from gas flow periodically. In later cycles, attempts to reestablish any kind of flow in Capsule 1 were unsuccessful. With little or no flow through Capsule 1, FPMS measurements and enumerations of failed particles in Capsule 1 were difficult or impossible as was the ability to control the helium/neon gas mixture used for temperature control. Gas flows and fission gas activity in the effluent gas from the other AGR-5/6/7 capsules were also impacted by the Capsule 1 gas flow issues and the large increase in fission gas released from the Capsule 1.

Explore related subjects

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALSAGR 5 6 7 Capsule 1TRISO

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Stempien, John D, Palmer, Joe, T Pham, Cam Binh. 2022-04-15. Initial Observations from AGR 5/6/7 Capsule 1. https://www.osti.gov/biblio/1863261

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Evaluating transient fission gas release in high burnup light water reactor fuel during loss of coolant accident conditions via new capabilities

In this work, the role of transient fission gas release (tFGR) in the cladding burst behavior of high burnup fuel during a loss-of-coolant accident (LOCA) in commercial light water reactors was further investigated via the use of a new apparatus. During the LOCA-related temperature ramps of high burnup fuel, the release of fission gases exceeds the steady-state release observed under normal operating conditions. An enhancement was made to the Oak Ridge National Laboratory Severe Accident Test Station (SATS) to probe the various factors influencing tFGR. Experiments were performed on commercially irradiated, zirconium-clad uranium dioxide fuel, and this paper details the design of the experimental setup, the initial test results, and the subsequent post-test analyses. Notably, the first test on high burnup fuel demonstrated a LOCA-relevant tFGR of 5.3% from an unpressurized fuel segment. The ultimate tFGR was 10.7% for beyond LOCA conditions. A follow-up test on similar fuel revealed a tFGR of 12.6% under comparable conditions. Microstructural analysis and an analysis of the released gas provide some insight regarding the source of tFGR in the fuel. Finally, a grain boundary bubble model may aid in the interpretation of the results and offer a guide for future work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

Characterization of ceramic fuel powder packing fractions to support INFLUX

Triply periodic minimal surface (TPMS)-based structures show marked potential in novel nuclear reactor fuel designs, as their high surface area-to-volume ratio increases the efficiency of heat transfer out of the fuel, enabling safer, more innovative reactor designs. This milestone report addresses the role of dUO 2 powder processing route on the fill behavior of TPMS-based cladding shells to understand and advance the feasibility of manufacturing TPMS-based nuclear fuel forms. dUO 2 powder was processed through either a dry granulation route, varying consolidation pressure, or through milling, varying milling time, milling method and milled size distribution. The lowest tapped bulk densities (TBD), but best powder flowabilities, were obtained when testing unprocessed dUO 2 powder which was prone to self-agglomeration and formed low-density spheroids. The highest TBD and lowest flowabilities were obtained when using powder produced by hammer-milling dUO 2 powder to pass through a 200-mesh sieve, which led to particles with angular morphologies. Powder produced by dry granulation exhibited TBD that varied according to the consolidation pressure used to form the initial pellets and exhibited improved flowabilities when compared to hammer-milled material. Because of the large span of granule sizes formed as well as the irregular shape associated with the granules, a packing fraction of 0.69 was achieved, exceeding the analytical solution for random close packing of mono-sized spheres. TPMS polymer shells were loaded with unprocessed, granulated, and hammer-milled dUO 2 powders, and their qualitative packing behaviors were analyzed using x-ray computed tomography (xCT). TBDs calculated after loading TPMS polymer shells were 10-20% lower when compared to tapped bulk density measurements taken in a glass graduated cylinder, indicating a non-trivial impact on the tapped bulk density of either the TPMS channel size, TPMS channel surface material, powder cohesiveness, or a combination of the two parameters. A metallic zircaloy-4 TPMS shell will be loaded with hammer-milled dUO 2 powder upon receipt of the shell from Oak Ridge National Laboratory (ORNL) and shipped to Idaho National Labs (INL) for subsequent hot isostatic pressing (HIP) densification experiments.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