Corrosion evaluation of Al-Cu-Mn-Zr cast alloys in 3.5% NaCl solution

Corrosion behavior of cast Al-Cu-Mn-Zr (ACMZ) and RR350 alloys was compared to a cast 319 alloy in 3.5 wt.% NaCl. After 168 h immersion, ACMZ and RR350 alloys suffered from preferential attack adjacent to intermetallic particles decorated at grain boundaries while the attack in 319 occurred in eutectic Al-Si dendritic boundaries. Electrochemical data allowed semiquantitative comparison of alloy resistance to corrosion initiation, and ACMZ type alloys, including RR350 and three alloys with higher Cu, were considered more resistant than 319 due to the absence of deleterious Si particles. In case of 319, such Si particles presumably drove higher micro-galvanic influence to initiate and sustain Al corrosion. With lower susceptibility to corrosion initiation, ACMZ alloys should exhibit higher or at minimum similar resistance compared to cast 319.

36 MATERIALS SCIENCE↗
DOE OSTI2024

The many faces of θ' -Al 2 Cu precipitates: Energetics of pristine and solute segregated Al/ θ' semi-coherent interfaces

θ'-Al 2 Cu precipitates in Al-Cu alloys have various distorted octagon shapes, which can be explained by the competition between {100} and {110} type semi-coherent interfaces with the Al matrix. While most prior studies on the semi-coherent Al/θ' interfaces have focused on the {100} orientation, little is known about the {110} interface. We have investigated the energetics of pristine and solute-segregated {110} semi-coherent Al/θ' interfaces with advanced characterization and first-principles studies. We report interfacial, strain, and solute segregation energetics of the {110} Al/θ' semi-coherent interface for 39 elements and compared them with previously reported values of the {100} interface. We discuss the atomic features and atomic local structures to identify similarities and differences between the two types of Al/θ' semi-coherent interfaces. Here, the isotropy in pristine Al/θ' semi-coherent interfacial energy and the anisotropy resulting from solute segregation provide insight into the formation of different types of θ' precipitate “faces” reported in the literature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Dual X-ray computed tomography-aided classification of melt pool boundaries and flaws in crept additively manufactured parts

In metal additive manufacturing (AM), understanding the process-structure-performance relationships requires a combination of multi-scale characterization techniques that allows for the measurement of the melt pool shape and boundary and classifying various defects and flaws in the AM parts. Such approaches can be destructive, only 2D in nature, or have a small field of view and can be complex to co-register and analyze. Here, in this work, we present a non-destructive 3D inspection technique that employs dual-energy X-ray computed tomography (XCT) along with a model-based iterative reconstruction (MBIR) and a new segmentation algorithm. The proposed approach and algorithm are not only capable of classifying and quantifying flaws such as pores, cracks, and inclusions, but they also allow for the extraction of microstructural features such as melt pool boundaries (MPB) and melt pool regions (MPR), that can help understand process-structure-performance relationships for alloys under study. As an exemplar application, we employed the method for characterization of an additively manufactured aluminum alloy crept under tensile stress at 300 °C for 1064 h. Our results demonstrate high quality segmentation and classification of various flaws and MPB and MPR, for the first time, using 3D X-ray CT inspection. The delineated MPB and MPR in the crept samples reveal the preferential growth paths of cracks that formed during creep deformation. The technique was used for successfully quantifying the characteristics (number of defects, their density, volume fraction, etc.) of the manufacturing-induced pores and creep-induced cracks, which is necessary to better understand the creep failure mechanisms of the material.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Enhancement of thermal stability in Al-Ni alloys through microalloying with slow-diffusing elements, specifically Zr, has been previously reported which is attributed to Zr segregation at the Al/Al 3 Ni interface. In this study, we explore the influence of microalloying Al-Ni alloys with Zr, Ti, V, and Fe on microstructural evolution, hardness, and electrical and thermal conductivity across a range of heat-treatment temperatures from 300 to 450 °C. The distribution of microalloying elements and precipitates after heat treatment is characterized using atom probe tomography (APT). Our investigation confirms Zr segregation to the Al/Al 3 Ni interface, while similar interfacial segregation is absent with the addition of Ti, V, and Fe. Additionally, our analysis of the Al 3 Ni microfiber morphology reveals that their coarsening and spheroidization rates are similar with and without interfacial segregation; thus, retaining the fiber reinforcement through interfacial segregation of slow diffusing elements may not be an effective strategy. Precipitation of L1 2 nanoparticles was found to be the dominant mechanism affecting enhanced hardness and electrical conductivity in Al-Ni-Zr alloys, attributed to precipitation strengthening and solute depletion, respectively. Similar precipitation was not observed for additions of Ti, V, and Fe following heat treatment. We provide a thermodynamic explanation for this limitation. Furthermore, the findings of this study suggest that an effective approach for designing Al-Ni alloys should involve prioritizing microalloying elements to maximize L1 2 precipitation and minimize solute content in the FCC-Al matrix post heat treatment, rather than focusing on Al/Al3Ni interfacial segregation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Creep deformation and cavitation in an additively manufactured Al-8.6Cu-0.4Mn-0.9Zr (wt%) alloy

