Characterization of a New Phase and Its Effect on the Work Characteristics of a Near-Stoichiometric Ni30Pt20Ti50 High-Temperature Shape Memory Alloy (HTSMA)

A Garg; D Gaydosh; M Kaufman; L Kovarik; M J Mills; R D Noebe; Santo Padula, II; G S Bigelow; D Diercks; Sarah McMurray

Home/Archive/NASA NTRS

NASA NTRS · 20090008504

Characterization of a New Phase and Its Effect on the Work Characteristics of a Near-Stoichiometric Ni30Pt20Ti50 High-Temperature Shape Memory Alloy (HTSMA)

A Garg·D Gaydosh·M Kaufman·L Kovarik·M J Mills·R D Noebe·Santo Padula, II·G S Bigelow·D Diercks·Sarah McMurray

View original source ↗Read source document ↗Export metadata ↓

Abstract

A new phase observed in a nominal Ni 30 Pt 20 Ti 50 (at.%) high temperature shape memory alloy has been characterized using transmission electron microscopy and 3-D atom probe tomography. This phase forms homogenously in the B2 austenite matrix by a nucleation and growth mechanism and results in a concomitant increase in the martensitic transformation temperature of the base alloy. Although the structure of this phase typically contains a high density of faults making characterization difficult, it appears to be trigonal (-3m point group) with a o ~1.28 nm and c o ~1.4 nm. Precipitation of this phase increases the microhardness of the alloy substantially over that of the solution treated and quenched single-phase material. The effect of precipitation strengthening on the work characteristics of the alloy has been explored through load-biased strain-temperature testing in the solution-treated condition and after aging at 500 ºC for times ranging from 1 to 256 hours. Work output was found to increase in the aged alloy as a result of an increase in transformation strain, but was not very sensitive to aging time. The amount of permanent deformation that occurred during thermal cycling under load was small but increased with increasing aging time and stress. Nevertheless, the dimensional stability of the alloy at short aging times (1-4 hours) was still very good making it a potentially useful material for high-temperature actuator applications.

Keep this discovery

BibTeX RIS

A Garg, D Gaydosh, M Kaufman, L Kovarik, M J Mills, R D Noebe, Santo Padula, II, G S Bigelow, D Diercks, Sarah McMurray. 2008-09-21. Characterization of a New Phase and Its Effect on the Work Characteristics of a Near-Stoichiometric Ni30Pt20Ti50 High-Temperature Shape Memory Alloy (HTSMA). https://ntrs.nasa.gov/citations/20090008504

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2005

Characterization of Ternary NiTiPt High-Temperature Shape Memory Alloys

Pt additions substituted for Ni in NiTi alloys are known to increase the transformation temperature of the alloy but only at fairly high Pt levels. However, until now only ternary compositions with a very specific stoichiometry, Ni 50-x Pt x Ti 50 , have been investigated and then only to very limited extent. In order to learn more about this potential high-temperature shape memory alloy system, a series of over twenty alloys along and on either side of a line of constant stoichiometry between NiTi and TiPt were arc melted, homogenized, and characterized in terms of their microstructure, transformation temperatures, and hardness. The resulting microstructures were examined by scanning electron microscopy and the phase compositions quantified by energy dispersive spectroscopy. "Stoichiometric" compositions along a line of constant stoichiometry between NiTi to TiPt were essentially single phase but any deviations from a stoichiometry of (Ni,Pt) 50 Ti 50 resulted in the presence of at least two different intermetallic phases, depending on the overall composition of the alloy. Essentially all alloys, whether single or two-phase, still under went a martensitic transformation. It was found that the transformation temperatures were depressed with initial Pt additions but at levels greater than 10 at.% the transformation temperature increased linearly with Pt content. Also, the transformation temperatures were relatively insensitive to alloy stoichiometry within the range of alloys examined. Finally, the dependence of hardness on Pt content for a series of Ni 50-x Pt x Ti 50 alloys showed solution softening at low Pt levels, while hardening was observed in ternary alloys containing more than about 10 at.% Pt. On either side of these "stoichiometric" compositions, hardness was also found to increase significantly.

Transformation Temperatures↗

DOE OSTI2026

Stoichiometric effects on grain growth in zirconium carbide coatings for high-temperature nuclear fuel

Interest in coated particle fuel for space nuclear propulsion (SNP) has expanded in recent years due to successful demonstrations of the resiliency of the coatings to extreme environments. For SNP applications, the coating layer for the particle design needs to be able to withstand exposure to high temperature hydrogen during operating conditions. ZrC has been proposed as a protective layer, however, it is important to understand the high temperature behavior to ensure adequate protection to this fuel. In this study, surrogate ZrC coated particles were heat treated at 1900 °C up to 300 min, to examine how the microstructure evolves when exposed to high temperature. Scanning electron microscopy and electron backscatter diffraction (EBSD) were conducted to determine grain size and grain boundary character and orientation to determine the degree of change in the ZrC layer post heat treatment. Raman spectroscopy provided insight to understand how the as-fabricated stoichiometry of each sample contributed to the differences in grain growth behavior. Despite the as-fabricated samples showing a similar initial grain size and grain boundary character, the samples with a higher amount of excess carbon exhibited smaller grain areas and slower growth rates when exposed to 1900 °C. In conclusion, this investigation details the as-fabricated microstructure of the ZrC layer, specifically grain size, evolved under high temperature as this can impact the performance of the fuel under operating conditions.

EBSD↗

DOE OSTI2025

Tunable high Néel temperature and large anomalous Hall response in antiferromagnetic Weyl semimetal Mn 3 Sn 1− x Ga x thin films

Antiferromagnetic Weyl semimetals based on Mn 3 X(X = Ge, Sn, Ga) kagome compounds exhibit the same ferromagnetic-like responses, including anomalous Hall, Nernst, and magneto-optical effects, as recently discussed for altermagnets. Driven by the Berry curvature due to Weyl fermions, these materials show a disproportionately large magnitude of electromagnetic effects even in the absence of large magnetization. For applications it is crucial to realize these responses in a wide range of temperatures both below and above 300 K. While stoichiometric Mn 3 X materials do not offer optimal performance, we show that Mn 3 Sn 1−x Ga x sputtered films with a variable composition offers a tunable Néel temperature, T N ≈ 425 ± 6–500 ± 15 K, which is crucial for device applications, together with a large tunable anomalous Hall effect. Our thin film growth method enables continuous and precise control over the film composition between x = 0 and x = 1. Through a detailed magnetization and Hall transport, we establish the magnetic phase diagram for the hexagonal Mn 3 Sn 1−x Ga x . Our results reveal an enhanced T N and antichiral magnetic phase in Ga-doped Mn 3 Sn and an enhanced anomalous Hall magnitude in Sn-doped Mn 3 Ga compared to their stoichiometric undoped forms. Our work demonstrates a route to optimize the technologically relevant antiferromagnets for various applications.

Magnetic properties and materials↗