Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines [Les consequences de l'endommagement des turbines I gaz par erosion, corrosion et objets étrangers]

Advisory Group for Aerospace Research and Development

Home/Archive/NASA NTRS

NASA NTRS · 19950013237

Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines [Les consequences de l'endommagement des turbines I gaz par erosion, corrosion et objets étrangers]

Advisory Group for Aerospace Research and Development

View original source ↗Export metadata ↓

Abstract

The Conference Proceedings contains 31 papers presented at the Propulsion and Energetics Panel Symposium on Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines which was held from 25-28th April 1994, in Rotterdam, The Netherlands. The Technical Evaluation Report and the Keynote Address are included at the beginning and discussions follow most papers. The Symposium was arranged in the following Sessions: Operational Experience and Requirements (7); Deposition and Erosion (7); Foreign Object Damage (5); Coatings, Repairs and Materials Aspects - 1 (4); Coatings, Repairs and Materials Aspects - 2 (7); and Testing and Certification Procedures (1).

Explore related subjects

Deposition Repair Coatings Sand Ice Dust Birds Foreign Bodies Erosion Corrosion Damage Aircraft Maintenance Gas Turbine Engines Aircraft Engines

Keep this discovery

BibTeX RIS

Advisory Group for Aerospace Research and Development. 1994-11-01. Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines [Les consequences de l'endommagement des turbines I gaz par erosion, corrosion et objets étrangers]. https://ntrs.nasa.gov/citations/19950013237

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Turbines component CORROSION subject DEPOSITION subject Dust subject erosion subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRS1994

New Trends in Coatings Developments for Turbine Blades: Materials Processing and Repair

Turbine engines for aeronautic applications now have to face strenuous requirements concerning not only operating performances but also reliability and repairability. This evolution of the specifications induces important consequences regarding the choice and the design of turbine blade protective coatings. This paper presents several key features concerning the deposition techniques and the real-life behavior of such coatings: (1) complex aluminides well suited to the protection against high temperature oxidation and hot corrosion of directionally solidified nickel-base superalloy turbine blades; (2) ceramic coatings used as thermal barriers - they have to exhibit both high resistance to thermomechanical fatigue and adequate smoothness; (3) processing techniques for thermal barriers, including plasma spraying, electron beam physical vapor deposition and plasma enhanced chemical vapor deposition; and (4) blades and coatings repair techniques.

S Alpérine↗

DOE OSTI2026

Healable Coatings as a Mechanism to Repair Leading Edge Erosion in Wind Energy

Wind turbine blades are highly engineered structures designed to face temperature extremes and high winds. However, erosion of the blade's leading edge and subsequent repair remains a significant and costly challenge for the wind energy industry. Repair of these leading edges can lead to large amounts of downtime for the turbine and significant operational inefficiencies. In this work, the strength of adhesion and healing ability of a commercially available vitrimer (Mallinda's VITRIMAX) was compared to that of a thermoplastic resin, which has previously been demonstrated in wind energy applications (Arkema's Elium) to evaluate their efficacy as surface coatings for wind turbine blades, particularly their leading edges. Vitrimers are a class of inherently reprocessable thermosets, and it was theorized that vitrimer-based leading edge coatings could enable more robust and efficient wind turbine blades with decreased operational downtime and safer maintenance practices. It was found that the VITRIMAX adhered better to the wind blades' surfaces than both the manufacturer's paint and Elium, with increases in pull-off strength of adhesion ranging from 24% to 83% above that of the original paint. Furthermore, the VITRIMAX adhered strongly to the underlying composite of each blade with strength of adhesion values increasing in ranges from 42% to 97% above that of the original paint. Finally, the vitrimer coating showed an 88% decrease in surface roughness compared to end-of-life blade materials, and initial healing demonstrations in which coatings were manually scratched and subsequently healed exhibited an ~84.5% decrease in scratch depths.

Hubbard, Amber [ORNL]↗

DOE OSTI2026

Feasibility of Nitrogen as a Carrier Gas for Inconel Cold Spray in Hydropower Application

Cold spray deposition of Inconel nickel alloys has emerged as a promising strategy for mitigating cavitation erosion in hydropower facilities. Most prior developments employ helium (He) as the carrier gas because it enables high particle velocities and the formation of dense coatings. However, He is nearly two orders of magnitude more expensive than nitrogen (N2), which limits its widespread adoption in the hydropower sector. Although He-based cold spray can be justified for high value repairs, the lower cost and broad availability of N2 make it an attractive alternative. This study assesses the feasibility of N2-based cold spray of Inconel 625 powders for hydropower applications. Cavitation erosion testing shows that He-based coating exhibits cavitation resistance of ~398% relative to the 304L stainless steel (SS304L) substrate. In contrast, N2-based coating shows substantially lower cavitation resistance, reaching only ~69% of the SS304L substrate, even when higher carrier gas temperature and pressure are applied. When the Inconel 625 powder size is reduced from 44 to 22 µm under N2-based cold spray conditions, cavitation resistance increases significantly to ~148% of the SS304L substrate. Additional improvement can be obtained by incorporating fine chromium carbide powders into the feedstock, resulting in cavitation resistance of ~172% of the SS304L substrate. Overall, with optimized feedstock design, N2-based cold spray offers a practical and cost-effective approach for producing cavitation resistant coatings on hydropower components, although He-based cold spray continues to deliver higher cavitation resistance.

Wang, Tianhao↗