Analysis of the Erosion of Cubic Centered and Face Centered Metallic Materials [Analyse de L'erosion de Matereaux Metalliques de Structures Cubiques Centree et Face Centree]

A Magnée
View original source ↗Export metadata ↓

Abstract

A generalized law of erosion, in nondimensional form, is proposed. The aforementioned explicitly gives an account of the nature and the microstructure of the material impacted, the angle of impact of the particles, and their hardness. The erosion behavior of various steels, pig iron, and cast iron is examined as well as the behavior of new ordered intermetallic materials, Fe-25% Al-(Zr, Cr, B). The concern of such alloys in an erosion-corrosion environment is shown. --- Une loi généralisée d'usure par érosion, sous forme non dimensionnelle, est proposée. Celle-ci rend compte explicitement de la nature et de la microstructure du matériau impacté, de l'angle d'impact des particules, de leur acuité at de leur durete. Le comportement à l'érosion de divers aciers et fontes est examiné ainsi que la tenue de nouveaux matériaux intermétalliques ordonnés Fe-25% Al - (Zr, Cr, B). L'interet de tels alliages dans des environnements agressifs du type érosion-corrosion est montré. Mots clés: usure, érosion, modèle, matériaux métalliques, intermétalliques Fe-Al.

Keep this discovery

BibTeXRIS

A Magnée. 1994-11-01. Analysis of the Erosion of Cubic Centered and Face Centered Metallic Materials [Analyse de L'erosion de Matereaux Metalliques de Structures Cubiques Centree et Face Centree]. https://ntrs.nasa.gov/citations/19950013258

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS1994

Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines [Les consequences de l'endommagement des turbines I gaz par erosion, corrosion et objets étrangers]

The Conference Proceedings contains 31 papers presented at the Propulsion and Energetics Panel Symposium on Erosion, Corrosion and Foreign Object Damage Effects in Gas Turbines which was held from 25-28th April 1994, in Rotterdam, The Netherlands. The Technical Evaluation Report and the Keynote Address are included at the beginning and discussions follow most papers. The Symposium was arranged in the following Sessions: Operational Experience and Requirements (7); Deposition and Erosion (7); Foreign Object Damage (5); Coatings, Repairs and Materials Aspects - 1 (4); Coatings, Repairs and Materials Aspects - 2 (7); and Testing and Certification Procedures (1).

Deposition↗
NASA NTRS2025

Erosion Results of the MISSE 9-15 Polymers and Composites Experiment 1-4 (PCE 1-4)

Polymers and other oxidizable materials on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded from reaction with atomic oxygen (AO). Therefore, in order to design durable spacecraft it is important to know the extent of erosion that will occur during a mission. This can be determined by knowing the LEO AO erosion yield, E y (volume loss per incident oxygen atom), of materials susceptible to AO reaction. In addition, recent flight experiments have shown that the AO E y can vary with the AO fluence and/or solar exposure. Therefore, obtaining AO E y data for materials flown on various spaceflight missions is important. NASA Glenn Research Center has flown numerous experiments as part of the Materials International Space Station Experiment (MISSE) missions on the exterior of the International Space Station (ISS) to characterize the LEO E y of polymers, composites, protective coatings, and other spacecraft materials. Recently, four Glenn experiments with 365 flight (F) samples were flown on ISS’s MISSE-Flight Facility (MISSE-FF). These experiments are the Polymers and Composites Experiment-1 (PCE-1) flown as part of the MISSE-9 mission, the PCE-2 flown as part of the MISSE-10 mission, the PCE-3 flown as part of the MISSE-12 and MISSE-15 missions, and the PCE-4 flown as part of the MISSE-13 mission. Although each experiment had numerous sample objectives, the primary objective was to determine the LEO AO E y of various spacecraft materials as a function of solar irradiation and AO fluence. This paper provides a summary of the erosion data for the PCE 1-4 AO E y samples. The AO E y for 150 samples flown in either the LEO ram, wake, zenith or nadir directions are provided. The AO ram fluence varied from 2.97×10 20 atoms/cm 2 after 0.89 years of direct space exposure (with relatively high levels of Si contamination) on MISSE 12 to 3.93×10 20 atoms/cm 2 after 1.17 years of direct space exposure on MISSE-10. The ram AO E y values for uncoated polymers range from 3.81×10 –25 cm 3 /atom for polytetrafluoroethylene (M9R-C20 F) exposed to an AO fluence of 3.44×10 20 atoms/cm 2 on MISSE-9 to 4.43×10 –23 cm 3 /atom for AO etched low density polyimide aerogel (M12R-C21 F) exposed to an AO fluence of 2.97×10 21 atoms/cm 2 on MISSE-12. Because of the low AO fluence and relatively high Si contamination, a number of PCE-3 wake samples experienced mass gain. Thus, AO E y values are not provided for these samples. Although there are calculated AO E y values for the zenith, wake and nadir samples, the ram AO E y for a particular material is a more reliable value in terms of AO exposure because the zenith, wake and nadir directions were exposed to either no or very little AO fluence and thus other space environmental factors (i.e. vacuum, thermal extremes and thermal cycling, and/or various types of radiation) are responsible for the mass loss.

Erosion yield↗