Basic failure mechanisms in advanced composites

Abstract

Fundamental failure mechanisms in carbon-epoxy composites were studied for more reliable prediction of the performance of these materials. Single and multiple fiber specimens were tested under tensile loads, and the sequence of failure events was observed. Parameters such as resin crack sensitivity, fiber surface treatment and variations in fibers from batch to batch are being evaluated. The analysis of bulk composite fracture processes using acoustic emission techniques is being studied in order to correlate microscopic observations with bulk composite behavior. Control of the fracture process through matrix and interface modification is being attempted, and study of failure processes in composite/metal specimens is being conducted. Most of the studies involved DEN 438 epoxy novolac as the matrix, but some experiments are now underway using the higher temperature resin ERLA 4617.