Laboratory Development of a Pot Calcination Process for Converting Liquid Wastes to Solids

Abstract

Simulated Darex, Purex, Thorex, and TBP-25 wastes were batch-evaporated and calcined to solids. The weight of residue was decreased to ~ 8% of the original waste for Darex, to ~ 4% for Purex, to ~ 2% for Thorex, and ~ 7% for TBP-25 by calcination to 1200°C. Semicontinuous evaporation and calcination to solids at 900°C of Darex and Purex wastes gave volume reduction factors of ~ 8 and 7 to 10, respectively. The nitrate contents of the residues from batch calcination to 800°C were from ~ 0.07 to 0.5 wt % while the nitrate contents of the residues from semicontinuous calcination to 900°C were from ~ 0.1 to 0.7 wt %. Sodium, calcium, and magnesium additives to Purex waste decreased the percent of sulfate volatilized into the condensate from ~ 30% to <0.5%. Replacement of the atmosphere above the waste with nitric oxide decreased ruthenium volatility from 50 to 60% of that originally present in Purex waste to 0.5 to 3.5%. The thermal conductivities for the calcined wastes, measured in situ, were all >0.1 Btu/hr ft °F at ~ 400°F and increased almost linearly with increasing temperature to >0.3 Btu/hr ft °F at ~ 1600°F in all cases studied.