Creep deformation and cavitation were investigated at 300 ºC in both tension and compression for an additively manufactured Al-8.6Cu-0.5Mn-0.9Zr (wt%) alloy in the as-fabricated state and after various aging treatments (aging at 300 °C/200 h or 350 °C/24 h and overaging at 400 °C/200 h). Creep mechanisms at 300 °C were determined by relating the measured creep response to corresponding microstructural and X-ray computed tomography observations. In compression, alloys in the as-fabricated and two aging conditions exhibited similarly high creep resistance. Overaging (400 °C/200 h) led to substantial coarsening of intragranular θ-Al2Cu precipitates and an expected drop in their Orowan strengthening contribution. In tension, minimum strain rates comparable to those in compression were obtained at any given stress; however, upon accumulation of some plastic strain in the matrix, creep cavities started to form, leading to accelerated tertiary stage creep deformation and rupture. Cavitation occurred exclusively along melt pool boundaries due to locally enhanced diffusion enabled by (i) large grain-boundary area in adjacent fine-grained zones and (ii) localization of creep strain in nearby heat-affected zones. Although cavity growth was initially diffusion-controlled, its rate was determined by matrix creep rate, consistent with constrained cavity growth mechanisms. This study reveals how microstructural complexities induced by the additive manufacturing process affect the creep and cavitation behavior of Al-Cu-Mn-Zr alloys. The underlying creep and cavitation mechanisms uncovered in this study point to pathways that improve the high-temperature properties of additively manufactured alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Reliability of Materials and Components for Solid Oxide Fuel Cells

Planar stack solid-oxide fuel cells (SOFCs) require seals that must operate reliably under demanding conditions for lifetimes of 40000 hours. This includes temperature fluctuations between 800°C and RT during on and off cycles, thermal stresses, oxidizing environments and chemical degradation to name a few. This comprehensive report provides results from long term testing of two commercially available multicomponent barium alkali silicate glasses: SCN and G6, chosen as sealing candidates. In this scope, the glass seals were deposited on YSZ and Al 2 O 3 substrates simulating electrolytes (Zrbased) and coatings (both zirconia and Al 2 O 3 ). The seal-substrate couples were subjected to 800°C under air and steam+H 2 +N 2 environments up to 40000 hours to test their integrity under real operating conditions. Extensive studies on the effects of exposure have been conducted over the span of testing at various time intervals. Within the context of characterization, mechanical properties such as density, roughness, thermal expansion and glass transition, viscosity and wettability behavior; and microstructural properties such as glass chemistries, defect formation (cracks and pores), phase transformations (devitrification) and glass-interface reactions are investigated. Results and discussions are provided with a focus on the degradation of the properties over long term interrupted testing.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2024

An additively manufactured near-eutectic Al-Ce-Ni-Mn-Zr alloy with high creep resistance

