Physical and mechanical properties were determined for plasma-sprayed MgO- or Y2O3-stabilized ZrO2 thermal barrier coatings. Properties were determined for the ceramic coating in both the freestanding condition and as-bonded to a metal substrate. The properties of the NiCrAlY bond coating were also investigated.
The fundamental failure mechanisms which result from the interaction of thermal cycling and mechanical loading of carbon-epoxy composites were studied. This work was confined to epoxy resin uniderictionally reinforced with HTS carbon fibers, and consists of first identifying local fiber, matrix and interface failure mechanisms using the model composite specimen containing a small number of fibers so that optical techniques can be used for characterization. After the local fracture process has been established for both mechanical loading and thermal cycling, engineering composite properties and gross fracture modes are then examined to determine how the local events contribute to real composite performance. Flexural strength in high fiber content specimens shows an increase in strength with increased thermal cycling. Similar behavior is noted for 25 v/o material up to 200 cycles; however, there is a drastic reduction after 200 cycles indicating a major loss of integrity probably through the accumulation of local cleavage cracks in the tensile region.
Failure mechanisms in carbon-epoxy composites are identified as a basis for more reliable prediction of the performance of these materials. The approach involves both the study of local fracture events in model specimens containing small groups of filaments and fractographic examination of high fiber content engineering composites. Emphasis is placed on the correlation of model specimen observations with gross fracture modes. The effects of fiber surface treatment, resin modification and fiber content are studied and acoustic emission methods are applied. Some effort is devoted to analysis of the failure process in composite/metal specimens.
Fundamental failure mechanisms in carbon-epoxy composites were studied for more reliable prediction of the performance of these materials. Single and multiple fiber specimens were tested under tensile loads, and the sequence of failure events was observed. Parameters such as resin crack sensitivity, fiber surface treatment and variations in fibers from batch to batch are being evaluated. The analysis of bulk composite fracture processes using acoustic emission techniques is being studied in order to correlate microscopic observations with bulk composite behavior. Control of the fracture process through matrix and interface modification is being attempted, and study of failure processes in composite/metal specimens is being conducted. Most of the studies involved DEN 438 epoxy novolac as the matrix, but some experiments are now underway using the higher temperature resin ERLA 4617.
Research in materials science - high temperature structural materials, wetting and adherence of nickel alloys to sapphire, boron carbide filaments, and ceramic and graphite fibers