NASA NTRS1986

Optimization of the Ni-Cr-Al-Y/ZrO2-Y2O3 thermal barrier system

The effects of bond and thermal barrier coating compositions, thicknesses, and densities on air plasma spray deposited Ni-Cr-Al-Y/ZrO2-Y2O3 life were evaluated in cyclic furnace oxidation tests at temperatures from 1110 to 1220 C. An empirical relation was developed to give life as a function of the above parameters. The thermal barrier system tested which had the longest life consisted of Ni-35.0 wt pct Cr-5.9 wt pct Al-0.95 wt pct Y bond coating and ZrO2-6.1 wt pct Y2O3 thermal barrier coating.

Stecura, S.↗

NASA NTRS1986

Advanced thermal barrier system bond coatings for use on nickel-, cobalt- and iron-base alloy substrates

New and improved Ni-, Co-, and Fe-base bond coatings have been identified for the ZrO2-Y2O3 thermal barrier coatings to be used on Ni-, Co-, and Fe-base alloy substrates. These bond coatings were evaluated in a cyclic furnace between 1120 and 1175 C. It was found that MCrAlYb (where M = Ni, Co, or Fe) bond coating thermal barrier systems have significantly longer lives than MCrAlY bond coating thermal barrier systems. The longest life was obtained with the FeCrAlYb thermal barrier system followed by NiCrAlYb and CoCrAlYb thermal barrier systems in that order.

Stecura, S.↗

NASA NTRS1985

Thermal barrier coating system

An oxide thermal barrier coating comprises ZrO3-Yb2O3 that is plasma sprayed onto a previously applied bond coating. The zirconia is partially stabilized with about 124 w/o ytterbia to insure cubic, monoclinic, and terragonal phases.

Stecura, S.↗

NASA NTRS1985

Advanced thermal barrier system bond coatings for use on Ni, Co-, and Fe-base alloy substrates

New and improved Ni-, Co-, and Fe-base bond coatings have been identified for the ZrO2-Y2O3 thermal barrier coatings to be used on NI-, Co-, and Fe-base alloy substrates. These bond coatings were evaluated in a cyclic furnace between 1120 and 1175 C. It was found that MCrAlYb (where M = Ni, Co, or Fe) bond coating thermal barrier systems. The longest life was obtained with the FeCrAlYb thermal barrier system followed by NiCrAlYb and CoCrAlYb thermal barrier systems in that order.

Stecura, S.↗

NASA NTRS1985

Optimization of the NiCrAl-Y/ZrO-Y2O3 thermal barrier system

The effects of bond and thermal barrier coating compositions, thicknesses, and densities on air plasma spray deposited Ni-Cr-Al-Y/ZrO2-Y2O3 life were evaluated in cyclic furnace oxidation tests at temperatures from 1110 to 1220 C. An empirical relation was developed to give life as a function of the above parameters. The thermal barrier system tested which had the longest life consisted of Ni-35.0 wt% Cr-5.9 wt% Al-0.95 wt% Y bond coating and ZrO2-6.1 wt% Y2O3 thermal barrier coating.

Stecura, S.↗

NASA NTRS1984

Thermal barrier coating system

A high temperature oxidation resistant, thermal barrier coating system is disclosed for a nickel cobalt, or iron base alloy substrate. An inner metal bond coating contacts the substrate, and a thermal barrier coating covers the bond coating. NiCrAlR, FeCrAlR, and CoCrAlR alloys are satisfactory as bond coating compositions where R=Y or Yb. These alloys contain, by weight, 24.9-36.7% chromium, 5.4-18.5% aluminum, and 0.05 to 1.55% yttrium or 0.05 to 0.53% ytterbium. The coatings containing ytterbium are preferred over those containing yttrium. An outer thermal barrier coating of partial stabilized zirconium oxide (zirconia) which is between 6% and 8%, by weight, of yttrium oxide (yttria) covers the bond coating. Partial stabilization provides a material with superior durability. Partially stabilized zirconia consists of mixtures of cubic, tetragonal, and monoclinic phases.

Stecura, S.↗

NASA NTRS1983

Improved performance thermal barrier coatings

Thermal barrier coatings offer an attractive approach to improving the durability and efficiency of the hot section of heat engines. The coatings typically consist of an inner alloy bond coating about 0.01 cm thick resistant to oxidation and hot corrosion and an outer ceramic layer, usually a stabilized zirconia, 0.01-0.05 cm thick. Here, the materials, thermomechanical stress, and hot corrosion problems associated with thermal barrier coatings are reviewed along with the capabilities and limitations of current technology. The coatings discussed include ZrO2-Y2O3/NiCrAlY, ZrO2-Y2O3/NiCoCrAlY, ZrO2-MgO/NiCoCrAlY, CaO-SiO2/Co-Cr-Al-Y, and CaO-SiO2/NiCrAlY systems. It is emphasized that the performance of thermal barrier coatings is governed by many complex and interrelated factors, so that optimization of these coatings always involves certain tradeoffs.

