Radiation sensitivity of quartz crystal oscillators experiment for the Long Duration Exposure Facility (LDEF)

J. S. Ahearn; J. D. Venables

Home/Archive/NASA NTRS

NASA NTRS · 19920017868

Radiation sensitivity of quartz crystal oscillators experiment for the Long Duration Exposure Facility (LDEF)

J. S. Ahearn·J. D. Venables

View original source ↗Export metadata ↓

Abstract

Factors determining the radiation sensitivity of quartz crystal oscillators were studied on NASA's LDEF. Quartz materials were examined in the transmission electron microscope (TEM) and classified as to their sensitivity to radiation damage by establishing the rate of damage caused by the electron beam in the microscope. Two types of materials, i.e., swept premium Q quartz and natural quartz were chosen because clear differences were observed in their response to the electron beam in the TEM studies. Quartz resonators were then fabricated from them, tested for frequency stability over a greater than 6 mo. period and flown on the LDEF satellite. After retrieval (more than 7 yrs in space) the stability of the resonators was again determined. All of the space exposed resonators fabricated with swept premium Q material exhibited a frequency shift above that of the control resonators: none of the resonators fabricated from the natural quartz materials exhibited such a shift. The significant differences observed between the two types of materials in both the ground-based TEM studies and the space radiation induced frequency changes suggest that there may be a correlation between the two observations.

Keep this discovery

BibTeX RIS

J. S. Ahearn, J. D. Venables. 1992-01-01. Radiation sensitivity of quartz crystal oscillators experiment for the Long Duration Exposure Facility (LDEF). https://ntrs.nasa.gov/citations/19920017868

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS1992

Long Duration Exposure Facility experiment M0003 deintegration observation database

The four trays of the M0003 materials experiment on LDEF contained 1274 samples from 19 subexperiments. The complete sample complement represented a broad range of materials, including thin film optical coatings, paints, polymer sheets and tapes, adhesives, and composites, for use in various spacecraft applications including thermal control, structures, optics, and solar power. Since some subexperiments included duplicate samples exposed on the leading and trailing edge trays, for 9 week, 19 week, 40 week, and 68 month durations on both the leading and trailing edges, comparisons provided a valuable time history of degradation. During the deintegration of the subexperiments from the M0003 trays, each sample was examined using bright field, dark field, and Normarski light microscopy techniques. Over 3,000 color macrographs and photomicrographs were made of the condition of M0003 trays and the individual samples. Records of the condition of the samples, photographic records, and all available references of publications on postflight analyses on each sample were collected in a database. The photographs provide a visual comparison of the response of materials common to various subexperiments in different LDEF environments. Aerospace Corporation is distributing the database records and photographs and written records on materials of interest from the database is given in this presentation.

S. R. Gyetvay↗

NASA NTRS1992

Degradation of optical components in a space environment

The objective of the Phillips Laboratory (PL) Long Duration Exposure Facility (LDEF) experiment is to determine the adverse effects of the natural space environment on laser optical component and coating materials. The LDEF experiment provides a unique opportunity for the study of optical material response to an extended low earth orbit space exposure. The PL samples consist of 10 sets of the six materials each. The materials are uncoated fused silica, magnesium fluoride coated fused silica, uncoated molybdenum, molybdenum coated with chromium, silver and thorium fluoride, diamond turned copper, and diamond turned nickel plated copper. Performance degradation will be correlated to establish trends between sample location, duration of exposure, atomic oxygen exposure and other space environmental conditions. This paper discusses the results of the tests thus far performed on the LDEF samples and the plans for the future.

Linda L. Dehainaut↗

NASA NTRS1992

Ruled and holographic experiment (AO 138-5)

The AO 138-5 experiment has been designed, via the French Cooperative Payload (FRECOPA) experiment with the aim to study the optical behavior of different diffraction gratings submitted to space vacuum long exposure and solar radiation. Samples were rules and holographic gratings, masters or replica, and some additional control mirrors with various coatings. The experiment was located on the B3, trailing edge of the Long Duration Exposure Facility (LDEF) and has been protected against atomic oxygen flux. The experienced thermal cycling has been evaluated from -23 C to 66 C during the flight, 34,000 orbits. The analysis has been focused on the triple point characterization including light efficiency, wavefront flatness quality and stray light level. Tests were conducted on control mirrors and gratings loaded but not exposed to cosmic dust or solar irradiations. They did not show any significant variations. Solar exposure has damaged the coating reflectivity in the ultraviolet region, the degradation is higher with the gratings, in terms of efficiency. However, wavefront flatness quality and stray light level tests revealed no additional changes.

Francis Bonnemason↗