A Study of Space Environment Effect on Highly Thermally Conductive Hybrid Carbon Fiber Polymer Composites

Joy Rosado·Jin Ho Kang·Keith L Gordon·Grace Belancik·Pranav Jagtap
View original source ↗Read source document ↗Export metadata ↓

Abstract

A set of novel highly thermally conductive hybrid carbon fiber (CF) polymer composites has been developed for lightweight thermal radiator applications in space missions. This study investigates the effects of the space environment on these materials following exposure in low-Earth orbit (LEO) during the Materials International Space Station Experiment (MISSE)-17 flight mission, where samples experienced 159 days of combined atomic oxygen (AO), ultraviolet (UV) radiation, high vacuum, space radiation and thermal cycling. Post-flight characterization included weight loss, surface morphology, thermo-optical properties, molecular structures, glass transition temperature, thermal degradation and thermal conductivity analyses. The pyrolytic graphite sheet (PGS) samples exhibited negligible weight loss, stable thermo-optical property, and only minor oxidation signature on the exposed surface. Although AO erosion of the epoxy polymer matrix was evident, carbon nanotube (CNT)-infused PGS/CF epoxy composites retained high thermal emissivity and preserved their high thermal conductivities. These results demonstrate that the novel highly thermally conductive hybrid CF composites possess strong environmental resilience and are promising candidates for lightweight thermal radiators and thermal management components in future space exploration missions.

Explore related subjects

Space EnvironmentPolymerCarbon FiberThermal ConductivityComposite

Keep this discovery

BibTeXRIS

Joy Rosado, Jin Ho Kang, Keith L Gordon, Grace Belancik, Pranav Jagtap. 2026-04-01. A Study of Space Environment Effect on Highly Thermally Conductive Hybrid Carbon Fiber Polymer Composites. https://ntrs.nasa.gov/citations/20260003187

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Carbon Fiber subjectCarbon composites materialComposite subjectPolymer subjectSPACE ENVIRONMENT subjectThermal Conductivity subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRS2026

Micromechanical Design of Carbon Nanotube Ribbon Reinforced Polymer Composite Materials

Lightweight materials are an important component of the design of aerospace structures. Carbon nanotube materials have been considered for this purpose due to the strength and stiffness of individual nanotubes, and the commercial availability of bulk formats such as fibers. These fibers can have a ribbon cross section which results in a different design space for their composites relative to traditional reinforcements which have a round cross section. This work applies brick-and-mortar micromechanical models and classical lamination theory with an inverse approach to investigate the design space of these composites. Using this approach, the influences of fiber geometry and axial and transverse mechanical properties are mapped. Finally, a sensitivity study is performed and the relative impacts of ±10% variations in the constituent material and geometric properties are ranked. Lamina axial moduli were found to range from a maximum of 3x to 1x minimum relative to a target quasi-isotropic laminate modulus depending on the anisotropy and shear modulus of the lamina. The fiber targets depended strongly on the fiber volume fraction in the lamina and the fiber axial modulus target was found to range from 4.8x to 3.2x the quasi-isotropic laminate target. The sensitivity analysis found that the largest driver of performance was the volume fraction, followed by the fiber axial modulus. While bio-based brick-and-mortar composites, such as nacre, can benefit from reinforcement aspect ratios above 10, for carbon nanotube ribbon (or carbon fiber)/polymer composites the sensitivity study indicated that the optimal cross-sectional aspect ratio was relatively smaller, potentially less than three.

Micromechanics↗
NASA NTRS2026

Mechanical Properties of Carbon Fiber Reinforced Composites Exposed to Cryogenic Conditions and Space Radiation via Simulation and Testing

As NASA missions extend beyond low Earth orbit, increasing reliance is placed on carbon fiber reinforced polymer (CFRP) composites for spacecraft structures where mass efficiency, durability, and long-term reliability are critical. In service, these materials are subjected to a combination of ultraviolet radiation, vacuum, ionizing radiation, atomic oxygen, and extreme thermal excursions under sustained mechanical loading. Flight systems such as the Boeing Starliner and SpaceX Dragon employ external composite structures that will experience these environments for extended durations. Although prior spaceflight and ground studies have reported limited changes in bulk mechanical properties, the synergistic effects of these environments on composite microstructure, particularly at the fiber matrix interphase, remain insufficiently characterized and represent a potential qualification and reliability risk. This study investigates the effects of short-term cryogenic exposure on a radiation shielding carbon epoxy composite, SC2020, as a ground-based analog for space relevant thermal extremes. The SC2020 material system has previously flown on the International Space Station under the Materials International Space Station Experiment (MISSE) program. Composite specimens were exposed to liquid nitrogen for 6 and 24 hours and evaluated using a multiscale characterization framework that combined ASTM D3039 tensile testing, Atomic Force Microscopy (AFM) based interphase analysis, and helium gas permeability measurements. Tensile testing showed no statistically significant or permanent degradation in global strength or modulus following cryogenic exposure. In contrast, AFM measurements revealed reductions in interphase modulus, weakened adhesion, and increased nanoscale heterogeneity, indicating localized degradation mechanisms not captured by conventional bulk testing. Gas permeability measurements showed a progressive increase in helium diffusion with exposure duration, consistent with micro-void formation or partial interfacial debonding. The results indicate that cryogenic exposure initiates degradation at the fiber matrix interphase while leaving global mechanical properties largely unchanged over short durations. These findings underscore the importance of multiscale diagnostics for identifying early-stage damage mechanisms that may influence long term performance and qualification margins for spaceflight composite structures. The data presented establish a cryogenic baseline for comparison with forthcoming MISSE flight exposure results and support ongoing NASA Established Program to Stimulate Competitive Research (EPSCoR) efforts aimed at improving composite qualification methodologies, risk assessment, and reliability prediction for space environments.

composite reliability↗