Materials Data on Li13Sn5 by Materials Project

Abstract

Li13Sn5 crystallizes in the trigonal P-3m1 space group. The structure is two-dimensional and consists of one Li5Sn2 sheet oriented in the (0, 0, 1) direction and one Li8Sn3 sheet oriented in the (0, 0, 1) direction. In the Li5Sn2 sheet, there are three inequivalent Li sites. In the first Li site, Li is bonded in a 8-coordinate geometry to eight Li and six equivalent Sn atoms. There are six shorter (2.86 Å) and two longer (2.93 Å) Li–Li bond lengths. All Li–Sn bond lengths are 3.28 Å. In the second Li site, Li is bonded in a distorted trigonal non-coplanar geometry to one Li and three equivalent Sn atoms. All Li–Sn bond lengths are 2.92 Å. In the third Li site, Li is bonded to three equivalent Li and four equivalent Sn atoms to form a mixture of distorted face, edge, and corner-sharing LiLi3Sn4 tetrahedra. There are one shorter (2.77 Å) and three longer (2.86 Å) Li–Sn bond lengths. Sn is bonded in a 7-coordinate geometry to ten Li atoms. In the Li8Sn3 sheet, there are four inequivalent Li sites. In the first Li site, Li is bonded to three equivalent Li and four Sn atoms to form distorted LiLi3Sn4 tetrahedra that share corners with four LiLi3Sn4 tetrahedra, edges with nine LiLi3Sn4 tetrahedra, and faces with three equivalent LiLi4Sn4 tetrahedra. All Li–Li bond lengths are 2.85 Å. There are one shorter (2.79 Å) and three longer (2.89 Å) Li–Sn bond lengths. In the second Li site, Li is bonded to four equivalent Li and four Sn atoms to form a mixture of distorted face, edge, and corner-sharing LiLi4Sn4 tetrahedra. There are one shorter (2.83 Å) and three longer (2.89 Å) Li–Li bond lengths. There are three shorter (2.86 Å) and one longer (2.88 Å) Li–Sn bond lengths. In the third Li site, Li is bonded in a distorted trigonal non-coplanar geometry to one Li and three equivalent Sn atoms. The Li–Li bond length is 2.93 Å. All Li–Sn bond lengths are 2.91 Å. In the fourth Li site, Li is bonded in a 11-coordinate geometry to eight Li and six Sn atoms. There are three shorter (3.29 Å) and three longer (3.32 Å) Li–Sn bond lengths. There are two inequivalent Sn sites. In the first Sn site, Sn is bonded in a body-centered cubic geometry to fourteen Li atoms. In the second Sn site, Sn is bonded in a 7-coordinate geometry to ten Li atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-14. Materials Data on Li13Sn5 by Materials Project. https://doi.org/10.17188/1205129

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