Silicon Solar Cell Process Development, Fabrication and Analysis

Abstract

The standard solar cells (2x2 cm) from the cast silicon (HEM) showed a maximum AMO efficiency of 10.1%. Cells from the low resistivity material (0.5 ohm-cm) showed lower performance than those of the high resistivity cast silicon (3 ohm-cm), an average efficiency 9.5% versus 7.6%. Maximum AMO efficiency of the standard solar cells from the EFG (RH) ribbons was about 7.5%. The solar cells from the controlled SiC, using the displaced die, showed more consistent and better performance than those of the uncontrolled SiC ribbons, an average efficiency of 6.6% versus 5.4%. The average AMO efficiency of the standard SOC solar cells were about 6%. These were large area solar cells (an average area of 15 sq cm). A maximum efficiency of 7.3% was obtained. The SOC solar cells showed both leakage and series resistance problems, leading to an average curve fill factor of about 60%.