Wave propagation in transversely impacted composite laminates

Abstract

An experimental study was conducted to determine the wave-propagation characteristics, transient strains and residual properties of unidirectional and angle-ply boron/epoxy and graphite/epoxy laminates impacted with silicon-rubber projectiles at velocities up to 250 m/sec. Results include the following: (1) the predominant wave is the flexural wave propagating at different velocities in different directions; (2) peak strains and strain rates in the transverse to the (outer) fiber direction are much higher than those in the direction of the fibers; (3) strain rates up to 640/sec were measured; and (4) unidirectional laminates under impact showed appreciable modulus and strength degradation in the direction transverse to fibers.