Evaluation of Particle Degradation of a Ytterbium Disilicate Gas Turbine Coating in a Combustion Environment

Jamesa L Stokes·Michael J Presby
View original source ↗Read source document ↗Export metadata ↓

Abstract

Ytterbium disilicate (Yb2Si2O7) is a state-of-the-art topcoat material used in environmental barrier coatings (EBCs) to protect SiC-SiC composites from water vapor corrosion in gas turbine engines. However, it’s degradation by thermochemical and thermomechanical particle interactions may limit its use in next generation engine systems. Several static furnace tests have been performed on Yb2Si2O7 to elucidate methods of degradation, although dynamic testing in an engine-relevant environment has not been carried out. Ultimately, testing and evaluation of materials that incorporates all environmental damage modes will allow for an accurate assessment of long-term durability and operating lifetime. This work details the investigation of particle-induced erosion and corrosion of Yb2Si2O7 in NASA Glenn’s Erosion Burner Rig Facility. Coating durability was investigated as a function of test temperature, particle size, and deposition rate. Thermal cycling was also incorporated into testing to determine the interplay of heating/cooling cycles with particle degradation. Overall, these analyses will be used to determine coating robustness in an engine relevant environment.

Keep this discovery

BibTeXRIS

Jamesa L Stokes, Michael J Presby. Evaluation of Particle Degradation of a Ytterbium Disilicate Gas Turbine Coating in a Combustion Environment. https://ntrs.nasa.gov/citations/20260002056

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Turbines component

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRSDate not supplied

Evaluation of Particle Degradation of a Ytterbium Disilicate Gas Turbine Coating in a Combustion Environment

Ytterbium disilicate (Yb2Si2O7) is a state-of-the-art topcoat material used in environmental barrier coatings (EBCs) to protect SiC-SiC composites from water vapor corrosion in gas turbine engines. However, it’s degradation by thermochemical and thermomechanical particle interactions may limit its use in next generation engine systems. Several static furnace tests have been performed on Yb2Si2O7 to elucidate methods of degradation, although dynamic testing in an engine-relevant environment has not been carried out. Ultimately, testing and evaluation of materials that incorporates all environmental damage modes will allow for an accurate assessment of long-term durability and operating lifetime. This work details the investigation of particle-induced erosion and corrosion of Yb2Si2O7 in NASA Glenn’s Erosion Burner Rig Facility. Coating durability was investigated as a function of test temperature, particle size, and deposition rate. Thermal cycling was also incorporated into testing to determine the interplay of heating/cooling cycles with particle degradation. Overall, these analyses will be used to determine coating robustness in an engine relevant environment.

Jamesa L Stokes↗
NASA NTRS1994

Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines [Les consequences de l'endommagement des turbines I gaz par erosion, corrosion et objets étrangers]

The Conference Proceedings contains 31 papers presented at the Propulsion and Energetics Panel Symposium on Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines which was held from 25-28th April 1994, in Rotterdam, The Netherlands. The Technical Evaluation Report and the Keynote Address are included at the beginning and discussions follow most papers. The Symposium was arranged in the following Sessions: Operational Experience and Requirements (7); Deposition and Erosion (7); Foreign Object Damage (5); Coatings, Repairs and Materials Aspects - 1 (4); Coatings, Repairs and Materials Aspects - 2 (7); and Testing and Certification Procedures (1).

Deposition↗
NASA NTRS1994

Resistance of Silicon Nitride Turbine Components to Erosion and Hot Corrosion/Oxidation Attack

Silicon nitride turbine components are under intensive development by AlliedSignal to enable a new generation of higher power density auxiliary power systems. In order to be viable in the intended applications, silicon nitride turbine airfoils must be designed for survival in aggressive oxidizing combustion gas environments. Erosive and corrosive damage to ceramic airfoils from ingested sand and sea salt must be avoided. Recent engine test experience demonstrated that NT154 silicon nitride turbine vanes have exceptional resistance to sand erosion, relative to superalloys used in production engines. Similarly, NT154 silicon nitride has excellent resistance to oxidation in the temperature range of interest - up to 1400 C. Hot corrosion attack of superalloy gas turbine components is well documented. While hot corrosion from ingested sea salt will attack silicon nitride substantially less than the superalloys being replaced in initial engine applications, this degradation has the potential to limit component lives in advanced engine applications. Hot corrosion adversely affects the strength of silicon nitride in the 850 to 1300 C range. Since unacceptable reductions in strength must be rapidly identified and avoided, AlliedSignal and the NASA Lewis Research Center have pioneered the development of an environmental life prediction model for silicon nitride turbine components. Strength retention in flexure specimens following 1 to 3300 hour exposures to high temperature oxidation and hot corrosion has been measured and used to calibrate the life prediction model. Predicted component life is dependent upon engine design (stress, temperature, pressure, fuel/air ratio, gas velocity, and inlet air filtration), mission usage (fuel sulfur content, location (salt in air), and times at duty cycle power points), and material parameters. Preliminary analyses indicate that the hot corrosion resistance of NT154 silicon nitride is adequate for AlliedSignal's initial engine applications. Protective coatings and/or inlet air filtration may be required to achieve required ceramic component lives in more aggressive environments.

Nitride↗