Two-layer thermal barrier coating for high temperature components

Abstract

A simple two-layer plasma-sprayed thermal barrier coating system was developed which has the potential for protecting high temperature air-cooled gas turbine components. Of the initially examined coatings, the most promising system is an Ni-16Cr-6Al-0.6Y (in wt%) bond coating (about 0.005 to 0.010 cm thick) and a ZrO2-12Y2O3 (in wt%) thermal barrier coating (about 0.025 to 0.064 cm thick). This thermal barrier substantially lowered the metal temperature of the air-cooled airfoil. The coating withstood 3200 cycles (80 s at 1280 C surface temperature) and 275 cycles (1 hr at 1490 C surface temperature) without cracking or spalling. No separation of the thermal barrier from the bond coating or the bond coating from the substrate was observed.