Levine, S. R.↗

NASA NTRS1982

Two-layer thermal-barrier systems for Ni-Al-Mo alloy and effects of alloy thermal expansion on system life

Cyclic furnace and cyclic natural gas-oxygen torch rig tests were conducted to (1) identify a thermal-barrier system for a nickel-aluminum-molybdenum alloy, (2) study the oxidation of the bond coating, and (3) study the effect of the substrate coefficient of thermal expansion on thermal barrier system life. It is found that the latter is affected by the composition of the bond coating, yttria concentration in zirconia, and the coefficient of thermal expansion of the substrate material. In addition, small compositional changes in the bond and thermal barrier coatings have greater effect on thermal barrier system life than the 40% increase in the coefficient of thermal expansion of the substrate material. No simple relation exists between the weight gain caused by bond-coating oxidation with increasing yttria concentration in zirconia and increasing bond coating thickness on the one hand, and thermal barrier system life on the other.

Stecura, S.↗

NASA NTRS1981

Effects of plasma spray parameters on two layer thermal barrier

The power level and the type of arc gas used during plasma spraying of a two layer thermal barrier system (TBS) were found to affect the life of the system. Life at 1095 C in a cyclic furnace test was improved by about 140 percent by increasing the power during plasma spray applications of the bond and thermal barrier coatings. This improvement is due to increases in the densities of the bond and thermal barrier coatings by 3 and 5 percent, respectively. These increases in densities are equivalent to about 45 and 30 percent reduction in mean porosities, respectively. The addition of hydrogen to the argon arc gas had the same effect as the reduction in power level and caused a reduction in TBS life.

Stecura, S.↗

NASA NTRS1981

Improved metallic and thermal barrier coatings

Low thermal conductivity two layer ceramic coatings are efficient thermal barriers between cooled matallic components and high temperature combustion gases. Potential components are combustors, blades, and vanes in aircraft engines of power-generating turbines. Presence of two layer coatings greatly reduces temperature and coolant requirements.

Stecura, S.↗

NASA NTRS1980

Performance of two-layer thermal barrier systems on directionally solidified Ni-Al-Mo and comparative effects of alloy thermal expansion on system life

A promising two-layer thermal barrier coating system (TBS), Ni-16.4Cr-5.1A1-0.15Y/ZrO2-6.1Y2O3 (all in weight percent), was identified for directionally solidified Ni-Al-Mo (gamma/gamma' alpha). In cyclic furnace tests at 1095 C this system on gamma/gamma' alpha was better than Ni-16. 4Cr-5.1Al-0.15Y/ZrO2-7.8Y2O3 by about 50 percent. In natural gas - oxygen torch rig tests at 1250 C the ZrO2-6.1Y2O3 coating was better than the ZrO2-7.8Y2O3 coating by 95 percent, on MAR-M509 substrates and by 60 percent on gamma/gamma' alpha substrates. Decreasing the coefficient of thermal expansion of the substrate material from 17-18x10 to the -6 power/C (MAR-M200 + Hf and MAR-M509) to 11x10 to the -6 power/C (gamma/gamma' alpha) also resulted in improved TBS life. For example, in natural gas - oxygen torch rig tests at 1250 C, the life of Ni-16.4Cr-5.1Al-0.15Y/ZrO26.1Y2O3 was about 30 percent better on gamma/gamma' alpha than on MAR-M509 substrates. Thus compositional changes in the bond and thermal barrier coatings were shown to have a greater effect on TBS life than does the coefficient of thermal expansion.

Stecura, S.↗

NASA NTRS1980

Effects of yttrium, aluminum and chromium concentrations in bond coatings on the performance of zirconia-yttria thermal barriers

A cyclic furnace study was conducted on thermal barrier systems to evaluate the effects of yttrium, chromium and aluminum in nickel-base alloy bond coatings and the effect of bond coating thickness on yttria-stabilized zirconia thermal barrier coating life. Without yttrium in the bond coatings, the zirconia coatings failed very rapidly. Increasing chromium and aluminum in the Ni-Cr-Al-Y bond coatings increased total coating life. This effect was not as great as that due to yttrium. Increased bond coat thickness was also found to increase life.