A new additively manufactured (AM) Al-7.5Ce-4.5Ni-0.4Mn-0.7Zr (wt.%) near-eutectic alloy is reported, which shows unprecedented creep resistance up to 400 °C (a homologous temperature of 0.72). The eutectic solidification microstructure comprises ~ 27 vol% of coarsening-resistant second phase network with an ultrafine (<100 nm) inter-phase spacing. Both Mn and Zr contribute to creep resistance of the alloy. Small amount of Mn addition promotes selection of coarsening resistant phases without compromising the alloy processability. Zr not only improves hot-tearing resistance, but further enhances the second phase coarsening resistance resulting in improved creep resistance. Neutron diffraction performed during creep deformation reveals that the underlying mechanism for creep resistance in this alloy is impedance to dislocation motion stemming from the ultrafine eutectic solidification microstructure, whereas load transfer strengthening becomes less effective as the creep temperature increases. The second phase forms a continuous network in the as-fabricated condition, which is maintained during long-term creep at 300 °C. However, this network is fragmented into fine dispersoids at higher temperatures. It is proposed that the rate-limiting deformation mechanism at 300–400 °C is (i) dislocation climb for the alloy with fragmented second phase dispersoids and (ii) Orowan looping for the alloy with a continuous second phase network. In conclusion, the present design of an AM-processable multicomponent eutectic alloy with high creep resistance can be applied to other metallic systems exhibiting eutectic reactions, with expected extreme creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure and strengthening of Al-6Ce-3Ni-0.7Fe (wt%) alloy manufactured by laser powder-bed fusion

In this study, an Al-6Ce-3Ni-0.7Fe (wt%) alloy was fabricated via laser powder-bed fusion and its microstructure, thermal stability, tensile properties, and creep properties are investigated for two rapid-solidification rates with different eutectic spacings. For both faster- and slower-cooled states, the as-fabricated alloy mostly shows elongated grains with very fine eutectic networks (~40 nm lamellar width) comprising a high-volume fraction (~18 %) of intermetallic phases. Faster-cooled samples, however, display a less continuous eutectic network with finer spacing (~100 nm), leading to higher Orowan strengthening and therefore superior microhardness and yield stress up to ~350 °C. Upon aging (300 - 450 °C), micron-size Al 9 (Ni,Fe) 2 needle-like precipitates form within grains, and the Al 11 Ce 3 eutectic network spheroidizes, while retaining a submicron width and spacing, resulting in 33–37 % drop in microhardness after 144 h aging at 400 °C. Limited tensile ductility (~6 %) and creep ductility (~1-2 %) are measured for both faster- and slower-cooled alloys due to an inhomogeneous microstructure, where cavitation preferentially initiates at melt-pool boundaries, precipitate-free zones, and/or denuded zones, eventually leading to local fracture. Denuded zones, induced by stress, form due to diffusional flow with stress-dependent orientations, and are identified as microstructurally weak regions leading to strain localization. The present alloy does not show a significant difference in 300 °C creep resistance between: (i) tensile and compressive loading, (ii) faster- and slower-cooled samples, and (iii) continuous and spheroidized eutectics. Creep resistance at 300 °C is comparable to that of a Ce-richer Al-10.5Ce-3.1Ni-1.2Mn (wt%) alloy, despite the formation of denuded zones and needle-like Al 9 (Ni,Fe) 2 precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Effect of Mn on eutectic phase equilibria in Al-rich Al-Ce-Ni alloys

