Degradation of optical components in a space environment

Linda L. Dehainaut; John Kenemuth; Cynthia E. Tidler; David W. Seegmiller

Home/Archive/NASA NTRS

NASA NTRS · 19920018064

Degradation of optical components in a space environment

Linda L. Dehainaut·John Kenemuth·Cynthia E. Tidler·David W. Seegmiller

View original source ↗Export metadata ↓

Abstract

The objective of the Phillips Laboratory (PL) Long Duration Exposure Facility (LDEF) experiment is to determine the adverse effects of the natural space environment on laser optical component and coating materials. The LDEF experiment provides a unique opportunity for the study of optical material response to an extended low earth orbit space exposure. The PL samples consist of 10 sets of the six materials each. The materials are uncoated fused silica, magnesium fluoride coated fused silica, uncoated molybdenum, molybdenum coated with chromium, silver and thorium fluoride, diamond turned copper, and diamond turned nickel plated copper. Performance degradation will be correlated to establish trends between sample location, duration of exposure, atomic oxygen exposure and other space environmental conditions. This paper discusses the results of the tests thus far performed on the LDEF samples and the plans for the future.

Keep this discovery

BibTeX RIS

Linda L. Dehainaut, John Kenemuth, Cynthia E. Tidler, David W. Seegmiller. 1992-06-01. Degradation of optical components in a space environment. https://ntrs.nasa.gov/citations/19920018064

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2026

A Study of Space Environment Effect on Highly Thermally Conductive Hybrid Carbon Fiber Polymer Composites

A set of novel highly thermally conductive hybrid carbon fiber (CF) polymer composites has been developed for lightweight thermal radiator applications in space missions. This study investigates the effects of the space environment on these materials following exposure in low-Earth orbit (LEO) during the Materials International Space Station Experiment (MISSE)-17 flight mission, where samples experienced 159 days of combined atomic oxygen (AO), ultraviolet (UV) radiation, high vacuum, space radiation and thermal cycling. Post-flight characterization included weight loss, surface morphology, thermo-optical properties, molecular structures, glass transition temperature, thermal degradation and thermal conductivity analyses. The pyrolytic graphite sheet (PGS) samples exhibited negligible weight loss, stable thermo-optical property, and only minor oxidation signature on the exposed surface. Although AO erosion of the epoxy polymer matrix was evident, carbon nanotube (CNT)-infused PGS/CF epoxy composites retained high thermal emissivity and preserved their high thermal conductivities. These results demonstrate that the novel highly thermally conductive hybrid CF composites possess strong environmental resilience and are promising candidates for lightweight thermal radiators and thermal management components in future space exploration missions.

Space Environment↗

NASA NTRS2026

Investigation of Bipropellant Plume-Induced Contamination Effects on Coverglass Materials

Contamination and degradation of external spacecraft materials by unburned and partially combusted species from bipropellant thruster plumes has long been observed as a key component of the induced space environment. Space shuttle flight experiments and returned flight hardware from the International Space Station (ISS) have both experienced microscopic impact features induced by high-velocity thruster plume droplets. Analytical results have shown that droplet impingement angle relative to a receiving surface plays a key role in the surface damage. Although impacts with normal impingement angles contribute more severely to surface degradation than highly oblique angles, surface effects at higher impingement angles should not be dismissed. Thruster plume-induced materials degradation is a complex phenomenon that depends on a variety of parameters, including but not limited to material type, system temperature and pressure, plume composition, and thruster firing specifications such as number of pulses, pulse duration, and sample distance from the thruster. For space applications, attaining the vacuum pressure and temperature conditions necessary for flight-like plume expansion and exposure conditions is not a trivial task. The German Aerospace Center (Deutsches Zentrum für Luft- und Raumfahrt, DLR) is a facility uniquely capable of simulating such conditions. Test coupons were exposed to bipropellant thruster firings under high vacuum at the DLR facility. Percent area coverage (PAC) and droplet size distributions were evaluated for the uncoated and coated solar array coverglass materials over a range of impingement angles (0̊ to 75̊). A post-test imaging workflow was developed that aimed to quantify changes in sample surface morphology obtained from scanning electron microscopy (SEM) images using the Image Processing and Analysis in Java (ImageJ) tool; an opensource image processing software. The goal was to create a framework through which to evaluate the effect of bipropellant-induced PAC and droplet size distribution on solar array coverglass optical transmission losses. Understanding this relationship is important because optical transmission losses are known to lead to current reduction in solar power generation systems. In addition to the development of surface characterization workflows, valuable lessons learned as they pertain to future investigations and experiments will be discussed. The authors hope that sharing these lessons will facilitate more utilization of DLR’s unique capabilities as well as open the conversation for how best to address experimental characterization of flight-like plume expansion and its impacts on materials surface degradation effects.

Gateway↗

NASA NTRS2026

Artemis Suit Material Optical Property Testing of Dust Exposed Fabrics

This paper highlights one aspect of NASA’s ongoing technology-infusion effort to design, fabricate, and test a next-generation outer shell fabric for a lunar Extravehicular Activity (EVA) space suit, a critical component of sustained lunar exploration. Managing thermal loads on the Moon is essential for astronaut safety and suit performance. The suit’s exterior fabric directly influences heat gain and loss through its optical properties: low solar absorptivity minimizes sunlight absorption, while high infrared emissivity aids radiative cooling. Lunar regolith complicates this balance. Its fine, abrasive particles possess unique optical behavior that can lower reflectivity and raise emissivity when embedded in or adhered to fabric surfaces, degrading thermal control and increasing the risk of overheating or cooling inefficiency. To quantify these effects, the Artemis Suit Materials (ASM) team measured solar absorptance and infrared emissivity of clean and dust-soiled Ortho Fabric, establishing beginning-of-life (BOL) and end-of-life (EOL) benchmarks. EOL conditions were simulated with a rotary tumbler abrasion process using lunar dust simulant and ceramic media to reproduce cumulative wear expected during surface operations. Tests also included unmodified fabrics and a fabric/film laminate system containing titanium dioxide to evaluate potential improvements in dust resistance and optical performance. Results from these evaluations provide critical insight into how lunar dust alters fabric thermal behavior and inform the design of bespoke suit materials that maintain required optical properties throughout mission life, supporting safe and effective long-duration EVA on the lunar surface.

Textile↗