Stecura, S.↗

NASA NTRS1980

Thermal barrier coatings - Burner rig hot corrosion test results

A Mach 0.3 burner rig test program was conducted to examine the sensitivity of thermal barrier coatings to Na- and V-contaminated combustion gases simulating potential utility gas turbine environments. Coating life of the standard ZrO2-12Y2O3/Ni-16.2Cr-5.6Al-0.6Y (composition in wt %) NASA thermal barrier coating system which was developed for aircraft gas turbines was significantly reduced in such environments. Two thermal barrier coating systems, Ca2SiO4/Ni-16.2Cr-5.6Al-0.6Y and ZrO2-8Y2O3/Ni-16.4Cr-5.1Al-0.15Y and a less insulative cermet coating system, 50 vol % MgO-50 vol % Ni-19.6Cr-17.1Al-0.97Y/Ni-16.2Cr-5.6Al-0.6Y, were identified as having much improved corrosion resistance compared to the standard coating.

Hodge, P. E.↗

NASA NTRS1980

Effects of yttrium, aluminum and chromium concentrations in bond coatings on the performance of zirconia-yttria thermal barriers

A cyclic furnace study was conducted on thermal barrier systems to evaluate the effects of yttrium, chromium, and aluminum in nickel-base alloy bond coatings and the effect of bond coating thickness on yttria-stabilized zirconia thermal barrier coating life. Without yttrium in the bond coatings, the zirconia coatings failed very rapidly. Increasing chromium and aluminum in the Ni-Cr-Al-Y bond coatings increased total coating life. This effect was not as great as that due to yttrium. Increased bond coat thickness was also found to increase life.

Stecura, S.↗

NASA NTRS1980

Thermal barrier coatings for aircraft gas turbines

Improvements in gas turbine performance are approaching the limits imposed by alloy properties and excessive cooling air requirements. Thin ceramic coatings can increase the difference between gas temperature and metal temperature by several hundred degrees. Thus, they are potentially a major step forward in surface protection. These coatings offer the potential to reduce fuel consumption by permitting reduced coolant flow or higher turbine inlet temperature or to improve durability by reducing metal temperatures and transient thermal stresses. At NASA Lewis, in-house and contractual programs are in place to bring this promising technology to engine readiness in the early 1980's. Progress towards this goal is summarized in this paper.

Miller, R. A.↗

NASA NTRS1980

Effects of yttrium, aluminum and chromium concentrations in bond coatings on the performance of zirconia-yttria thermal barriers

A cyclic furnace study was conducted on thermal barrier systems to evaluate the effects of yttrium, chromium and aluminum in nickel-base alloy bond coatings and the influence of the bond coating thickness on yttria-stabilized zirconia thermal barrier coating lifetimes. Without yttrium in the bond coatings, the zirconia coatings failed very rapidly. Increasing concentrations of chromium and aluminum in the Ni-Cr-Al-Y bond coatings increased the total coating lifetimes. This effect was not as great as that due to yttrium. Increased bond coating thickness was also found to increase the lifetimes.

Stecura, S.↗

NASA NTRS1979

Effects of yttrium, aluminum, and chromium concentrations in bond coatings on the performance of zirconia-yttria thermal barriers

A cyclic furnace study was conducted between 990 - 280 C and 1095 - 280 C to evaluate the effects of yttrium, chromium, and aluminum concentrations in nickel base alloy bond coatings and also the effect of the bond coating thickness on the performance of yttria-stabilized zirconia thermal barrier coatings. The presence and the concentration of yttrium is very critical. Without yttrium, rapid oxidation of Ni-Al, Ni-Cr, and Ni-Cr-Al bond coatings causes zirconia thermal barrier coatings to fail very rapidly. Concentrations of chrominum and aluminum in Ni-Cr-Al-Y bond coating have a very significant effect on the thermal barrier coating life. This effect, however, is not as great as that due to yttrium. Furthermore, the thickness and the thickness uniformity also have a very significant effect on the life of the thermal barrier system.

Stecura, S.↗

NASA NTRS1979

Effects of compositional changes on the performance of a thermal barrier coating system

Systems consisting of Ni-base bond coatings containing about 16Cr, 6Al, and from 0.15 to 1.08Y (all in wt %) and zirconium oxide layers containing from 4.0 to 24.4Y2O3 were evaluated for suitability as thermal barrier systems for advanced aircraft gas turbine engine components. The evaluations were performed in a cyclic furnace between 990 and 280 C as well as between 1095 and 280 C on solid specimens; in a natural gas-oxygen torch rig between about 1200 and 100 C on solid specimens and up to 1580 C surface temperatures on air-cooled blades; and in a Mach 1.0 burner rig up to 1570 C surface temperatures on air-cooled blades. The data indicate that the best systems consist of combinations involving the Ni-16.4Cr-5.1Al-0.15Y and Ni-17.0Cr-5.4Al-0.35Y bond coatings and the 6.2Y2O3- and 7.9Y2O3- (all in wt %) stabilized zirconium oxide layers.

Stecura, S.↗