Fabricating Solid-State Batteries for Electric Aviation

Griffin Usie·Donald A Dornbusch·Yi Lin·William Huddleston·Rocco P Viggiano
View original source ↗Export metadata ↓

Abstract

All-solid-state lithium batteries are widely reputed as the next major step in energy storage technology on account their drastically improved safety over wet cells, as solid electrolytes lack the volatile compounds in wet electrolytes that make them combustible. This enhanced safety enables a far wider range of products and vehicles to go fully electric and aligns with future NASA missions that require high performing, reliable, and safe batteries. However, they currently face issues with implementation in consumer products due to the often-poor mechanical properties of the solid electrolyte and relative difficulty to manufacture. Typical solid-state electrolyte challenges were bypassed by incorporating a range of polymeric binders into a solid electrolyte suspension and cast onto a composite carbon-sulfide cathode to create a single bilayer film. The resulting films display superior flexibility and durability compared to solid-electrolyte films typically discussed in literature without compromising the thinness of the films. The bilayer film was then punched into 12.7 cm diameter discs and 4 cm by 5 cm sheets, pressed, and assembled into coin cells and pouch cells respectively.

Explore related subjects

BatteriesSolid-stateLithium-sulfurSolid-state batteriesEnergy storage

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Griffin Usie, Donald A Dornbusch, Yi Lin, William Huddleston, Rocco P Viggiano. Fabricating Solid-State Batteries for Electric Aviation. https://ntrs.nasa.gov/citations/20240004219

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Elucidating Lithium Transport Mechanisms in Disordered LiF from Machine-Learning Molecular Dynamics Simulations

Lithium fluoride (LiF) is a ubiquitous component of solid- and cathode–electrolyte interphases, yet its functional role remains unclear under the structural and chemical heterogeneity typical of cycling batteries. Here, we systematically quantify how structural disorder, off-stoichiometry, and strain govern Li-ion transport in LiF. Using a machine-learning potential to enable extensive molecular-dynamics sampling, we compare crystalline and amorphous LiF, Li 0.95 F, and LiF 0.95 , and evaluate the impact of small homogeneous deformations. Defect-free crystalline LiF is effectively ion-blocking at 300−500 K, whereas amorphization generates free-volume–assisted percolation pathways that facilitates Li-ion diffusion. At elevated temperatures, thermodynamically driven crystallization disrupts these pathways, leading to non-Arrhenius behavior. In crystalline phases, Li deficiency activates vacancy-mediated diffusion, while in amorphous LiF, transport is governed primarily by network connectivity. Strain is found to have only a marginal effect on Li mobility in both crystalline and amorphous structures.

Batteries↗
DOE OSTI2026

Thermodynamic Control of Interface Directs MnO 2 Nucleation Chemistry for Dense and Conformal Electrodeposition

Manganese dioxide (MnO 2 ) is widely recognized as a promising material for high-energy-density energy storage systems due to its broad applicability and facile electrodeposition. However, achieving uniform, thin, and high-mass-loading MnO 2 coatings on high-surface-area electrodes remains a significant challenge. Conventional electrodeposition methods typically yield nonuniform, thick layers with poor conductivity and limited material utilization, restricting their practical use. Here, we uncover a thermodynamically engineered vanadyl/pervanadyl (VO 2+ /VO 2 + ) interface that fundamentally reshapes MnO 2 electrodeposition chemistry, enabling highly uniform and dense coatings. Here, combining in situ AFM measurement, Classical Nucleation Theory, and Johnson–Mehl–Avrami–Kolmogorov modeling, we show that this interface reduces early-stage detectable MnO 2 island size by 35-fold and shifts the MnO 2 growth from diffusion-limited to reaction-limited progressive nucleation. This thermodynamically controlled interface yields highly dense and conformal MnO 2 films with record-high mass loading of 241 mg cm –2 (1607 mg cm –3 ) on 3D-printed graphene aerogels, without compromising porosity or inducing thickness gradient. As a prototype demonstration, the resulting MnO 2 electrodes deliver record-setting volumetric performance in both capacitors (106 F cm –3 ) and Zn//MnO 2 pouch cells (162 mAh cm –3 ). Beyond energy storage, our findings demonstrate the significance of thermodynamic interface control in MnO 2 nucleation chemistry for achieving dense and uniform coatings on various substrates, with implications for electrocatalysis, semiconductor processing, and advanced materials manufacturing.

Batteries↗