Microstructural analysis of additively manufactured (AM) Al-Ce-Ni-Mn alloys has identified phases not predicted from existing ternary liquidus projections in the Al-Ce-Ni system. Because the rapid cooling rate of AM is orders of magnitude above that of traditional casting, it is unclear if these additional phases arose from the non-equilibrium processing conditions of AM, a drastic shift in phase stability in the system due to the addition of 1 wt% Mn, or some combination of these two influences. The phases and microstructure of cast samples of Al-Ce-Ni and Al-Ce-Ni-Mn alloys were characterized for several annealing conditions which revealed the equilibrium phases at different temperatures. Phase analysis confirmed that minute levels of Mn substituted for Ni in the system drastically shifts the liquidus projection in the Al-rich corner of the ternary phase diagram such that the eutectic Al 3 Ni phase is suppressed in favor of the Al 23 Ni 6 (Ce,Mn) 4 phase. Further addition of Mn promotes the formation of Al 20 Mn 2 Ce and Al 10 Mn 2 Ce phases. The phase analysis data was then used to improve the CALPHAD modeling of the liquidus projection and isothermal sections for the Al-rich Al-Ce-Ni-Mn quaternary system. Thermodynamic modeling and experimental analysis on phases in the AM sample of Al-Ce-Ni with Mn confirmed that the phases present are consistent with Mn-containing Al-Ce-Ni cast samples. Here, this investigation demonstrates the potential for using secondary alloying elements to drastically alter phase stability and microstructure in alloy systems.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure and mechanical properties of hypoeutectic Al–6Ce–3Ni-0.7Fe (wt.%) alloy

Here, a hypoeutectic, Fe-modified Al–Ce–Ni alloy (Al–6Ce–3Ni-0.7Fe, wt.%) is studied in terms of microstructure, thermal stability, ambient temperature strengthening, and creep resistance. The as-cast microstructure consists of primary Al dendrites and interdendritic binary eutectic regions (Al–Al11Ce3 and/or Al–Al9(Fe,Ni)2), with micron/submicron lamellar spacing, depending on the location along the height of the ingot. The cast alloy exhibits excellent coarsening resistance at 400 °C, with mostly unchanged microstructure and microhardness after 6 weeks of aging, indicating good thermal stability of Al11Ce3 and Al9(Fe,Ni)2. Orowan strengthening and load transfer are identified as strengthening mechanisms at ambient and elevated temperature. A high volume fraction of the intermetallic phases (providing load transfer) and relatively coarse eutectic spacing (for modest Orowan strengthening) result in a moderate as-cast microhardness of 566 ± 32 MPa. Creep resistance at 300 and 350 °C is similar to a binary Al-12.5Ce eutectic alloy (with twice the Ce content) because of two countering effects: Al–6Ce–3Ni-0.7Fe shows a higher volume fraction of strengthening intermetallic phases, but it also exhibits a large fraction of primary Al dendrites which weaken the alloy. By contrast, the alloy, when laser-remelted at the surface, has a fully eutectic microstructure without primary aluminum dendrites achieved by high undercooling on solidification, with a refined network of eutectic phases that doubles the microhardness as compared to the cast alloy. Whereas coarsening is faster due to the shorter diffusion distances between the eutectic phases, hardness remains ~30% higher than the as-cast alloy after ~6 weeks aging at 400 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2023

3D Printed eutectic aluminum alloy has facility for site-specific properties

Additive manufacturing (AM) has the ability to print structures with site-specific properties. Existing AM approaches for site-specific properties are, however, based on complex processing-microstructure relationships in conventional alloys that were not designed for this purpose. Here, in this work, we report a straightforward approach for achieving site-specific properties that takes advantage of eutectic solidification characteristics. We demonstrate that the yield strength of a eutectic Al-Cu-Ce-Zr alloy can be tuned by varying the laser scan speed in concert with hatch spacing in laser powder bed fusion AM. A faster speed increases solidification rate resulting in finer eutectic spacing and higher strength. The hatch spacing is reduced at faster speeds to ensure overlap between melt pools which become smaller with increasing scan speed. The yield strength and its anisotropy relative to build direction are further tunable with a heat treatment. The scan speed-eutectic spacing-strength relationship is successfully applied to print a complex pattern of site-specific hardness in the alloy. The generalized principle of using AM for a eutectic alloy to create site-specific properties and anisotropy in properties is demonstrated.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Aluminum-cerium-manganese alloy embodiments for metal additive manufacturing

Disclosed herein are embodiments of an Al—Ce—Mn alloy for use in additive manufacturing. The disclosed alloy embodiments provide fabricated objects, such as bulk components, comprising a heterogeneous microstructure and having good mechanical properties even when exposed to conditions used during the additive manufacturing process. Methods for making and using alloy embodiments also are disclosed herein.

