NASA NTRS1983

Method for compression testing of composite materials at high strain rates

A method is presented for testing composite materials in compression at strain rates up to approximately 500 per s. The method uses a thin ring specimen (4 in. in diameter, 1 in. wide, six-eight plies thick) loaded dynamically by an external pressure pulse applied explosively through a liquid. Strains in the specimen and in a steel calibration ring are recoorded with a digital processing oscilloscope. Results are plotted by an x-y plotter in the form of a dynamic stress-strain curve. Data analysis is based on a numerical solution of the equation of motion. A computer program is used which involves smoothing and approximation of the strain magnitude, strain rate, and strain acceleration. Dynamic stress-strain curves obtained for 0-deg and 90-deg specimens of two graphite/epoxy composites are presented.

Daniel, I. M.↗

NASA NTRS1982

Strain rate characterization of unidirectional graphite/epoxy composite

For an investigation of problems of composites at high strain rates with dominant wave propagation effects, such as dynamically loaded composite jet engine blades, the longitudinal, transverse, and in-plane shear properties of unidirectional SP 288/AS graphite/epoxy were measured at various strain rates ranging from quasi-static to over 500/s. The test specimens were rings 10.16 cm in diameter, 2.54 cm long, 6 to 8 plies thick, and with fibers at 0, 90, and 10 deg off-axis. Quasi-static testing was conducted in a fixture which applies hydraulic pressure to the ring specimens, and dynamic testing was conducted by applying an internal pressure pulse through a liquid in a special fixture. Dynamic stress-strain curves are presented. For the 0-deg specimens, the modulus increases with strain up to 20 percent of the static value. The modulus and strength increase sharply in the 90-deg rings with strain rate reaching values two to three times the corresponding static rate.

Daniel, I. M.↗

NASA NTRS1979

Wave propagation in transversely impacted composite laminates

An experimental study was conducted to determine the wave-propagation characteristics, transient strains and residual properties of unidirectional and angle-ply boron/epoxy and graphite/epoxy laminates impacted with silicon-rubber projectiles at velocities up to 250 m/sec. Results include the following: (1) the predominant wave is the flexural wave propagating at different velocities in different directions; (2) peak strains and strain rates in the transverse to the (outer) fiber direction are much higher than those in the direction of the fibers; (3) strain rates up to 640/sec were measured; and (4) unidirectional laminates under impact showed appreciable modulus and strength degradation in the direction transverse to fibers.

Daniel, I. M.↗