Allard, Lawrence F.↗
DOE OSTI2023

Additively manufactured Al-Ce-Ni-Mn alloy with improved elevated-temperature fatigue resistance

Here, the high cycle fatigue behavior of an additively manufactured (AM) Al-10.5Ce-3.1Ni-1.2Mn wt% alloy was evaluated at 350 °C. The measured fatigue strength of 50 MPa at this temperature is comparable to the most fatigue resistant wrought Al alloys (2618-T6 and 7079-T6) at 315 °C. Refinement of pore populations through advanced AM processing in the examined alloy led to oxide inclusions becoming dominant fatigue crack initiation sites. The distribution of microstructural features that determine crack initiation was measured by X-ray computed tomography and served as input to make fatigue strength model predictions with various methodologies. A Monte-Carlo based approach that was previously applied to predict the fatigue strength of cast aluminum alloys through pore size distributions yielded accurate predictions for the fatigue strength of this AM alloy. Given the tunability of defect distributions in AM alloys, the sensitivity of the Al-Ce-Ni-Mn alloy fatigue behavior to defect distributions and outstanding elevated-temperature fatigue resistance of this alloy; the results together suggest the possibility of a new generation of fatigue-resistant alloys produced by the additive manufacturing route.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Heat-resistant aluminium alloys

Scandium added to Al–Cu–Mg–Ag alloys leads to an in situ phase transformation of coherent Cu-rich nanoprecipitates at elevated temperature, with Sc atoms diffusing and occupying their interstitial sites. Notably, the transformed nanoprecipitates have enhanced thermal stability while maintaining a large volume fraction and these two microstructural features enable high tensile strength of the Al alloy with creep resistance up to 400 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Load shuffling during creep deformation of an additively manufactured AlCuMnZr alloy

Here, the high-temperature deformation behavior of an additively manufactured Al-Cu-Mn-Zr alloy is evaluated in the as-fabricated and heat-treated states using traditional ex-situ and in-situ neutron diffraction creep experiments performed at 300 °C. The dominant reinforcement phase in the alloy, θ-Al 2 Cu, despite its high volume fraction of ~10%, does not provide load transfer strengthening during creep deformation. Instead, the lattice strain evolution suggests a new mechanism we term “load shuffling” wherein the initial load is transferred away from precipitate-free zones along the grain boundaries where most of the θ-Al 2 Cu particles are located to precipitate-strengthened grain interiors. Notwithstanding the lack of load transfer strengthening, the as-fabricated AM Al-Cu-Mn-Zr alloy still possesses improved creep resistance at 300 °C relative to a cast alloy with similar composition. The proposed load shuffling mechanism explains the lack of observed L1 2 -Al 3 Zr strengthening at 300 °C and helps identify several strategies for improvement of elevated-temperature mechanical response of AM Al alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2022

First-principles study of Al/Al 3 Ni interfaces

Al-Ni alloys have shown promise for high-temperature applications due to the strengthening of Al 3 Ni fibers resistant to coarsening and spheroidization up to 400°C. While the interface between Al and Al 3 Ni phases affects the coarsening rate of Al 3 Ni at elevated temperatures, its characteristics are largely unknown to date. Here, we have constructed various supercells to model this interface and performed a first-principles study based on density functional theory (DFT). We have considered three groups of Al/Al 3 Ni interfaces: experimentally reported orientation relationships from the solidification studies, crystallographically similar Fe-Fe 3 C pearlite interfaces, and the family of low-index (100) termination planes. We have analyzed the correlation between the DFT Al/Al 3 Ni interfacial energies and characteristic features, e.g., excess free volume and the number of broken bonds. We outline the further experimental and computational analysis required to improve the interface modeling of Al/Al 3 Ni.